Applications of Kelvin probe technique in the studies of atmospheric corrosion

Journal of the Chinese Society of Corrosion and Protection

Volumn 24, Issue 1, 2004, Pages 61-64

  Wang, Yanhua ^a,b   Zhang, Tao ^b,c   Wang, Jia ^c,d   Wang, Fuhui ^c  

^a INSTITUTE OF OCEANOLOGY   (China)

^b UNIVERSITY OF CHINESE ACADEMY OF SCIENCES   (China)

^c INSTITUTE OF METAL RESEARCH   (China)

^d OCEAN UNIVERSITY OF CHINA   (China)

Author keywords

Atmospheric corrosion; Kelvin probe technique

Indexed keywords

ATMOSPHERIC CORROSION; COATING; ELECTROLYTE; MEASUREMENT METHOD; PROCESSING TECHNIQUE;

EID: 2142657935     PISSN: 10054537     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (41)

1. Barton K. Protection Against Atmospheric Corrosion[M]. London: Wiley, 1976
2. Vernon W H J. Effect of sulphur dioxide on the atmospheric corrosion of copper[J]. Trans. Faraday Soc., 1933, 27:35
3. Evans U R. The Corrosion and Oxidation of Metals[M]. London: Edward Arnold, 1960
4. Rozenfeld I L. Atmospheric corrosion of metals[A]. National Association of Corrosion Engineers[C]. Houston, 1972
5. Barton K. Protection Against Atmospheric Corrosion[M]. London: Wiley, 1976
6. Blott B H, Lee T J. A two frequency vibrating capacitor method for contact potential difference measurements [J]. J. Sci. Instrum., 1969, 46(2):785
7. Craig P P, Radeka V. Stress dependence of contact potential: the ac Kelvin method[J]. Rev. Sci. Instrum., 1970, 41(2):258
8. Besocke K, Berger S. Piezoelectric driven Kelvin probe for contact potential difference studies[J]. Rev. Sci. Instrum., 1976, 47(7): 840
9. Stratmann M. The investigation of the corrosion properties of metals, covered with adsorbed electrolyte layers - a new experimental technique[J]. Corros. Sci., 1987, 27(8):869
10. Stratmann M, Streckel H. On the atmospheric corrosion of metals which are covered with thin electrolyte layers - 1. Verification of the experimental technique[J]. Corros. Sci., 1990, 30(6/7):681
11. Zou F, Han W, Long K, et al. Determination of Kelvin potential by linear regression[J]. Corros. Sci. Prot. Technol., 1995, 7(1):17
12. Zou F, Han W. Electrochemical study of metals under thin electrolyte layer with Kelvin probe method[J]. Corros. Sci. Prot. Technol., 1995, 7(3):192
13. Wang J. Electrochemical measurements for marine atmospheric corrosion studies using Kelvin probe reference electrode[J]. Chin. J. Oceanol. Limnol., 1996, 14(3):266
14. Wang J. Electrochemical studies on the cathodic reaction of marine atmospheric corrosion [J]. Chin. J. Oceanol. Limnol., 1996, 14 (4):291
15. Yee S, Oriani R A, Stratmann M. Application of a Kelvin microprobe to the corrosion of metals in humid atmospheres[J]. J. Electrochem. Soc., 1991, 138(1):55
16. Atanasoski R T, Huang S M, Albani O, et al. A dry redox couple employed as the reference material in work function and corrosion potential measurements by the Kelvin technique[J]. Corros. Sci., 1994, 36(9):1513
17. Yasutake M, Aoki D, Fujihira M. Surface potential measurements using the Kelvin probe force microscope[J]. Thin Solid Films, 1996, 273(1/2):279
18. Stratmann M, Streckel H. Monitoring of blistering of organic coatings by a contact - free measurement[J]. Werkstoffe und Korrosion, 1992, 43:316
19. Stratmann M, Wolpers M, Streckel H, et al. Use of a scanning - Kelvin probe in the investigation of electrochemical reactions at the metal/polymer interface[J]. Ber. Bunsenges Phys. Chem., 1991, 95:1365
20. Fürbeth W, Stratmann M. Investigation of the delamination of polymer films from galvanized steel with the scanning Kelvin probe[J]. Fresenius Janal Chem., 1995, 353:337
21. Fürbeth W, Stratmann M. The delamination of polymeric coatings from electrogalvanised steel - a mechanistic approach. part 1:delamination from a defect with intact zinc layer[J]. Corros. Sci., 2001, 43:207
22. Fürbeth W, Stratmann M. The delamination of polymeric coatings from electrogalvanised steel - a mechanistic approach. part 2: delamination from a defect down to steel[J]. Corros. Sci., 2001, 43: 229
23. 2[J]. Corros. Sci., 2001, 43:243
24. Leng A, Streckel H, Stratmann M. The delamination of polymeric coatings from steel. part 1 : calibration of the Kelvin probe and basic delamination mechanism[J]. Corros. Sci., 1999, 41:547
25. Leng A, Streckel H, Stratmann M. The delamination of polymeric coatings from steel. part 2: first stage of delamination, effect of type and concentration of cations on delamination, chemical analysis of the interface[J]. Corros. Sci., 1999, 41:579
26. Leng A, Streckel H, Stratmann M. The delamination of polymeric coatings from steel. part 3; effect of the oxygen partial pressure on the delamination reaction and current distribution at the metal/polymer interface[J]. Corros. Sci., 1999, 41:599
27. Wolpers M, Stratmann M, Viefhaus H, et al. The structure and stability of metal surfaces modified by silane Langmuir - Blodgett films[J]. Thin Solid Films, 1992, 210/211:592
28. Schmidt W, Stratmann M. Scanning Kelvin probe investigations of filiform corrosion on aluminum alloy 2024 - T3[J]. Corros. Sci., 1998, 40(8):1441
29. Lobnig R E, Siconolfi D J, Psota - Kelty L, et al. Atmospheric corrosion of zinc in the presence of ammonium sulfate particles[J]. J. Electrochem. Soc., 1994, 141(1):2935
30. Lobnig R E, Siconolfi D J, Psota - Kelty L, et al. Atmospheric corrosion of aluminum in the presence of ammonium sulfate particles [J]. J. Electrochem. Soc., 1996, 143(4):1176
31. Lobnig R E, Siconolfi D J, Psota - Kelty L, et al. Mechanism of atmospheric corrosion of copper in the presence of submicron ammonium sulfate particles at 300 and 373K[J]. J. Electrochem. Soc., 1996, 143(5):1539
32. Stratmann M, Bohnenkamp K, Ramchandran T. The influence of copper upon the atmospheric corrosion of iron[J]. Corros. Sci., 1987, 27(9):905
33. Stratmann M, Streckel H . On the atmospheric corrosion of metals which are covered with thin electrolyte layers - 2. experimental results[J]. Corros. Sci., 1990, 30(6/7):697
34. Kamimura T, Stratmann M. The influence of chromium on the atmospheric corrosion of steel[J]. Corros. Sci., 2001, 43:429
35. Wang J, Tsuru T. An investigation on oxygen reduction under thin electrolyte layer using Kelvin probe reference electrode [J]. J. Chin. Soc. Corros. Prot., 1995, 15(3):179
36. Yamashita M, Nagano H, Oriani R A. Dependence of corrosion potential and corrosion rate of a low - alloy steel upon depth of aqueous solution[J]. Corros. Sci., 1998, 40(9):1447
37. Masuda H. Effect of magnesium chloride liquid thickness on atmospheric corrosion of pure iron[J]. Corrosion, 2001, 57(2):99
38. Han L T, Mansfeld F. Scanning Kelvin probe analysis of welded stainless steel[J]. Corros. Sci., 1997, 39(1):199
39. Nazarov A, Thierry D. Analysis of surface carbon contamination on phosphated zinc surfaces by scanning Kelvin probe measurements [J]. J. Electrochem. Soc., 1998, 145(3):L39
40. Leng A, Stratmann M. The inhibition of the atmospheric corrosion of iron by vapour - phase - inhibitors[J]. Corros. Sci., 1993, 34 (10):1657
41. Grundmeier G, Stratmann M. Influence of oxygen and argon plasma treatments on the chemical structure and redox state of oxide covered iron[J]. Appl. Surf. Sci., 1999, 141:43-56