Investigation of the rolling contact fatigue resistance of laser cladded twin-disc specimens: FE simulation of laser cladding, grinding and a twin-disc test

International Journal of Fatigue

Volumn 27, Issue 6, 2005, Pages 702-714

  Ringsberg, Jonas W ^a   Skyttebol, Anders ^a   Josefson, B Lennart ^a  

^a CHALMERS UNIVERSITY OF TECHNOLOGY   (Sweden)

Author keywords

Finite element analysis; Laser cladding; Multiaxial fatigue; Rolling contact fatigue; Thermo mechanical analysis; Twin disc test

Indexed keywords

COATED MATERIALS; COMPUTER SIMULATION; ELASTIC MODULI; FATIGUE OF MATERIALS; FINITE ELEMENT METHOD; LASER BEAM WELDING; POISSON RATIO; RAILS; RESIDUAL STRESSES; SPECIFIC HEAT; SURFACE TREATMENT; TENSORS; THERMAL EXPANSION;

LASER CLADDING; MULTIAXIAL FATIGUE; ROLLING CONTACT FATIGUE; THERMO-MECHANICAL ANALYSIS; TWIN-DISC TEST;

ROLLING;

EID: 14544280223     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2004.10.006     Document Type: Article

References (28)

1. M.K. Stanford, and V.K. Jain Friction and wear characteristics of hard coatings Wear 251 2001 990 996
2. L. Shepeleva, B. Medres, W.D. Kaplan, M. Bamberger, and A. Weisheit Laser cladding of turbine blades Surf Coat Technol 125 2000 45 48
3. E.J.M. Hiensch, F.J. Franklin, J.C.O. Nielsen, J.W. Ringsberg, G.J. Weeda, and A. Kapoor Prevention of RCF damage in curved track through development of the INFRA-STAR two-material rail Fatigue Fracture Eng Mater Struct 26 2003 1007 1017
4. Hiensch EJM, Larsson PO, Nilsson O, Levy D, Kapoor A, Franklin FJ, et al. Two-material rail development: field test results regarding rolling contact fatigue and squeal noise behaviour. In: Ekberg A, Kabo E, Ringsberg JW, editors. Proceedings of the 6th international conference on contact mechanics and wear of rail/wheel systems-CM2003. Göteborg, Sweden: Vasastadens Bokbinderi AB; 2003. p.39-47 [Wear, in press].
5. Ringsberg JW, Franklin FJ, Josefson BL, Kapoor A, Nielsen JCO. Fatigue evaluation of surface coated railway rails using shakedown theory, finite element calculations, and lab and field trials. Research report 2004:7; 2004 Department of Applied Mechanics, Chalmers University of Technology, Göteborg, Sweden: Int J Fatigue, [in press].
6. A. Rosselet Modelling of residual stresses in laser cladding M. Cross J. Campbell Proceedings of the 7th conference on modeling of casting, welding and advanced solidification processes 1995 Minerals, Metals and Materials Society London, UK/Warrendale, PA, USA 327 334
7. A.P. Wu, J.L. Ren, Z.S. Peng, H. Murakawa, and Y. Ueda Numerical simulation for the residual stresses of Stellite hard-facing on carbon steel J Mater Proc Technol 101 2000 70 75
8. M. Mahdi, and L. Zhang Applied mechanics in grinding. Part 7. Residual stresses induced by the full coupling of mechanical deformation, thermal deformation and phase transformation Int J Mach Tools Manuf 39 1999 1285 1298
9. R. Vilar Laser cladding Int J Powder Met 37 2001 31 48
10. J. Grum A review of the influence of grinding conditions on resulting residual stresses after induction surface hardening and grinding J Mater Proc Technol 114 2001 212 226
11. P.N. Moulik, H.T.Y. Yang, and S. Chandrasekar Simulation of thermal stresses due to grinding Int J Mech Sci 43 2001 831 851
12. J. Grum, and P. Žerovnik Residual stresses in steels after heat treatments and grinding T. Ericsson M. Odén A. Andersson Proceedings of the 5th international conference on residual stresses - ICRS-5; 1997 Linköping University, Department of Mechanical Engineering, Division of Engineering Materials Linköping, Sweden 250 255
13. D.I. Fletcher, and J.H. Beynon Development of a machine for closely controlled rolling contact fatigue and wear testing J Test Eval 28 2000 267 275
14. K. Dang Van, G. Cailletaud, J.F. Flavenot, A. Le Douaron, and H.P. Lieurade Criterion for high cycle fatigue failure under multiaxial loading M.W. Brown K.J. Miller Biaxial and multiaxial fatigue, EGF 3 1989 Mechanical Engineering Publications London, UK 459 478
15. J.W. Ringsberg Life prediction of rolling contact fatigue crack initiation Int J Fatigue 23 2001 575 586
16. A. Conde, F. Zubiri, and J. De Damborenea Cladding of Ni-Cr-B-Si coatings with a high power diode laser Mater Sci Eng A334 2002 233 238
17. Deloro stellite. http://www.stellite.com ; 2004.
18. S. Niederhauser, and B. Karlsson Mechanical properties of laser cladded steel Mater Sci Technol 19 2003 1611 1616
19. Hibbitt, Karlsson & Sorensen. ABAQUS/Analysis User's Manual version 6.4. ABAQUS, Inc., Pawtucket, RI, USA; 2003.
20. Niederhauser S, Karlsson B, Sotkovszki P. Microstructural development in the heat affected zone of a laser cladded steel plate, Submitted for publication. Zeitschrift für Metallkunde.
21. J. Basu, S.L. Srimani, and D.S. Gupta Rail behaviour during cooling after hot rolling J Strain Anal 39 2004 15 24
22. Skyttebol A, Sotkovszki P, Josefson BL, Johansson H. Microstructural evaluation and mechanical properties of the welded zone in flash-butt welded rails. Research report 2004:6, Department of Applied Mechanics, Chalmers University of Technology, Göteborg, Sweden; 2004.
23. D. Radaj Welding residual stresses and distortion 2003 DVS Düsseldorf, Germany
24. L-E. Lindgren Finite element modeling and simulation of welding. Part 2. improved material modeling J Therm Stress 24 2001 195 231
25. Rowan T. Functional stability analysis of numerical algorithms. Doctoral thesis, University of Texas, Austin, TX, USA; May 1990.
26. J.W. Ringsberg, M. Loo-Morrey, B.L. Josefson, A. Kapoor, and J.H. Beynon Prediction of fatigue crack initiation for rolling contact fatigue Int J Fatigue 22 2000 205 215
27. ASTM E837-99 Standard test method for determining residual stresses by the hole-drilling strain-gage method Annual books of ASTM standards vol.03.01 2000 American Society for Testing and Materials (ASTM) International West Conshohocken, PA, USA p. 675-684
28. K.L. Johnson Contact mechanics 1987 Cambridge University Press Cambridge