Mechanism of Long Life Fatigue Fracture Induced by Interior Inclusion for Bearing Steel in Rotating Bending

Author keywords

Bearing steel; Duplex S N curve; Fine granular area; Inclusion; Rotating bending; Structural changes

Indexed keywords

BEARING CAPACITY; BENDING (DEFORMATION); CRACKS; FATIGUE OF MATERIALS; FRACTURE; INCLUSIONS; LOADING; SCANNING ELECTRON MICROSCOPY; SURFACE ROUGHNESS; TRANSMISSION ELECTRON MICROSCOPY;

EID: 1642577097     PISSN: 05145163     EISSN: None     Source Type: Journal    
DOI: 10.2472/jsms.52.1292     Document Type: Article
Times cited : (47)

References (19)
  • 1
    • 85039584528 scopus 로고    scopus 로고
    • Japanese source
  • 3
    • 85039579370 scopus 로고    scopus 로고
    • Japanese source
  • 4
    • 85039567811 scopus 로고    scopus 로고
    • Japanese source
  • 5
    • 85039567669 scopus 로고    scopus 로고
    • Japanese source
  • 6
    • 85039573322 scopus 로고    scopus 로고
    • Japanese source
  • 8
    • 85039566470 scopus 로고    scopus 로고
    • Japanese source
  • 11
    • 85039581818 scopus 로고    scopus 로고
    • Japanese source
  • 12
    • 85039587960 scopus 로고    scopus 로고
    • Japanese source
  • 13
    • 85039586390 scopus 로고    scopus 로고
    • Japanese source
  • 14
    • 85039563734 scopus 로고    scopus 로고
    • Japanese source
  • 15
    • 85039562457 scopus 로고    scopus 로고
    • Japanese source
  • 16
    • 85039562884 scopus 로고    scopus 로고
    • Japanese source
  • 18
    • 85039577774 scopus 로고    scopus 로고
    • Japanese source
  • 19
    • 85039569802 scopus 로고    scopus 로고
    • Japanese source


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.