Criterion for ductile cracking for the evaluation of steel structure under large scale cyclic loading

Proceedings of the International Conference on Offshore Mechanics and Arctic Engineering - OMAE

Volumn 3, Issue , 2001, Pages 85-98

  Toyoda, Masao ^a   Ohata, Mitsuru ^a   Yokota, Masaki ^a   Yasuda, Osamu ^b   Hirono, Masahiko ^b  

^a OSAKA UNIVERSITY   (Japan)

^b Takadakiko Co Ltd   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLE FRACTURE; COALESCENCE; CRACK INITIATION; CYCLIC LOADS; FINITE ELEMENT METHOD; FRACTURE TOUGHNESS; NUMERICAL ANALYSIS; PLASTIC FLOW; STEEL STRUCTURES; STRESS CONCENTRATION; TENSILE TESTING;

CYCLIC BENDING; SEISMIC LOADING;

DUCTILE FRACTURE;

EID: 0345549604     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (38)

1. AIJ, Steel Committee of Kinki Branch, 1995, Reconnaissance Report on Damage to Steel Building Structures Observed from the 1995 Hyogoken-Nanbu (Hanshin/Awaji) Earthquake, (in Japanese).
2. Okashita, K., Ohminami, R., Michiba, K., Yamamoto, A., Tomimatsu, M., Tanji, Y. and Miki, C., 1998, "Investigation of the Brittle Fracture at the Corner of P75 Rigid-Frame Pier in Kobe Harbor Highway during the Hyogoken-Nanbu Earthquake," Journals of the Japan Society of Civil Engineers, No. 591/I-43, pp.243-, (in Japanese).
3. Thomason, P. F., 1968, "A Theory for Ductile Fracture by Internal Necking of Cavities," J. Ins. Metals, Vol. 96, pp. 360-365.
4. McClintock, F. A., 1968, "A criterion for Ductile Fracture by the Growth of Holes," J. Appl. Mech, 35, pp. 363-371.
5. McClintock, F. A., Kaplan, S. M. and Berg, C. A., 1996, "Ductile Fracture by Hole Growth in Shear Bands," Int. J. Fracture Mech., Vol. 2, No.4, pp. 614-627.
6. Rice, J. R. and Tracey, D. M., 1969, "On the Ductile Enlargement of Voids in Triaxial Stress fields," J. Mech. Phys. Solids, 17, pp. 201-217.
7. Hancock, J. W. and Mackenzie, A. C., 1976, "On the Mechanisms of Ductile Failure in High-Strength Steels Subjected to Multi-Axial Stress-States," J. Mech. Phys. Solids, 24, pp. 147-169.
8. Mackenzie, A. C., Hancock, J.W. and Brown, O.K., 1977, "On the Influence of State of Stress on Ductile Failure Initiation in High Strength Steels," Eng. Fract. Mech., Vol. 9, pp. 167-188.
9. Otsuka, A., Miyata, T., Nishimura, S., Kimura, M. and Mabuchi, M., 1980, "Effect of Stress Triaxiality on Ductile Fracture Initiation of Low Strength Steels," J. Soc. Mater. Sci., Vol. 29, No. 322, pp. 717-723, (in Japanese).
10. Otsuka, A., Miyata, T., Sakurai, T. and Iida, H., 1985,"Effect of Stress Triaxiality on Ductile Fracture,' J. Soc. Mater. Sci., Vol. 34, No. 381, pp. 622-626, (in Japanese).
11. Tohgo, K., Otsuka, A. and Gao, H.-W., 1988, "Behavior of Ductile Crack Initiation from a Notch under Mixed Mode Loading," J. Soc. Mater. Sci., Vol. 37, No. 419, pp. 885-890, (in Japanese).
12. Tohgo, K., Otsuka, A. and Gao, H.-W., 1989, "Mechanism of Ductile Crack Initiation from a Notch under Mode II Loading," J. Soc. Mater. Sci., Vol. 38, No. 432, pp. 1014-1018, (in Japanese).
13. Ohji, K., Ogura, K., Ohmori, K. and Nomizu, T., 1980, " Observations of Microvoid and Critical Condition for Its Initiation in Ductile Failure of High Strength Materials," J. Soc. Mat. Sci., Vol. 29, No. 321, pp. 550-555, (in Japanese).
14. Clayton, J. Q. and Knott, J. F., 1976, "Observation of fibrous fracture modes in a prestrained low-alloy steel," Met. Sci., pp. 63-71.
15. Hahn, G. T. and Rosenfield, A. R., 1975, "Metallurgical Factors Affecting Fracture Toughness of Aluminum Alloy," Metall. Trans. A, Vol. 6A, pp. 653-668.
16. Okamoto, S., Terasaki, F. and Kunitake, T., 1977, "Influence of MnS Inclusion on Ductility and Ductile Fracture of High Strength Steels," Tetsu-to-Hagane,Vol. 63, No. 12, pp. 1878-1886, (in Japanese).
17. Giovanola, J. H., Kirkpatrick, S. W. and Croker, J. E., 1999, "Fracture of Geometrically Scaled, Notched Three-Point-Bend Bars of High Strength Steel," Eng. Fract. Mech., Vol. 62, pp. 291-310.
18. Miyata, T., Otsuka, A. and Okuyama, H., 1988, "Shear Fracture under Combined Tension and Tortion Stresses," J. Soc. Mater. Sci., Vol. 37, No. 420, pp. 1036-1042, (in Japanese).
19. Tohgo, K., Otsuka, A. and Gao, H.-W., 1990, "Behavior of Ductile Crack Initiation from a Crack under Mixed Mode Loading," J. Soc. Mater. Sci., Vol. 39, No. 443, pp. 1089-1094, (in Japanese).
20. Nishitani, H. and Makabe, C., 1982, "Mechanism of Ductile Fracture in Tensile Test of 7: 3 Brass," J. Soc. Mater. Sci., Vol. 31, No. 344, pp. 452-457, (in Japanese).
21. Terazawa, K., Otani, M., Yoshida, T. and Terai, K., 1960, "Effect of Prestrain at High temperatures on the Retained Ductility of Steel," J. Soc. Nav. Architects, Vol. 108, pp. 419-433, (in Japanese).
22. Ohji, K., Ogura, K. and Mutoh, Y., 1977, "An Investigation of Processes of Ductile Fracture Using Prestrained Tough-Pitch and Sintered Coppers," J. Jpn. Inst. Metals, Vol. 41, No. 2, pp. 130-135, (in Japanese).
23. Ohji, K., Ogura, K. and Mutoh, Y., 1977, "Effects of Pearlite Colony Morphology and Hydrostatic Pressure on Ductile Fracture Processes of Ferrite-Pearlite Carbon Steels," J. Jpn Inst. Metals, Vol. 41, No. 11, pp. 1094-1101, (in Japanese).
24. Morino, K., Nisitani, H., Beppu, T. and Nishimura, F., 1993, "Mechanism of Decrease in Fracture Ductility due to Prestrain," Trans. Jpn. Soc. Mech. Eng., Vol. 59, No. 567, pp. 2540-2545, (in Japanese).
25. Argon, A. S., Im, J. and Needleman, A., 1975, "Cavity Formation from Inclusions in Ductile Fracture," Met. Trans., A, 6, pp. 825-837.
26. Argon, A. S. and Im, J., 1975, "Separation of Second Phase Particles in Spheroidized 1045 Steel, Cu-0.6Pct Cr Alloy, and Maraging Steel in Plastic Straining," Met. Trans., A, 6, pp. 839-851.
27. Gardner, R. N. and Wilsdorf, H.G.F., 1980, "Ductile Fracture Initiation in Pure a-FE: PartII. Microscopic Observation of an Initiation Mechanism," Met. Trans., 11, pp. 659-669.
28. Beremin, F. M., 1981, "Cavity Formation from Inclusion in Ductile Fracture of A508 Steel," Met. Trans, 12, pp. 723-731.
29. Goods, S. H. and Brown, L.M., 1979, "The Nucleation of Cavities by Plastic Deformation," Acta Met., Vol. 27, pp. 115.
30. Otsuka, A., Nishimura, S. and Miyata, T., 1982, "Local Criterion of Ductile Crack Growth," J. Soc. Mater. Sci., Vol. 31, No. 344, pp. 447-451, (in Japanese).
31. Ishikawa, N., Kobayashi, Y., Kurihara, M., Osawa, K. and Toyoda, M., 1999, "Ductile Crack Initiation Behavior of Structural Steel under Cyclic Loading," Tetsu-to-Hagane, Vol. 85, No. 1, pp. 71-77, (in Japanese).
32. Hibbitt, Karlsson & Sorensen, Inc., 1998, ABAQUS/Standard User's Manuals, Version 5.8 Vols. 1 to 3.
33. Davidenkov, N. N. and Spiridonova, N. I., 1952, Proc. Am. Soc. Test. Mat., 46, pp. 1147.
34. Yamada, Y., 1978, "Constitutive Modelling of Inelastic Behavior and Numerical Solution of Nonlinear Problems by the Finite Element Method," Computers and Structures, Vol. 8, pp. 533-543.
35. Zhonghua, L. and Haicheng, G., 1990, "Bauschinger Effect and Residual Phase Stresses in Two Ductile-Phase Steels: Part I. The Effect of Microstructure and Mechanical Properties of the Constituent Phases on Bauschinfer Effect and Residual Phase Stresses," Met. Trans.,A, Vol. 21 A, pp. 717-724.
36. Zhonghua, L. and Haicheng, G., 1990, "Bauschinger Effect and Residual Phase Stresses in Two Ductile-Phase Steels: Part II. The Effect of Microstructure and Mechanical Properties of the Constituent Phases on Bauschinfer Effect and Residual Phase Stresses," Met. Trans.,A, Vol. 21 A, pp. 725-732.
37. Horstemeyer, M. F., 1998, "Damage Influence on Bauschinger Effect of a Cast A356 Aluminum Alloy," Scripta Materialia, Vol 39, No. 11, pp. 1491-1495.
38. Toyoda, M., Ohata, M., Ayukawa, N., Ohwaki, G., Ueda, Y. and Takeuchi, I., 2000, "Ductile Fracture Initiation Behavior of Pipe under A Large Scale of Cyclic Bending," Proc. 3rd Int. Pipeline Technology Conf., Brugge, Belgium, Vol. 2, pp. 87-102.