Application of a fracture mechanics based life prediction method for contact fatigue

International Journal of Fatigue

Volumn 26, Issue 5, 2004, Pages 511-520

  Conner, B P ^a   Lindley, T C ^b   Nicholas, T ^c   Suresh, S ^a  

^a Massachusetts Institute of Technology Cambridge   (United States)

^b IMPERIAL COLLEGE LONDON   (United Kingdom)

^c UNIVERSITY OF DAYTON RESEARCH INSTITUTE   (United States)

Author keywords

Contact mechanics; Fracture mechanics and crack analogue; Fretting fatigue; Life prediction

Indexed keywords

CONTACT ANGLE; CRACK PROPAGATION; CRACKS; DATA REDUCTION; FATIGUE OF MATERIALS; FRETTING CORROSION; MATHEMATICAL MODELS; NUCLEATION; STRESS ANALYSIS; STRESS INTENSITY FACTORS; THICKNESS MEASUREMENT; YIELD STRESS;

CONTACT MECHANICS; FRETTING FATIGUE; LIFE PREDICTION;

FRACTURE MECHANICS;

EID: 1242276462     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2003.09.003     Document Type: Article

References (28)

1. Hutson A.L., Nicholas T., Olson S.E., Ashbaugh N.E. Effect of sample thickness on local contact behavior in a flat-on-flat fretting fatigue apparatus. International Journal of Fatigue. 23:(S1):2001;445-453.
2. Naboulsi S., Mall S. Fretting fatigue crack initiation behavior using process volume approach and finite element. Tribology International. 36:(2):2003;121-131.
3. Ruiz C., Chen K.C. Life assessment of dovetail joints between blades and discs in aero-engines. Proceedings of the International Conference on Fatigue, Sheffield, UK :1986.
4. Engine Structural Integrity Program (ENSIP), MIL-HDBK-1783B, February 2002.
5. El Haddad M.H., Smith K.N., Topper T.H. Fatigue crack propagation of short cracks. Journal of Engineering Materials and Technology. 101:1979;42-46.
6. Kitagawa H., Takahashi S. Applicability of fracture mechanics to very small cracks or the cracks in the early stage. Proceedings of the Second International Conference on Mechanical Behaviour of Materials, Boston, MA :1976;627-631.
7. Giannakopoulos A.E., Lindley T.C., Suresh S. Aspects of equivalence between contact mechanics and fracture mechanics: theoretical connections and a life-prediction methodology for fretting-fatigue. Acta Materialia. 46:(9):1998;2955-2968.
8. Nadai A.I. Theory of flow and fracture of solids. 1963;McGraw-Hill, New York.
9. Sadowski M. Zweidimensionale probleme der elastizitatstheorie. Z Angew Math Mech. 8:1928;107-121.
10. Williams M.L. On the stress distribution at the base of a stationary crack. Journal of Applied Mechanics. 24:1957;109-114.
11. Giannakopoulos A.E., Venkatesh T.A., Lindley T.C., Suresh S. The role of adhesion in contact fatigue. Acta Materialia. 47:(18):1999;4653-4664.
12. McFarlane J.S., Tabor D. Adhesion of solids and the effect of surface films. Proceedings of the Royal Society, London. A202:1950;224-243.
13. Cotterell B., Rice J.R. Slightly curved or kinked cracks. International Journal of Fracture. 16:1980;155-169.
14. Isida M. Tension of a half plane containing array cracks, branched cracks, and cracks emanating from sharp notches. Transactions of the Japan Society of Mechanical Engineers A. 45:1979;306-319.
15. Paris P.C., Gomez M.P., Anderson W.P. A rational analytic theory of fatigue. Trends in Engineering. 13:1961;9-14.
16. Giannakopoulos A.E., Lindley T.C., Suresh S., Chenut C. Similarities of stress concentrations in contact at round punches and fatigue in notches: implications to fretting fatigue crack initiation. Fatigue and Fracture of Engineering Materials and Structures. 23:2000;562-571.
17. Creager M., Paris P.C. Elastic field equations for blunt cracks with reference to stress corrosion cracking. International Journal of Fracture Mechanics. 3:1967;247-252.
18. Barsom J.M., McNichol R.C. Effect of stress concentration on fatigue crack initiation in HY-130 steel. Fracture Toughness and Slow-Stable Cracking, ASTM STP 559. 1974;183-204 American Society for Testing and Materials.
19. Venkatesh T.A., Conner B.P., Lee C.S., Giannakopoulos A.E., Lindley T.C., Suresh S. An experimental investigation of fretting fatigue in Ti-6Al-4V: the role of contact conditions and microstructure. Metallurgical Transactions. 32A:2001;1131-1146.
20. Conner BP. Mechanical and microstructural effects on fretting fatigue of Ti-6Al-4V. Master's thesis, Massachusetts Institute of Technology, 2000.
21. Conner BP. Contact fatigue: life prediction and palliatives. PhD thesis, Massachusetts Institute of Technology, 2002.
22. Conner BP, Nicholas T. Using a dovetail fixture to study fretting fatigue and fretting palliatives. Journal of Engineering Materials and Technology (in press).
23. Peters J.O., Roder O., Boyce B.L., Thompson A.W., Ritchie R.O. Role of foreign object damage on thresholds for high cycle fatigue in Ti-6Al-4V. Metallurgical and Materials Transactions A. 31A:2000;1571-1583.
24. Campbell J.P., Ritchie R.O. Mixed-mode fatigue-crack growth thresholds in Ti-6Al-4V at high frequency. Scripta Materialia. 41:(10):1999;1067-1071.
25. Campbell J.P., Ritchie R.O. Mixed-mode, high cycle fatigue-crack growth thresholds in Ti-6Al-4V: A comparison of large and short crack behavior. Engineering Fracture Mechanics. 67:2000;209-227.
26. Hutson A.L., Nicholas T. Fretting fatigue behavior of Ti-6Al-4V against Ti-6Al-4V under flat-on-flat contact with blending radii. Hoeppner D.W., Chandrasekaran V., Elliot C.B. Fretting Fatigue: Current Technology and Practices, ASTM STP 1367. 2000;308-321 American Society for Testing and Materials, West Conshohocken, Pennsylvania.
27. Szolwinski M.P., Farris T.N. Observation, analysis and prediction of fretting fatigue in 2024-T351 aluminum alloy. Wear. 221:1998;24-36.
28. Hills D.A., Nowell D. Crack initiation criteria in fretting fatigue. Wear. 136:(1):1989;329-343.