A feasible study of fatigue life prediction for marine structures based on crack propagation analysis

Author keywords

crack growth rate curve; cumulative fatigue damage theory; cycle by cycle integration; fatigue crack propagation theory; fatigue life prediction; load sequence effect; marine structures; S N curve

Indexed keywords

CRACKS; DAMAGE DETECTION; DAMAGE TOLERANCE; FAILURE (MECHANICAL); FATIGUE CRACK PROPAGATION; FORECASTING; OCEAN STRUCTURES; OFFSHORE OIL WELL PRODUCTION;

EID: 1542664417     PISSN: 14750902     EISSN: 20413084     Source Type: Journal    
DOI: 10.1243/147509003321623112     Document Type: Article
Times cited : (24)

References (29)
  • 1
    • 0036132163 scopus 로고    scopus 로고
    • Comparative fatigue strength assessment of a structural detail in a containership using various approaches of classification societies
    • Fricke W, et al. Comparative fatigue strength assessment of a structural detail in a containership using various approaches of classification societies. Mar. Struct.. 2002 ; 15 (1). 1-13
    • (2002) Mar. Struct. , vol.15 , Issue.1 , pp. 1-13
    • Fricke, W.1
  • 2
    • 0030150454 scopus 로고    scopus 로고
    • A history of fatigue
    • Schutz W. A history of fatigue. Engng Fracture Mechanics. 1996 ; 54 (2). 263-300
    • (1996) Engng Fracture Mechanics , vol.54 , Issue.2 , pp. 263-300
    • Schutz, W.1
  • 4
    • 23044532116 scopus 로고    scopus 로고
    • A state-Of-The-Art Review on fatigue life prediction methods for metal structures
    • Cui W. A state-of-the-art Review on fatigue life prediction methods for metal structures. J. Mar. Sci. Technol.. 2002 ; 7 (1). 43-56
    • (2002) J. Mar. Sci. Technol. , vol.7 , Issue.1 , pp. 43-56
    • Cui, W.1
  • 6
    • 0036943028 scopus 로고    scopus 로고
    • Relation between crack growth rate curve and S-N curve for metal fatigue
    • Cui W. Relation between crack growth rate curve and S-N curve for metal fatigue. J. Ship Mechanics. 2002 ; 6 (6). 93-106
    • (2002) J. Ship Mechanics , vol.6 , Issue.6 , pp. 93-106
    • Cui, W.1
  • 7
    • 0347029686 scopus 로고    scopus 로고
    • The merging of fatigue and fracture mechanics concepts: A historical perspective
    • Newman J C. The merging of fatigue and fracture mechanics concepts: A historical perspective. Prog. Aerospace Sci.. 1998 ; 34: 347-390
    • (1998) Prog. Aerospace Sci. , vol.34 , pp. 347-390
    • Newman, J.C.1
  • 9
    • 0035214679 scopus 로고    scopus 로고
    • A fatigue crack driving force parameter with load ratio effects
    • Kujawski D. A fatigue crack driving force parameter with load ratio effects. Int. J. Fatigue. 2001 ; 23: S239 - S246
    • (2001) Int. J. Fatigue , vol.23 , pp. 239-S246
    • Kujawski, D.1
  • 10
    • 85014447649 scopus 로고
    • A critical analysis of crack propagation laws
    • Paris P C, Erdogan F. A critical analysis of crack propagation laws. J. Basic Engng. 1963 ; 85: 528-534
    • (1963) J. Basic Engng , vol.85 , pp. 528-534
    • Paris, P.C.1    Erdogan, F.2
  • 12
    • 85014886277 scopus 로고
    • Numerical analysis of crack propagation in cyclic-loaded structures
    • Foreman R G, Kearney V E, Engle R M. Numerical analysis of crack propagation in cyclic-loaded structures. J. Basic Engng. 1967 ; 89: 459-464
    • (1967) J. Basic Engng , vol.89 , pp. 459-464
    • Foreman, R.G.1    Kearney, V.E.2    Engle, R.M.3
  • 15
    • 0038808166 scopus 로고
    • Philadelphia, Pennsylvania: American Society for Testing and Materials;
    • Elber W Damage Tolerance in Aircraft Structures. Philadelphia, Pennsylvania: American Society for Testing and Materials ; 1971: 230-242.
    • (1971) Damage Tolerance in Aircraft Structures , pp. 230-242
    • Elber, W.1
  • 17
    • 0033078998 scopus 로고    scopus 로고
    • Fatigue-life prediction methodology using small-crack theory
    • Newman J C, Phillips E P, Swain M H. Fatigue-life prediction methodology using small-crack theory. Int. J. Fatigue. 1999 ; 21: 109-119
    • (1999) Int. J. Fatigue , vol.21 , pp. 109-119
    • Newman, J.C.1    Phillips, E.P.2    Swain, M.H.3
  • 19
    • 0033227627 scopus 로고    scopus 로고
    • An evaluation of Δkeff estimation procedure on 6061-T6 and 2024-T3 aluminum alloys
    • Donald K, Paris P C. An evaluation of ΔKeff estimation procedure on 6061-T6 and 2024-T3 aluminum alloys. Int. J. Fatigue. 1999 ; 21: S47 - S57
    • (1999) Int. J. Fatigue , vol.21 , pp. 47-S57
    • Donald, K.1    Paris, P.C.2
  • 20
    • 0035254423 scopus 로고    scopus 로고
    • Enhanced model of partial crack closure for correlation of R-ratio effects in aluminum alloys
    • Kujawski D. Enhanced model of partial crack closure for correlation of R-ratio effects in aluminum alloys. Int. J. Fatigue. 2001 ; 23: 95-102
    • (2001) Int. J. Fatigue , vol.23 , pp. 95-102
    • Kujawski, D.1
  • 21
    • 0035214023 scopus 로고    scopus 로고
    • Analysis of fatigue crack growth under compression-compression loading
    • Vasudevan A K, Sadananda K. Analysis of fatigue crack growth under compression-compression loading. Int. J. Fatigue. 2001 ; 23: S365 - S374
    • (2001) Int. J. Fatigue , vol.23 , pp. 365-S374
    • Vasudevan, A.K.1    Sadananda, K.2
  • 25
    • 0012058040 scopus 로고
    • On-site indication of fatigue damage under complex loading
    • Anzai H, Endo T. On-site indication of fatigue damage under complex loading. Int. J. Fatigue. 1979 ; 1 (1). 49-57
    • (1979) Int. J. Fatigue , vol.1 , Issue.1 , pp. 49-57
    • Anzai, H.1    Endo, T.2
  • 26
    • 0025243907 scopus 로고
    • A fast and efficient response surface approach for structural reliability problems
    • Bucher C G, Bourgund U. A fast and efficient response surface approach for structural reliability problems. Struct. Saf.. 1990 ; 7: 57-66
    • (1990) Struct. Saf. , vol.7 , pp. 57-66
    • Bucher, C.G.1    Bourgund, U.2
  • 27
    • 84930470307 scopus 로고    scopus 로고
    • Waterloo, Canada: University of Waterloo Press;
    • McEvily A J, Groeger J Fracture. Waterloo, Canada: University of Waterloo Press ; 1997: 1293-1298.
    • (1997) Fracture , pp. 1293-1298
    • McEvily, A.J.1    Groeger, J.2
  • 28
    • 0000215475 scopus 로고
    • Four lectures on fatigue crack growth
    • Schijve J. Four lectures on fatigue crack growth. Engng Fracture Mechanics. 1979 ; 11: 167-221
    • (1979) Engng Fracture Mechanics , vol.11 , pp. 167-221
    • Schijve, J.1
  • 29
    • 0000215475 scopus 로고
    • Four lectures on fatigue crack growth
    • Schijve J. Four lectures on fatigue crack growth. Engng Fracture Mechanics. 1979 ; 11: 167-221
    • (1979) Engng Fracture Mechanics , vol.11 , pp. 167-221
    • Schijve, J.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.