Overall thermoelastic properties of symmetric laminates containing obliquely crossed matrix cracks

Composites Science and Technology

Volumn 65, Issue 11-12, 2005, Pages 1647-1654

  Yokozeki, Tomohiro ^a   Aoki, Takahira ^b  

^a JAPAN AEROSPACE EXPLORATION AGENCY   (Japan)

^b UNIVERSITY OF TOKYO   (Japan)

Author keywords

B. Matrix cracking; B. Thermomechanical properties; C. Laminates; C. Transverse cracking; Multiple ply crack

Indexed keywords

CRACKS; ELASTICITY; SHEAR STRESS; THERMOELASTICITY;

CROSSED MATRIX CRACKS; SHEAR-LAG ANALYSIS; SYMMETRIC LAMINATES; THERMOELASTIC PROPERTIES;

LAMINATES;

COMPOSITE PROPERTY;

EID: 21644476141     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compscitech.2005.02.016     Document Type: Article

References (28)

1. K.W. Garrett J.E. Bailey Multiple transverse fracture in 90° cross-ply laminates of a glass fibre-reinforced polyester J Mater Sci 12 1977 157-168
2. Y.M. Han H.T. Hahn R.B. Croman A simplified analysis of transverse ply cracking in cross-ply laminates Compos Sci Technol 31 1988 165-177
3. Z. Hashin Analysis of cracked laminates: A variational approach Mech Mater 4 1985 121-136
4. L.N. McCartney Theory of stress transfer in a 0°-90°-0° cross-ply laminate containing a parallel array of transverse cracks J Mech Phys Solids 40 1992 27-68
5. G.A. Schoeppner N.J. Pagano Stress fields and energy release rates in cross-ply laminates Int J Solids Struct 35 1998 1025-1055
6. J.A. Nairn S. Hu Micromechanics of damage: A case study of matrix microcracking In: R. Talreja editor. Damage mechanics of composite materials 1994 Elsevier Amsterdam 187-243
7. J.A. Nairn Matrix microcracking in composites In: R. Talreja J.A.E. Manson Polymer editors. matrix composites 2000 Elsevier Amsterdam 403-432
8. L.N. McCartney Predicting transverse crack formation in cross-ply laminates Compos Sci Technol 58 1998 1069-1081
9. L.N. McCartney Model to predict effects of triaxial loading on ply cracking in general symmetric laminates Compos Sci Technol 60 2000 2255-2279
10. Soutis C, Kashtalyan M. Damage mechanisms in angle-ply composite laminates under in-plane tensile loading. AIAA conference paper 2001-1638
11. J.M. Whitney Effective thermo-elastic constants for monoclinic laminates containing transverse ply cracks J Reinf Plast Compos 22 2003 203-227
12. N.J. Pagano Stress fields in composite laminates Int J Solids Struct 14 1978 385-400
13. P. Gudmundson W. Zang An analytic model for thermoelastic properties of composite laminates containing transverse matrix cracks Int J Solids Struct 30 1993 3211-3231
14. R. Talreja Damage characterization by internal variables In: R. Talreja editor. Damage mechanics of composite materials 1994 Elsevier Amsterdam 53-78
15. H.L. McManus J.R. Maddocks On microcracking in composite laminate under thermal and mechanical loading Polym Polym Compos 4 1996 304-314
16. J. Zhang K.P. Herrmann Stiffness degradation induced by multilayer intralaminar cracking in composite laminates Composites A 30 1999 683-706
17. Z. Hashin Analysis of orthogonally cracked laminates under tension J Appl Mech 54 1987 872-879
18. J. Aboudi S.W. Lee C.T. Herakovich Three-dimensional analysis of laminates with cross cracks J Appl Mech 55 1988 389-397
19. C.L. Tsai I.M. Daniel J.W. Lee Progressive matrix cracking of crossply composite laminates under biaxial loading In: G.J. Dvorak D.C. Lagoudas (Eds.) Microcracking-induced damage in composites 1993 American Society of Mechanical Engineers New York 9-18
20. C.L. Tsai I.M. Daniel The behavior of cracked crossply composite laminates under general in-plane loading In: G.Z. Voyiadjis editor. Damage in composite materials 1993 Elsevier Amsterdam 51-66
21. C. Henaff-Gardin M.C. Lafarie-Frenot D. Gamby Doubly periodic matrix cracking in composite laminates. Part1: General in-plane loading Compos Struct 36 1996 113-130
22. C. Henaff-Gardin M.C. Lafarie-Frenot D. Gamby Doubly periodic matrix cracking in composite laminates. Part2: Thermal biaxial loading Compos Struct 36 1996 131-140
23. M. Kashtalyan C. Soutis Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting Composites A 31 2000 107-119
24. T. Yokozeki T. Aoki Stress analysis of symmetric laminates with obliquely crossed matrix cracks Adv Compos Mater 13 2004 121-140
25. Salpekar SA, O'Brien TK. Analysis of matrix cracking and local delamination in [0/θ/-θ]s graphite epoxy laminates under tension load. In: Proceedings of 8th international conference on composite materials, Honolulu, Hawaii, USA; 1991. p. 1-14
26. J.A. Lavoie E. Adolfsson Stitch cracks in constraint plies adjacent to a cracked ply J Compos Mater 35 2001 2077-2097
27. T. Yokozeki T. Aoki T. Ishikawa Consecutive matrix cracking in contiguous plies of composite materials Int J Solids Struct 42 2005 2785-2802
28. R.M. Jones Mechanics of composite materials 2nd ed. 1999 Taylor & Francis Philadelphia