Enhanced model of partial crack closure for correlation of R-ratio effects in aluminum alloys

International Journal of Fatigue

Volumn 23, Issue 2, 2001, Pages 95-102

  Kujawski, Daniel ^a  

^a Parkview Campus   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CORRELATION METHODS; CRACK PROPAGATION; MATHEMATICAL MODELS; STRESS ANALYSIS;

DONALD-PARIS CRACKS; PARTIAL CRACK CLOSURES;

ALUMINUM ALLOYS;

EID: 0035254423     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(00)00085-2     Document Type: Article

References (18)

1. Elber W. The significance of fatigue crack closure. Damage tolerance in aircraft structures. 1971;230-242 American Society for Testing and Materials, Philadelphia (PA). ASTM STP 486.
2. Klesnil M, Lukas P. Effect of stress cycle asymmetry on fatigue crack growth. Mater Sci Eng. 9:1972;231-240.
3. Kujawski D, Ellyin F. A fatigue crack growth model with load ratio effects. Eng Fract Mech. 28:1987;367-378.
4. Wei RP, McEvily AJ. Fracture mechanics and corrosion fatigue. Proceedings of a Conference on Corrosion Fatigue. 1971;381-395 NACE, Stores (CN).
5. Ritchie RO. Influence of microstructure on near-threshold fatigue-crack propagation in ultra-high strength steel. Metal Sci. 1977;368-381. Aug./Sept.
6. Sadananda K, Vasudevan AK. Analysis of fatigue crack closure and threshold. Erdogan F. Fracture mechanics. 25:1993;484-501 American Society for Testing and Materials, Philadelphia (PA). ASTM STP 1220.
7. Sadananda K, Vasudevan AK. Short crack growth behavior. Piascik R, Dowling N, Newman J. Fatigue and fracture mechanics. 27:1997;301-316 American Society for Testing and Materials, Philadelphia (PA).
8. Kirby BR, Beevers CJ. Slow fatigue crack growth and threshold behavior in air and vacuum of commercial aluminum alloys. Fract Eng Mater Struct. 1:1979;203-215.
9. King JE. Surface damage and near threshold fatigue crack growth in a Ni-based superalloy in vacuum. Fract Eng Mater Struct. 5:1982;177-188.
10. Macha DE, Corby DM, Jones JW. On the variation of fatigue-crack-opening load with measurement location. Proceedings of the Society of Experimental Stress Analysis. 36:1979;207-213.
11. Shin CS, Smith RA. Fatigue crack growth from sharp notches. Int J Fatigue. 7:1985;87-93.
12. Hertzberg RW, Newton CH, Jaccard R. Crack closure: correlation and confusion. Mechanics of fatigue crack closure. 1988;139-148 American Society for Testing and Materials, Philadelphia (PA). ASTM STP 982.
13. Lawson L, Chen EY, Meshii M. Near-threshold fatigue: a review. Int J Fatigue. 21:1999;S15-S34.
14. eff estimation procedure on 6061-T6 and 2024-T3 aluminum alloys. Int J Fatigue. 21:1999;S47-S57.
15. Paris PC, Tada H, Donald JK. Service load fatigue damage - a historical perspective. Int J Fatigue. 21:1999;S35-S46.
16. McEvely AJ, Ritchie RO. Crack closure and the fatigue-crack propagation threshold as a function of load ratio. Fatigue Fract Eng Mater Struct. 21:1998;847-855.
17. Lang M, Marci G. Reflecting on the mechanical driving force for fatigue crack propagation. Panontin TL, Sheppard SD. Fatigue and fracture mechanics. 29:1998;American Society for Testing and Materials, Philadelphia (PA).
18. Tada H, Paris PC, Irwin GR. 2nd ed The stress analysis of cracks handbook. 1985;Paris Production.