Journal of Composite Materials

Volumn 35, Issue 23, 2001, Pages 2077-2097

Stitch cracks in constraint plies adjacent to a cracked ply

(2) Lavoie, J André a Adolfsson, Erik b

a VIRGINIA POLYTECHNIC INSTITUTE AND STATE UNIVERSITY (United States)

b ROYAL INSTITUTE OF TECHNOLOGY (Sweden)

Author keywords

Cracks inconstraint plies; Matrix crack; Microcrack

Indexed keywords

COMPOSITE MICROMECHANICS; CRACK PROPAGATION; DELAMINATION; FATIGUE OF MATERIALS; LAMINATES; NONMETALLIC MATRIX COMPOSITES; RESIDUAL STRESSES; THERMAL STRESS;

COMPOSITE DAMAGE MECHANICS MODELS; CONSTRAINT PLIES; MONOTONIC LOADING; STITCH CRACKS;

MICROCRACKS;

EID: 0035709063 PISSN: 00219983 EISSN: None Source Type: Journal
DOI: 10.1106/41A4-BFMJ-7CUE-U6NA Document Type: Article

Times cited : (42)

References (12)

1
- 0000269955
- Constrained cracking in glass fibre-reinforced epoxy cross-ply laminates
- (1978) Journal of Materials Science , vol.13 , pp. 195-201
- Parvizi, A.¹ Garrett, K.W.² Bailey, J.E.³

2
- 0008285450
- Cracked composite laminates least prone to delamination
- (1994) Proceedings of the Royal Society London , vol.444 , pp. 17-35
- Wang, J.¹ Karihaloo, B.L.²

3
- 84958508474
- Characterization of delamination onset and growth in a composite laminate
- ASTM STP 775, American Society for Testing and Materials, Philadelphia
- (1982) Damage in Composite Materials , pp. 140-167
- O'Brien, T.K.¹

4
- 0003268932
- Local delaminations in laminates with angle ply matrix cracks, part II: Delamination fracture analysis and fatigue characterization
- ASTM STP 1156, W. W. Stinchcomb and N. E. Ashbaugh, Eds., American Society for Testing and Materials, Philadelphia
- (1993) Composite Materials: Fatigue and Fracture, Fourth Volume , pp. 407-538
- O'Brien, T.K.¹

5
- 0043187449
- s laminates
- July
- (2000) Journal of Composites Technology and Research, American Society for Testing and Materials , vol.22 , Issue.3 , pp. 153-160
- Lavoie, J.A.¹ Morton, J.²

6
- 0021598748
- Characterization and analysis of damage mechanisms in tension-tension fatigue of graphite/epoxy laminates
- ASTM STP 836, American Society for Testing and Materials
- (1984) Effects of Defects in Composite Materials , pp. 21-55
- Jamison, R.D.¹ Schulte, K.² Reifsnider, K.L.³ Stinchcomb, W.W.⁴

7
- 0021897702
- First-ply failure of graphite/epoxy laminates
- ASTM STP 864, J. R. Vinson and M. Taya, Editors, American Society for Testing and Materials, Philadelphia
- (1985) Recent Advances in Composites in the United States and Japan , pp. 44-61
- Kistner, M.D.¹ Whitney, J.M.² Browning, C.E.³

8
- 0022093997
- Transverse cracking and stiffness reduction in composite laminates
- July
- (1985) Journal of Composite Materials , vol.19 , pp. 355-375
- Talreja, R.¹

9
- 0027663284
- A critical evaluation of theories for predicting microcracking in composite laminates
- (1993) Journal of Materials Science , vol.28 , Issue.18 , pp. 5099-5111
- Nairn, J.A.¹ Bark, J.²

10
- 0029229351
- Influence of stacking sequence on the transverse matrix cracking of continuous fiber cross ply laminates
- (1995) Journal of Composite Materials , vol.29 , Issue.10 , pp. 1337-1358
- Xu, L.-Y.¹

11
- 0027805757
- An analytic model for thermoelastic properties of composite laminates containing transverse matrix cracks
- (1993) International Journal of Solids and Structures , vol.30 , Issue.23 , pp. 3211-3231
- Gudmundson, P.¹ Zang, W.²

12
- 0033541073
- Matrix crack initiation and progression in composite laminates subjected to bending and extension
- (1999) International Journal of Solids and Structures , vol.36 , Issue.21 , pp. 3131-3169
- Adolfsson, E.¹ Gudmundson, P.²

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.