Degradation of Fe-Cr-Al-RE and Ni-Cr-Al-RE foils in air and combustion gas atmospheres

Materials at High Temperatures

Volumn 20, Issue 3, 2003, Pages 439-451

  Simms, N J ^a   Newton, R ^a   Norton, J F ^a   Encinas Oropesa, A ^a   Oakey, J E ^a   Nicholls, J R ^a   Wilber, J ^a  

^a CRANFIELD UNIVERSITY   (United Kingdom)

Author keywords

Fe Cr Al RE; Gas turbines; Ni Cr Al REfoils

Indexed keywords

GAS TURBINES; HONEYCOMB STRUCTURES; NICKEL ALLOYS; NUCLEATION; OXIDATION; OXIDATION RESISTANCE; RATE CONSTANTS; THERMAL CYCLING; THICKNESS MEASUREMENT;

COMBUSTION GAS; FE-CR-AL-RE; NI-CR-AL-RE FOILS; SEALING SYSTEM;

IRON ALLOYS;

EID: 10644268685     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2003.051     Document Type: Article

References (12)

1. Brown, C., Vergheze, E., Sporer, D. and Sallors, R. Paper 98-GT-565. 43rd ASME Gas Turbine and Aeroengine Tech. Congress, Stockholm, Sweden, ASME International (1998)
2. Simms, N.J. Norton, J.F., Encinas-Oropesa, A. Oakey, J.E., Wilshaw, D. and McColvin, G., Degradation of Fe- and Ni-based Cr. Al-containing foils in a Combustion Gas Atmosphere Proc. of John Stringer Symp. High Temperature Corrosion. (ASM. November 2001).
3. Stott, F.H., Wood, G.C. and Stringer, J. The Influence of Alloying Elements on the Development and Maintenance of Protective Scales. Oxidat. Met., 44, 113-145 (1995).
4. Wilber, J.P. Bennett, M.J. and Nicholls, J.R. Life-time extension of alumina forming FeCrAl-RE alloys: influence of alloy thickness. Mater. High Temp., 17, 125-132 (2000).
5. Quadakkers, W.J , Clemens, D. and Bennett, M.J. Measures to Improve the Oxidation Limited Service Life of Fe-based ODS Alloys. In: Microscopy of Oxidation 3, pp. 195-206 Newcomb, S. and Little, J. A. (eds), The Institute of Metals, London (1997).
6. Newton, R , Bennett, M.J., Wilber, J.P., Nicholls, J.R., Naumenko, D., Quadakkers, W.J., Al-Badairy, H , Tatlock, G , Strehl, G., Borchardt, G , Kolb-Telieps, A. Jonsson, B., Westerlund, A., Guttmann, V., Maier, M. and Beaven, P. The Oxidation Lifetime of Commercial FeCrAl(RE) Alloys. In: Lifetime Modelling of High Temperature Corrosion Processes, pp. 15-36, Schütze, M. et al. (eds), European Federation of Corrosion Publication No. 34. Maney Publishing, London (2001).
7. Kolb-Telieps, A., Miller, U., Al-Badairy, H , Tatlock, G., Naumenko, D., Quadakkers, W.J , Strehl, G., Borchardt, G., Newton, R., Nicholls, J R., Maier, M. and Baxter, D , The Role of Bioxidant Corrodents on the Lifetime Behaviour of FeCrAl(RE) Alloys. In: Lifetime Modelling of High Temperature Corroston Processes, pp. 123-134, Schütze, M. et al, (eds) European Federation of Corrosion Publication No. 34, Maney Publishing, London (2001).
8. Nicholls, J.R., Newton, R., Bennett, M.J., Evans, H.E., Al-Badairy, H., Tatloek, G.J. Naumenko, D. Quadakkers, W.J , Strehl, G. and Borchardt, G., Development of a Life Prediction Model for the Chemical Failure of FeCrAl(RE) Alloys in Oxidising Environments. In: Lifetime Modelling of High Temperature Corrosion Processes, pp. 83-106, Schütze, M. et al. (eds). European Federation of Corrosion Publication No. 34, Maney Publishing, London (2001).
9. Simms, N.J., Oakey, J.E., Nicholls, J R., Newton, R., Wilber, J., Encinas-Oropesa, A. and Norton, J.F , Degradation of Fe-Cr-Al-RE foils in combustion gas and air atmospheres. Proc. TMS meeting on Effects of Water Vapour on High Temperature Oxidation. TMS. February (2002)
10. Nicholls, J.R., Simms, N.J., Newton, R. and Norton, J.F., Oxidation of ODS Alloys in Mixed Gaseous Atmospheres Proc. 3rd Int. Workshop On Life Cycle Issues in Advanced Energy Systems. Woburn, UK, June 2002. (Mater. High Temp.) 20 (in press).
11. Draft Code of Practice for 'Discontinuous Corrosion Testing in High Temperature Gaseous Atmospheres', EC Project SMT4-CT95-2001. ERA Technology, UK (2000).
12. Whittle, D.P. Oxidation mechanisms for allovs in single oxidant gases In High Temperature Corrosion, pp. 171-183, Rapp, R A (ed.) (NACE, 1983).