Overload effects on corrosion fatigue crack initiation life and life prediction of aluminum notched elements under variable amplitude loading

Engineering Fracture Mechanics

Volumn 63, Issue 5, 1999, Pages 557-572

  Zheng, Xiulin ^a   Wang, Rong ^a  

^a NORTHWESTERN POLYTECHNICAL UNIVERSITY   (China)

Author keywords

Aluminum alloy; Continuous strain hardening; Corrosion fatigue crack initiation; Cumulative fatigue damage rule; Life prediction; Overload effect; Variable amplitude loading

Indexed keywords

ALUMINUM ALLOYS; CORROSION FATIGUE; CRACK INITIATION; LOADS (FORCES); MATHEMATICAL MODELS; SODIUM CHLORIDE; SPECTRUM ANALYSIS; STRAIN HARDENING;

CORROSION FATIGUE CRACK INITIATION; EQUIVALENT STRESS AMPLITUDE; LIFE PREDICTION; LOAD SPECTRA; NOTCHED ELEMENTS; OVERLOAD EFFECTS; VARIABLE AMPLITUDE LOADING;

SHEET METAL;

ALUMINUM ALLOY; CORROSION; CRACK INITIATION; FATIGUE CRACK; FATIGUE LIFE ANALYSIS;

EID: 0345062336     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(99)00038-7     Document Type: Article

References (29)

1. Kim YH, Speaker SM, Gordon DE, Manning SD, Wei RP. Development of fatigue and crack propagation design and analysis methodology in a corrosive environment for typical mechanically-fastened joints. Report No. NADC-83126-60, vol. 1 (AD-A136414), December 1983.
2. Kim YH, Speaker SM, Gordon DE, Manning SD, Wei RP. Development of fatigue and crack propagation design and analysis methodology in a corrosive environment for typical mechanically-fastened joints (state of the art assessment). Report No. NADC 83126-60, vol. 2 (AD-A136415), December 1983.
3. Wanhill RJH, De Luccia JJ, Russo MT. The fatigue in aircraft corrosion testing (FACT) programme. AGARD Report No. 713 (AD-A208-359), 1989.
4. Jiang Zugou. Corrosion fatigue of aircraft structures. 1992;Press of Aviation Industry, Beijing. (in Chinese).
5. Lee E.U. Corrosion fatigue and stress corrosion cracking of 7475-T7351 aluminum alloy. Goel V.S. Corrosion Cracking, Conf. Proc. ASM, Salt Lake City. December 1985;123-128.
6. Gordon D.E., Manning S.D., Wei R.P. Effects of salt water environment and loading frequency on crack initiation in 7075-T7651 aluminum alloy and Ti-6Al-4V. Goel V.S. Conf. Proc. ASM, Salt Lake City. December 1985;157-168.
7. Dequette DJ. Environment effects (1), General fatigue resistance and crack nucleation in metals and alloys. Fatigue and Microstructure ASM 1978;335-363.
8. Marcus HL. Environment effects (2), Fatigue crack growth in metals and alloys. Fatigue and Microstructure ASM 1978;365-383.
9. Buch A. Int. J. Fatigue. 11:1989;97-106.
10. Xu Hao. Fatigue strength. 1988;Press of High Education, Beijing. (in Chinese).
11. Zhao Mingpan. Handbook of strain fatigue analysis. 1988;Publishing House of Science, Beijing. (in Chinese).
12. Khan Z., Younas M. Corrosion-fatigue life prediction for notched components based on the local strain and linear elastic fracture mechanics concepts. Int. J. Fatigue. 18:(7):1996;491-496.
13. ECCS recommendations for the fatigue design of steel structures, 1st ed. 1985.
14. van Dijk GM, de Jonge JB. Introduction to a fighter aircraft loading standard for fatigue evaluation. FALSTAFF, NLR MP 75017U, The Netherlands, 1975.
15. Xue Y.L., Xu J.L., Li Y.P., Li H. On the corrosion fatigue of welded joints under variable amplitude loading in sea water. Proc. 5th Natl. Conf. Fatigue, Weihai. September 1991;426-429. (in Chinese).
16. Zheng X.L. Modeling fatigue crack initiation life. Int. J. Fatigue. 15:1993;461-466.
17. Zheng X.L. Overload effects on fatigue behavior and life prediction of low-carbon steels. Int. J. Fatigue. 17:1995;331-337.
18. Ling Chao, Zheng Xiulin. Fatigue crack initiation life of LC4CS aluminum alloy sheets and its overloading effect: a general formula for FCIL of aluminum alloys. J. Northwestern Polytechnical University (NPU) (in Chinese). 9:(1):1991;30-35.
19. Wang R. Quantitative investigation of the corrosion fatigue of aluminum alloys. Doctorate thesis, Northwestern Polytechnical University, June 1994 (in Chinese).
20. Lu Baotong, Zheng Xiulin. Predicting fatigue crack initiation life of an aluminum alloy below room temperature. Fatigue Fract. Eng. Mater. Struct. 15:(12):1992;1213-1221.
21. Clark W.G. Jr. ASTM STP. 559:1973;205-224.
22. Dowling N.E. ASTM STP. 677:1979;247-273.
23. Lu Minxu, Zheng Xiulin. A new microcomputer-aided system for measuring fatigue crack propagation threshold and selecting testing parameters. Eng. Fract. Mech. 45:(6):1993;889-896.
24. Zheng Xiulin, Wang Rong. On the corrosion fatigue crack initiation model and expression of metallic notched elements. Eng. Fract. Mech. 57:(6):1997;617-624.
25. Zheng X.L., Ling C., Zheng S.T. An approximate formula for calculating local strain range. Advanced Computational Methods, Proc. 1st Int. Conf. Localized Damage Computer Aided Assessment and Control, Portsmouth. June 1990;253-261 Computational Mechanics Publications, Southampton, UK.
26. Ohta A., Maeda Y., Suzuki N. Fatigue strength of butt-welded joints under constant maximum stress and random minimum stress conditions. Fatigue Fract. Engng. Mater. Struct. 9:(2/3):1996;265-275.
27. Raithby KR, Longson J. Some fatigue characteristics of a two-spar light alloy structure. H.M.O.S., Aero. Res. Council, Current Paper 258, 1956.
28. Schijve J. Endurance under program-fatigue testing. Plantema F.J., Schijve J. Full-scale fatigue testing of aircraft structures. 1961;41-59 Pergamon Press, London.
29. Zheng Xiulin. Further study for fatigue crack initiation life(II): Prediction of fatigue crack initiation life. Goel V.S. Fatigue Life, Conf. Proc. ASM, Salt Lake City, USA. December 1985;1-4.