Threshold intensity factors as lower boundaries for crack propagation in ceramics

BioMedical Engineering Online

Volumn 3, Issue , 2004, Pages

  Marx, Rudolf ^a   Jungwirth, Franz ^a   Walter, Per Ole ^a  

^a UNIVERSITY HOSPITAL RWTH AACHEN   (Germany)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION ASSISTED STRESSES; CRACK TIPS; DENTAL RESTORATIONS; THRESHOLD STRESS INTENSITY FACTORS;

ALUMINA; BODY FLUIDS; CRACK PROPAGATION; INDENTATION; INTERFACIAL ENERGY; RESIDUAL STRESSES; STRESS INTENSITY FACTORS; TOUGHNESS; ZIRCONIA;

CERAMIC MATERIALS;

ALUMINUM OXIDE; ZIRCONIUM OXIDE; CERAMICS; DENTAL MATERIAL; ZIRCONIUM;

ARTICLE; BODY FLUID; COMPRESSIVE STRENGTH; COMPUTER PROGRAM; CONTROLLED STUDY; CORROSION; DENTAL SURGERY; EUROPE; MECHANICAL STRESS; TOOTH PROSTHESIS; VELOCITY; CERAMICS; CHEMISTRY; DEVICE FAILURE ANALYSIS; HUMIDITY; MATERIALS TESTING; PROCEDURES; SURFACE PROPERTY;

CERAMICS; DENTAL MATERIALS; EQUIPMENT FAILURE ANALYSIS; HUMIDITY; MATERIALS TESTING; STRESS, MECHANICAL; SURFACE PROPERTIES; ZIRCONIUM;

EID: 13144290924     PISSN: 1475925X     EISSN: None     Source Type: Journal    
DOI: 10.1186/1475-925X-3-41     Document Type: Article

References (23)

1. Lawn B: Fracture of brittle solids Cambridge: University Press; 1991.
2. Wan KT, Lathabai S, Lawn BR: Crack Velocity Functions and Thresholds in Brittle Solids. J Eur Ceram Soc 1990, 6: 59-268.
3. Cook RF: Influence of crack velocity thresholds on stabilized nonequilibrium fracture. J Appl Phys 1989, 65: 902-1910.
4. De Aza AH, Chevalier J, Fantozzi G, Schehl M, Torrecillas R: Crack growth resistance of alumina, zirkonia and zirkonia toughened alumina ceramics for joint prostheses. Biomaterials 2002, 23: 37-945.
5. Drouin JM, Cales B, Chevalier J, Fantozzi G: Fatigue behaviour of zirconia hip joint heads - experimental results and finite element analysis. J Biomed Mater Research 1997, 34: 49-155.
6. Kocer C, Collins RE: Measurement of Very Slow Crack Growth in Glass. J Am Ceram Soc 2001, 84:2585-2593.
7. 3 with submicron grain size. J Eur Ceram Soc 2003, 23:81-89.
8. Sglavo VM, Green DJ: Threshold Stress Intensity Factor in Soda-Lime Silicate Glass by Interrupted Static Fatigue Test. J Eur Ceram Soc 1996, 16:645-651.
9. Sglavo VM, Green DJ: The interrupted static fatigue test for evaluating threshold stress intensity factor in ceramic materials: A numerical analysis. J Eur Ceram Soc 1995, 15:777-785.
10. Evans AG: A method for evaluating the time-dependent failure characteristics of brittle materials - and its application to polycrystalline alumina. J of material science 1972, 7: 137-1146.
11. Salomonson J, Zeng K, Rowcliffe D: Decay of residual stress at indentation cracks during slow crack growth in soda-lime glass. Acta mater 1996, 44:543-546.
12. Cook RF, Liniger EG: Kinetics of Indentation Cracking in Glass. J Am Ceram Soc 1993, 76:1096-1105.
13. Sglavo VM, Green DJ: Indentation Determination of Fatigue Limits in Silicate Glasses. J Am Ceram Soc 1999, 82: 269-1274.
14. Seidel J, Rödel J: Measurement of Crack Tip Toughness in Alumina as a Function of Grain Size. J Am Ceram Soc 1997, 80:433-438.
15. Irwin GR: Fracture. In In Handbuch der Physik Volume 6. Berlin: Springer; 1958.
16. Munz D, Fett T: Ceramics - Mechanical Properties, Failure Behaviour, Materials Selection Berlin: Springer; 1999.
17. Rhee YW, Kim HW, Deng Y, Lawn BR: Brittle Fracture versus Quasi Plasticity in Ceramics: A simple Predictive Index. J Am Ceram Soc 2001, 84:561-565.
18. Chevalier J, Olagnon C, Fantozzi G, Calès B: Crack propagation behavior of Y-TZP Ceramics. J Am Ceram Soc 1995, 78:1889-1894.
19. Dauskardt RH, Yu W, Ritchie RO: Fatigue Crack Propagation in Transformation-Toughened Zirconia Ceramic. J Am Ceram Soc 1987, 70:C-248-C-252.
20. Shimizu K, Oka M, Kumar P, Kotoura Y, Yamamuro T, Makinouchi K, Nakamura T: Time-dependent changes in the mechanical properties of zirconia ceramic. J Biomed Mater Res 1993, 27:729-734.
21. 2 (MgO). J of Mat Science 1986, 21:297-300.
22. Marx R, Fischer H, Weber M, Jungwirth F: Rissparameter und Weibullmodule: unterkritisches Risswachstum und Langzeitfestigkeit vollkeramischer Materialien. Dtsch Zahnärztl Z 2001, 56: 0-98.
23. Fischer J, Krämer V, Kappert HF: Qualitative Untersuchungen zur Oberflächen-Kristallisation dentaler Glaskeramik (Dicor). Dtsch Zahnärztl Z 1989, 44:891-893.