Volumn 17, Issue 3, 2004, Pages 91-97

Residual stress measurement and fatigue crack growth prediction after cold expansion of cracked fastener holes

Author keywords

Cracking; Fasteners; Fatigue tests; Fracture mechanics; Residual stress; X ray diffraction

Indexed keywords

COMPRESSIVE STRESS; CRACK INITIATION; CRACK PROPAGATION; EXPANSION; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE MECHANICS; NEUTRON DIFFRACTION; RESIDUAL STRESSES; X RAY DIFFRACTION ANALYSIS;

EID: 14044273659     PISSN: 08931321     EISSN: None     Source Type: Journal    
DOI: 10.1061/(ASCE)0893-1321(2004)17:3(91)     Document Type: Article
Times cited : (23)

References (28)
  • 1
    • 0031672228 scopus 로고    scopus 로고
    • Experimental investigation on the effects of cold expansion of fastener holes
    • Ball, D., and Lowry, D. R. (1998). "Experimental investigation on the effects of cold expansion of fastener holes." Fatigue Fract. Eng. Mater. Struct., 21(1), 17-34.
    • (1998) Fatigue Fract. Eng. Mater. Struct. , vol.21 , Issue.1 , pp. 17-34
    • Ball, D.1    Lowry, D.R.2
  • 2
    • 0028739776 scopus 로고
    • Fatigue crack growth in residual stress fields: Experimental results and modelling
    • Beghini, M., Bertini, L., and Vitale, E. (1994). "Fatigue crack growth in residual stress fields: Experimental results and modelling." Fatigue Fract. Eng. Mater. Struct., 17(12), 1433-1444.
    • (1994) Fatigue Fract. Eng. Mater. Struct. , vol.17 , Issue.12 , pp. 1433-1444
    • Beghini, M.1    Bertini, L.2    Vitale, E.3
  • 3
    • 0025720261 scopus 로고
    • Modelling residual stresses and fatigue crack growth at cold-expanded fastener holes
    • Clark, G. (1991). "Modelling residual stresses and fatigue crack growth at cold-expanded fastener holes." Fatigue Fract. Eng. Mater. Struct., 14(5), 579-589.
    • (1991) Fatigue Fract. Eng. Mater. Struct. , vol.14 , Issue.5 , pp. 579-589
    • Clark, G.1
  • 4
    • 0000173615 scopus 로고    scopus 로고
    • Use of Rietveld refinement for elastic macrostrain determination and for evaluation of plastic strain history from diffraction spectra
    • Daymond, M. R., Bourke, M. A. M., von Dreele, R. B., Clausen, B., and Lorentzen, T. (1997). "Use of Rietveld refinement for elastic macrostrain determination and for evaluation of plastic strain history from diffraction spectra." J. Appl. Phys., 82(4), 1554-1562.
    • (1997) J. Appl. Phys. , vol.82 , Issue.4 , pp. 1554-1562
    • Daymond, M.R.1    Bourke, M.A.M.2    Von Dreele, R.B.3    Clausen, B.4    Lorentzen, T.5
  • 5
    • 0141943176 scopus 로고
    • The effect of slip distribution on the mechanical properties of aluminum alloys
    • J. Bilde-Sorenson, ed., Risø National
    • Edwards, L. (1983). "The effect of slip distribution on the mechanical properties of aluminum alloys." Deformation of multi-phase and particle containing materials, J. Bilde-Sorenson, ed., Risø National
    • (1983) Deformation of Multi-phase and Particle Containing Materials
    • Edwards, L.1
  • 6
    • 14044251665 scopus 로고    scopus 로고
    • Laboratory, Risø, Denmark, 442-450
    • Laboratory, Risø, Denmark, 442-450.
  • 7
    • 0011409261 scopus 로고    scopus 로고
    • Neutron diffraction determination of the complete 3D residual stress distribution surrounding a cold-expanded hole
    • S. Denis, J.-L. Lebrun, B. Bourniquel, M. Barrai, and J.-F. Flavenot, eds., ENSAM, Paris
    • Edwards, L., and Wang, D. Q. (1996). "Neutron diffraction determination of the complete 3D residual stress distribution surrounding a cold-expanded hole." Proc., 4th European Conf. on Residual Stresses, S. Denis, J.-L. Lebrun, B. Bourniquel, M. Barrai, and J.-F. Flavenot, eds., ENSAM, Paris, 619-626.
    • (1996) Proc., 4th European Conf. on Residual Stresses , pp. 619-626
    • Edwards, L.1    Wang, D.Q.2
  • 8
    • 0032049137 scopus 로고    scopus 로고
    • Fatigue crack/residual stress interactions and their implications for damage tolerant design
    • Fitzpatrick, M. E., and Edwards, L. (1998). "Fatigue crack/residual stress interactions and their implications for damage tolerant design." J. Mater. Eng. Perform., 7(2), 190-198.
    • (1998) J. Mater. Eng. Perform. , vol.7 , Issue.2 , pp. 190-198
    • Fitzpatrick, M.E.1    Edwards, L.2
  • 9
    • 82255161038 scopus 로고
    • Cold expansion of holes using the standard split sleeve system (Cx) and countersink cold expansion
    • Seattle
    • Fatigue Technology Incorporated (FTI). (1994). "Cold expansion of holes using the standard split sleeve system (Cx) and countersink cold expansion." Engineering Process Specification 8101C, Seattle.
    • (1994) Engineering Process Specification 8101C
  • 10
    • 0037669177 scopus 로고
    • Rep. MCIC-HB-01R, Air Force Wright Aeronautical Laboratories, Wright-Patterson Air Force Base, Ohio
    • Gallagher, J. (1983). "Damage tolerant design handbook, Vol. 3." Rep. MCIC-HB-01R, Air Force Wright Aeronautical Laboratories, Wright-Patterson Air Force Base, Ohio.
    • (1983) Damage Tolerant Design Handbook , vol.3
    • Gallagher, J.1
  • 11
    • 14044274420 scopus 로고    scopus 로고
    • Effect of cold expansion on the residual stress distribution and fatigue properties in a alloy 7050 containing fastener holes with residual fatigue cracks
    • T. Ericsson, M. Odén, and A. Andersson, eds., Univ. of Linköping, Linköping, Sweden
    • Holdway, P., and Cook, R. (1997). "Effect of cold expansion on the residual stress distribution and fatigue properties in a alloy 7050 containing fastener holes with residual fatigue cracks." Proc., 5th Int. Conf. on Residual Stresses, T. Ericsson, M. Odén, and A. Andersson, eds., Univ. of Linköping, Linköping, Sweden, 76-81.
    • (1997) Proc., 5th Int. Conf. on Residual Stresses , pp. 76-81
    • Holdway, P.1    Cook, R.2
  • 12
    • 0002059820 scopus 로고
    • On the stresses in the neighbourhood of a circular hole in a strip under tension
    • Howland, R. C. (1930). "On the stresses in the neighbourhood of a circular hole in a strip under tension." Philos. Trans. R. Soc., A229, 49-86.
    • (1930) Philos. Trans. R. Soc. , vol.A229 , pp. 49-86
    • Howland, R.C.1
  • 13
    • 0031548562 scopus 로고    scopus 로고
    • ENGIN-a new instrument for engineers
    • Johnson, M. W., Edwards, L., and Withers, P. J. (1997). "ENGIN-a new instrument for engineers." Physica B, 234, 1141-1143.
    • (1997) Physica B , vol.234 , pp. 1141-1143
    • Johnson, M.W.1    Edwards, L.2    Withers, P.J.3
  • 14
    • 0028336287 scopus 로고
    • Influence of residual stresses on fatigue crack growth at stress-coined holes
    • Josefson, B. L., and Karlsson, S. (1994). "Influence of residual stresses on fatigue crack growth at stress-coined holes." Eng. Fract. Mech., 234-236, 13-27.
    • (1994) Eng. Fract. Mech. , vol.234-236 , pp. 13-27
    • Josefson, B.L.1    Karlsson, S.2
  • 15
    • 3343023298 scopus 로고
    • D6ac steel bolt hole life improvement, F-111 Coldwork Modification Development Program (Phase II)
    • General Dynamics, Forth Worth Div., Fort Worth, Tex.
    • Lowry, D. R. (1991). "D6ac steel bolt hole life improvement, F-111 Coldwork Modification Development Program (Phase II)." Tech. Rep. FZS-12-588, General Dynamics, Forth Worth Div., Fort Worth, Tex.
    • (1991) Tech. Rep. , vol.FZS-12-588
    • Lowry, D.R.1
  • 17
    • 0000303043 scopus 로고
    • Stress intensity equations for cracks in three-dimensional finite bodies subjected to tension and bending loads
    • S. N. Atluri, ed., Elsevier, London
    • Newman, J. C., Jr., and Raju, I. S. (1986). "Stress intensity equations for cracks in three-dimensional finite bodies subjected to tension and bending loads." Computational methods in mechanics of fracture, S. N. Atluri, ed., Elsevier, London, 311-344.
    • (1986) Computational Methods in Mechanics of Fracture , pp. 311-344
    • Newman Jr., J.C.1    Raju, I.S.2
  • 19
    • 0032595115 scopus 로고    scopus 로고
    • Effect of residual stress around cold worked holes on fracture under superimposed mechanical load
    • Pavier, M. J., Poussard, C. G., and Smith, D. J. (1999). "Effect of residual stress around cold worked holes on fracture under superimposed mechanical load." Eng. Fract. Mech., 63(6), 751-773.
    • (1999) Eng. Fract. Mech. , vol.63 , Issue.6 , pp. 751-773
    • Pavier, M.J.1    Poussard, C.G.2    Smith, D.J.3
  • 21
    • 0001925686 scopus 로고
    • The role of the peak location method in X-ray stress measurement
    • SEM, Bethel, Conn.
    • Pfeiffer, W. (1994). "The role of the peak location method in X-ray stress measurement." Proc., 4th Int. Conf. on Residual Stresses, SEM, Bethel, Conn., 148-155.
    • (1994) Proc., 4th Int. Conf. on Residual Stresses , pp. 148-155
    • Pfeiffer, W.1
  • 22
    • 85167823373 scopus 로고
    • Stress intensity factors for through and part-through cracks originating at fastener holes
    • ASTM, Philadelphia
    • Shah, R. C. (1976). "Stress intensity factors for through and part-through cracks originating at fastener holes." Mechanics of crack growth, ASTM STP 590, ASTM, Philadelphia, 429-459.
    • (1976) Mechanics of Crack Growth, ASTM STP , vol.590 , pp. 429-459
    • Shah, R.C.1
  • 24
    • 0004274342 scopus 로고
    • Cambridge University Press, Cambridge, U.K.
    • Suresh, S. (1991). Fatigue of materials, Cambridge University Press, Cambridge, U.K.
    • (1991) Fatigue of Materials
    • Suresh, S.1
  • 25
    • 0033339605 scopus 로고    scopus 로고
    • A strip yield analysis of fatigue crack growth in the residual stress field
    • Wang, G. S. (1999). "A strip yield analysis of fatigue crack growth in the residual stress field." Int. J. Fract., 96(3), 247-277.
    • (1999) Int. J. Fract. , vol.96 , Issue.3 , pp. 247-277
    • Wang, G.S.1
  • 27
    • 0031340702 scopus 로고    scopus 로고
    • Relaxation of residual stresses at cold-worked fastnener holes due to fatigue loading
    • Özdemir, A. T., and Edwards, L. (1997). "Relaxation of residual stresses at cold-worked fastnener holes due to fatigue loading." Fatigue Fract. Eng. Mater. Struct., 20(10), 1443-1451.
    • (1997) Fatigue Fract. Eng. Mater. Struct. , vol.20 , Issue.10 , pp. 1443-1451
    • Özdemir, A.T.1    Edwards, L.2
  • 28
    • 0001580621 scopus 로고
    • Rietveld refinement with spallation neutron powder diffraction data
    • Von Dreele, R. B., Jorgensen, J. D., and Windsor, C. G. (1982). "Rietveld refinement with spallation neutron powder diffraction data." J. Appl. Crystallogr., 15, 581-589.
    • (1982) J. Appl. Crystallogr. , vol.15 , pp. 581-589
    • Von Dreele, R.B.1    Jorgensen, J.D.2    Windsor, C.G.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.