Threshold stress intensity factor in soda-lime silicate glass by interrupted static fatigue test

Journal of the European Ceramic Society

Volumn 16, Issue 6, 1996, Pages 645-651

  Sglavo, Vincenzo M ^a   Green, David J ^a  

^a PENNSYLVANIA STATE UNIVERSITY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; GLASS; SILICATE; STRESS INTENSITY FACTORS;

EID: 0029671496     PISSN: 09552219     EISSN: None     Source Type: Journal    
DOI: 10.1016/0955-2219(95)00176-X     Document Type: Article

References (33)

1. Wiederhorn, S. M. & Bolz, L. H., Stress corrosion and static fatigue of glass. J. Am. Ceram. Soc., 53 (10) (1970) 543-8.
2. Evans, A. G., A simple method for evaluating slow crack growth in brittle materials. Int. J. Fract., 9 (3) (1973) 267-75.
3. Wiederhorn, S. M., Subcritical crack growth in ceramics. In Fracture Mechanics of Ceramics, ed. R. C. Bradt, D. P. H. Hasselmann & F. F. Lange. Plenum, New York, 1974, Vol. 2. pp. 613-46.
4. Evans, A. G., Slow crack growth in brittle materials under dynamic loading conditions. Int. J. Fract., 10 (2) (1974) 251-9.
5. Simmons, C. J. & Freiman, S. W., Effect of corrosion processes on subcritical crack growth in glass. J. Am. Ceram. Soc., 64 (11) (1981) 683-6.
6. Wan, K., Lathabai, S. & Lawn, B. R., Crack velocity functions and threshold in brittle solids. J. Eur. Ceram. Soc., 6 (1990) 259-68.
7. Gehrke, E., Ullner, C. & Hähnert, M., Effect of corrosive media on crack growth of model glasses and commercial silicate glasses. Glastech. Ber., 63(9) (1990) 255-65.
8. Gehrke, E., Ullner, C. & Hähnert, M., Fatigue limit and crack arrest in alkali-containing silicate glasses. J. Mater. Sci., 26 (1991) 5445-55.
9. Stuart, D. A. & Anderson, O. L., Dependence of ultimate strength of glass under constant load on temperature, ambient atmosphere, and time. J. Am. Ceram. Soc., 36 (12) (1953) 416-24.
10. Shand, E. B., Experimental study of fracture of glass: I, The fracture process. J. Am. Ceram. Soc., 37 (2) (1954) 52-60.
11. Mould, R. E. & Southwick, R. D., Strength and static fatigue of abraded glass under controlled ambient conditions: II, Effect of various abrasions and the universal fatigue curve. J. Am. Ceram. Soc., 42 (12) (1959) 582-92.
12. Mould, R. E., Strength and static fatigue of abraded glass under controlled ambient conditions: III, Aging of fresh abrasions. J. Am. Ceram. Soc., 43 (3) (1960) 160-7.
13. Shand, E. B., Fracture velocity and fracture energy of glass in the fatigue range. J. Am. Ceram. Soc., 44 (1) (1961) 21-6.
14. Mould, R. E., Strength and static fatigue of abraded glass under controlled ambient conditions: IV, Effect of surrounding medium. J. Am. Ceram. Soc., 4 (10) (1961) 481-91.
15. Watanabe, M., Caporali, R. V. & Mould, R. E., The effect of chemical composition on the strength and static fatigue of soda-lime glass. Phys. Chem. Glasses, 2 (1) (1961) 12-23.
16. Shand, E. B., Strength of glass - the Griffith method revised. J. Am. Ceram. Soc., 48 (1) (1965) 43-9.
17. Hillig, W. B. & Charles, R. J., Surfaces, stresses-dependent surface reactions, and strength. In High Strength Materials, ed. V.F. Zakay. John Wiley & Sons, New York, 1965, pp. 683-705.
18. Pavelchek, E. K. & Doremus, R. H., Static fatigue in glass - a reappraisal. J. Non-Cryst. Solids, 20 (1976) 305-21.
19. Gehrke, E., Ullner, C. & Hähnert, M., Strength and fatigue of some binary and ternary silicate glasses. J. Non-Cryst. Solids, 80 (1986) 269-76.
20. Gehrke, E., Ullner, C. & Hähnert, M., Correlation between multistage crack growth and time-dependent strength in commercial silicate glasses. Part 1. Influence of ambient media and types of initial cracks. Glastech. Ber., 60 (8) (1987) 268-78.
21. Gehrke, E., Ullner, C. & Hähnert, M., Correlation between multistage crack growth and time-dependent strength in commercial silicate glasses. Part 2. Influence of surface treatment. Glastech. Ber., 60 (10) (1987) 340-5.
22. Evans, A. G., A method for evaluating the time-dependent failure characteristics of brittle materials - and its application to polycrystalline alumina. J. Mater. Sci., 7 (1972) 1137-46.
23. Michalske, T. A., The stress corrosion limit: its measurement and implications. In Fracture Mechanics of Ceramics, ed. R. C. Bradt, D. P. H. Hasselmann & F. F. Lange. Plenum Press, New York, 1983, Vol. 5, pp. 277-89.
24. Sglavo, V. M. & Green, D. J., The interrupted static fatigue test for evaluating threshold stress intensity factor in ceramic materials: a theoretical analysis. J. Eur. Ceram. Soc., 15 (1995) 777-86.
25. Wilkins, B. J. S. & Dutton, R., Static fatigue limit with particular reference to glass. J. Am. Ceram. Soc., 59 (3-4) (1975) 108-12.
26. Minford, E. J. & Tressler, R. E., Determination of threshold stress intensity for crack growth at high temperature in silicon carbide ceramics. J. Am. Ceram. Soc., 66 (5) (1983) 338-40.
27. Minford, E. J., Kupp, D. M. & Tressler, R. E., Static fatigue limit for sintered silicon carbide at elevated temperatures. J. Am. Ceram. Soc., 66 (11) (1983) 769-73.
28. Foley, M. R. & Tressler, R. E., Threshold stress intensity for crack growth at elevated temperatures in a silicon nitride ceramic. Adv. Ceram. Mater., 34 (1988) 383-6.
29. Yavuz, B. O. & Tressler, R. E., Threshold stress intensity for crack growth in silicon carbide ceramics. J. Am. Ceram. Soc., 76(4) (1993) 1017-24.
30. Hayashi, K., Easler, T. E. & Bradt, R. C., A fracture statistics estimate of the fatigue limit of a borosilicate glass. J. Eur. Ceram. Soc., 12 (1993) 487-91.
31. Ogasawara, T., Hori, T. & Okada, A., Threshold stress intensity for oxidative crack healing in sintered silicon nitride. J. Mater. Sci. Lett., 13 (1994) 404-6.
32. Wiederhorn, S. M., Fracture surface energy of glass. J. Am. Ceram. Soc., 52 (1969) 99-105.
33. Hahn, G. J. & Shapiro, S. S., Statistical Models in Engineering. John Wiley & Sons, New York, 1967.