Damage concept for evaluating ductile cracking of steel structure subjected to large-scale cyclic straining

Science and Technology of Advanced Materials

Volumn 5, Issue 1-2, 2004, Pages 241-249

  Ohata, Mitsuru ^a   Toyoda, Masao ^a  

^a OSAKA UNIVERSITY   (Japan)

Author keywords

Back stress; Bauschinger effect; Combined hardening model; Damage evolution; Ductile crack; Large scale cyclic loading; Two phase structural steel; Void nucleation

Indexed keywords

BRITTLE FRACTURE; CRACK INITIATION; CYCLIC LOADS; DUCTILITY; NUCLEATION; SEISMOLOGY; STRAIN; STRAIN HARDENING; STRESS ANALYSIS; TENSILE TESTING;

BACK STRESS; BAUSCHINGER EFFECTS; COMBINED HARDENING MODEL; DAMAGE EVOLUTION; DUCTILE CRACK; LARGE SCALE CYCLIC LOADING; TWO-PHASE STRUCTURAL STEEL;

WELDED STEEL STRUCTURES;

EID: 1542506932     PISSN: 14686996     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.stam.2003.10.007     Document Type: Article

References (25)

1. Steel Committee of Kinki Branch: Reconnaissance Report on Damage to Steel Building Structures Observed from the 1995 Hyogoken-Nanbu (Hanshin/Awaji) Earthquake. 1995;. (in Japanese).
2. Okashita K., Ohminami R., Michiba K., Yamamoto A., Tomimatsu M., Tanji Y., Miki C. Investigation of the brittle fracture at the corner of P75 rigid-frame pier in Kobe Harbor Highway during the Hyogoken-Nanbu earthquake. J. Jpn Soc. Civil Engrs. 591/I-43:1998;243. (in Japanese).
3. Thomason P.F. A theory for ductile fracture by internal necking of cavities. J. Inst. Met. 96:1968;360-365.
4. McClintock F.A. A criterion for ductile fracture by the growth of holes. J. Appl. Mech. 35:1968;363-371.
5. McClintock F.A., Kaplan S.M., Berg C.A. Ductile fracture by hole growth in shear bands. Int. J. Fract. Mech. 2:(4):1996;614-627.
6. Rice J.R., Tracey D.M. On the ductile enlargement of voids in triaxial stress fields. J. Mech. Phys. Solids. 17:1969;201-217.
7. Hancock J.W., Mackenzie A.C. On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states. J. Mech. Phys. Solids. 24:1976;147-169.
8. Mackenzie A.C., Hancock J.W., Brown D.K. On the influence of state of stress on ductile failure initiation in high strength steels. Engng Fract. Mech. 9:1977;167-188.
9. Otsuka A., Miyata T., Nishimura S., Kimura M., Mabuchi M. Effect of stress triaxiality on ductile fracture initiation of low strength steels. J. Soc. Mater. Sci. 29:(322):1980;717-723. (in Japanese).
10. Otsuka A., Miyata T., Sakurai T., Iida H. Effect of stress triaxiality on ductile fracture. J. Soc. Mater. Sci. 34:(381):1985;622-626. (in Japanese).
11. Terazawa K., Otani M., Yoshida T., Terai K. Effect of prestrain at high temperatures on the retained ductility of steel. J. Soc. Nav. Architects. 108:1960;419-433. (in Japanese).
12. Ohji K., Ogura K., Mutoh Y. An investigation of processes of ductile fracture using prestrained tough-pitch and sintered coppers. J. Jpn Inst. Met. 41:(2):1977;130-135. (in Japanese).
13. Ohji K., Ogura K., Mutoh Y. Effects of pearlite colony morphology and hydrostatic pressure on ductile fracture processes of ferrite-pearlite carbon steels. J. Jpn Inst. Met. 41:(11):1977;1094-1101. (in Japanese).
14. Morino K., Nisitani H., Beppu T., Nishimura F. Mechanism of decrease in fracture ductility due to prestrain. Trans. Jpn. Soc. Mech. Engng. 59:(567):1993;2540-2545. (in Japanese).
15. Argon A.S., Im J., Needleman A. Cavity formation from inclusions in ductile fracture. Met. Trans. A6:1975;825-837.
16. Ishikawa N., Kobayashi Y., Kurihara M., Osawa K., Toyoda M. Ductile crack initiation behavior of structural steel under cyclic loading. Tetsu-to-Hagane. 85:(1):1999;71-77. (in Japanese).
17. Toyoda M., Ohata M., Ayukawa N., Ohwaki G., Ueda Y., Takeuchi I. Ductile fracture initiation behavior of pipe under a large scale of cyclic bending. Proc. Third Int. Pipeline Technol. Conf., Brugge, Belgium. 2:2000;87-102.
18. Toyoda M., Ohata M., Yokota M., Yasuda O., Hirono M. Criterion for ductile cracking for the evaluation of steel structure under large scale cyclic loading. Proceedings of the 20th International Conference on Offshore Mechanics and Arctic Engineering, Rio de Janeiro, Brazil. 2001;. OMAE01/MAT-3103.
19. Mori H., Fujita H. Behavior of dislocation in copper under reverse stress. J. Phys. Soc. Jpn. 8:(5):1975;1348-1356.
20. Hasegawa T., Yakou T., Kocks U.F. Forward and reverse rearrangement of dislocations in tangled walls. Mater. Sci. Engng. 81:1986;189-199.
21. Yakou T., Hasegawa T., Shimizu M., Karashima S. Relation between Bauschinger effect and work-hardening in copper single crystals. J. Jpn Inst. Met. 47:(7):1983;555-560. (in Japanese).
22. Hu Z., Rauch E.F., Teodosiu C. Work-hardening behavior of mild steel under stress reversal at large strains. Int. J. Plast. 8:1992;839-856.
23. Peeters B., Kalidindi S.R., Van Houtte P., Aernoudt E. A crystal plasticity based work-hardening/softening model for B.C.C. metals under changing strain paths. Acta Mater. 48:2000;2123-2133.
24. Bate P.S., Wilson D.V. Analysis of the Bauschinger effect. Acta Metall. 34:(6):1986;1097-1105.
25. Peeters B., Seefeldt M., Teodosiu C., Kalidindi S.R., Van Houtte P., Aernoudt E. Work-hardening/softening behavior of B.C.C. polycrystals during changing strain paths. I. An integrated model based on substructure and texture evolution, and its prediction of the stress-strain behavior of an IF steel during two-stage strain paths. Acta Mater. 49:2001;1607-1619.