On the corrosion fatigue crack initiation model and expression of metallic notched elements

Engineering Fracture Mechanics

Volumn 57, Issue 6, 1997, Pages 617-624

  Xiulin, Zheng ^a   Rong, Wang ^a  

^a NORTHWESTERN POLYTECHNICAL UNIVERSITY   (China)

Author keywords

Aluminum alloy; Corrosion; Fatigue crack initiation; Fatigue life; Fatigue threshold; Notched element; Titanium alloy

Indexed keywords

ALUMINUM ALLOYS; CORROSION FATIGUE; CORROSION RESISTANCE; CRACK INITIATION; MATHEMATICAL MODELS; STRESS CORROSION CRACKING; TENSILE STRENGTH; TITANIUM ALLOYS;

METALLIC NOTCHED ELEMENTS;

STRUCTURAL METALS;

ALUMINUM ALLOY; CORROSION; FATIGUE CRACK; MODEL;

EID: 0043044852     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/s0013-7944(97)00062-3     Document Type: Article

References (26)

1. Kim, Y. H., Speaker, S. M., Gordon, D. E., Manning, S. D. and Wei, R. P., Development of fatigue and crack propagation design and analysis methodology in a corrosive environment for typical mechanically-fastened joints. Report No. NADC-83126-60, Vol. 1 (AD-A136414), December 1983.
2. Kim, Y. H., Speaker, S. M., Gordon, D. E., Manning, S. D. and Wei, R. P., Development of fatigue and crack propagation design and analysis methodology in a corrosive environment for typical mechanically-fastened joints (state of the art assessment). Report No. NADC-83126-60, Vol. 2 (AD-A136415), December 1983.
3. Wanhill, R. J. H., De Luccia, J. J. and Russo, M. T., The fatigue in Aircraft Corrosion Testing (FACT) Programme, AGARD Report No. 713 (AD-A208-359), 1989.
4. Zuguo Jiang (ed.), Corrosion Fatigue of Aircraft Structures. Press of Aeronautical Industry, Beijing, 1992 (in Chinese).
5. Dequette, D. J., Environmental effects (1): general fatigue resistance and crack nucleation in metals and alloys. In Fatigue and Microstructure, ASM, 1978, pp. 335-363.
6. Pelloux, R. M., Fatigue-corrosion. In La Fatigue des Materiaux et des Structures. Les Presses Del'Universite De Montreal, 1981, pp. 271-289.
7. Fougue, J. D., Effect d'environment. In La Fatigue des Materiaux et des Structures, 1981, pp. 290-311.
8. Minpan Zhao (ed.), Handbook of strain Fatigue Analysis. Publishing House of Science, Beijing, 1991.
9. Coffin, L. F., Jr, Fatigue in machines and structures. In Fatigue and Microstructures, ASM, 1978, pp. 4-7.
10. Buch, A., Fatigue Strength Calculations. Trans. Tech. Publications, Switzerland, 1988.
11. Zheng, X., Int. J. Fatigue, 1986, 8(1), 17-21.
12. Xiulin Zheng, Further study on fatigue crack initiation life (II) - Prediction of fatigue crack initiation life. In Fatigue Life Conf. Proc. ASM (ed. V. S. Goal), Salt Lake City, December 1985, pp. 1-4.
13. Zheng, X. and Chao, L.. Engineering Fracture Mechanics, 1988, 31(6), 959-966.
14. Lu, B., Zheng, X. L. and Lu, X., Metall. Trans., 1989, 20A(2), 413-419.
15. Lu, B. and Lu, X., Fatigue Fracture Engineering Mater. Struct., 1992, 15(21), 1213-1221.
16. Tay, C. J., Tay, T. E., Shang, H. M. and Yap, C. M.. Int. J. Fatigue, 1994, 16, 423.
17. Lu, B. and Zheng, X., Weld. J., 1993, 72(2), 793-805.
18. Zheng, X., Lu, B., Cui, T., Lu, X. and Ling, C., Int. J. Fracture, 1994, 68, 275.
19. Zheng, X., Int. J. Fatigue, 1993, 15(6), 461-466.
20. Zheng, X., Int. J. Fatigue, 1995, 17(5), 331-337.
21. Zheng, X., Li, Z. and Lu, B., Int. J. Fatigue, 1995, 18(2), 81-86.
22. Xiulin Zheng, Local strain range and fatigue crack initiation life. In Fatigue of Steel and Concrete Structures, IABSE Proc. Fatigue Colloquium, Lausanne, 1982, pp. 169-178.
23. Xiulin Zheng and Boatong Lu, Fatigue formula under cyclic strain. In Fatigue and Fracture Mechanics, Proc. 1st Int. Conf. Localized Damage Computer Aided Assessment and Control of Localized Damage, ed. M. H. Aliabadi et al., Portsmouth, June 1990, pp. 175-184.
24. Frost, N. E., Marsh, K. J. and Pook, L. P., Metal Fatigue. Clarendon Press, Oxford, 1974.
25. Rong Wang, Quantitative investigation of the corrosion fatigue of aluminum alloy. Doctoral Thesis, Northwestern Polytechnical University, June 1994.
26. Gordon, D. E., Manning, S. D. and Wei, R. P., Effects of salt water environment and loading frequency on crack initiation in 7075-T7651 aluminum alloy and Ti-6A1-4V. In Corrosion Cracking, Conf. Proc. ASM, ed. V. S. Goal, Salt Lake City, December 1985, pp. 157-166.