Circumferential crack problem for an fgm cylinder under thermal stresses

Journal of Thermal Stresses

Volumn 22, Issue 7, 1999, Pages 659-687

  Dağ, Serkan ^a   Kadioğlu, Suat ^a   Yahşi, O Selçuk ^a  

^a MIDDLE EAST TECHNICAL UNIVERSITY   (Turkey)

Author keywords

Crack Problem; Elastic Foundation; Functionally Graded Material; Stress Intensity Factor; Thermal Stress; Thin walled Cylinder

Indexed keywords

COMPOSITE MATERIALS; CRACK INITIATION; CYLINDERS (CONTAINERS); ELASTICITY; MATHEMATICAL MODELS; MECHANICAL PROPERTIES; PERTURBATION TECHNIQUES; STRESS CONCENTRATION; STRESS INTENSITY FACTORS; THERMAL LOAD; THERMODYNAMIC PROPERTIES;

CIRCUMFERENTIAL CRACK PROBLEM; CRACK GEOMETRY; ELASTIC FOUNDATION; FUNCTIONALLY GRADED MATERIAL; THIN WALLED CYLINDER;

THERMAL STRESS;

EID: 0343825906     PISSN: 01495739     EISSN: 1521074X     Source Type: Journal    
DOI: 10.1080/014957399280698     Document Type: Article

References (16)

1. F. Erdogan, Fracture Mechanics of Functionally Graded Materials, Comp. Engrg., vol. 5, pp. 753-770, 1995.
2. F. Delale and F. Erdogan, The Crack Problem for a Nonhomogeneous Plane, J. Appl. Mech., vol. 50, pp. 609-614, 1983.
3. F. Erdogan, The Crack Problem for Bonded Nonhomogene ous Materials under Antiplane Shear Loading, J. Appl. Mech., vol. 52, pp. 823-828, 1985.
4. N. Konda and F. Erdogan, The Mixed Mode Crack Problem in a Nonhomogeneous Elastic Medium, Engrg. Fracture Mech., vol. 47, pp. 533-545, 1994.
5. Y. F. Chen and F. Erdogan, The Interface Crack Problem in Nonhomogeneous Bonded Materials of Finite Thickness, ONR contract no. N00014-89-318 8 Final Project Report, Lehigh University, 1992.
6. M. Ozturk and F. Erdogan, The Axisymmetric Crack Problem in a Nonhomogeneous Medium, J. Appl. Mech., vol. 60, pp. 406-413, 1993.
7. H. Fildis, The Axisymmetric Crack Problem in a Nonhomogeneous Interfacial Region Between Homogeneous Half Spaces, Ph.D. Thesis, Middle East Technical University, Ankara, 1995.
8. T. Ishiguro, A. Makino, and N. Araki, Transient Temperature Response in Functionally Gradient Materials, Int. J. Thermophysics, vol. 14, pp. 101-121, 1993.
9. Z. H. Jin and R. C. Batra, Stress Intensity Relaxation at the Tip of an Edge Crack in a Functionally Graded Material Subjected to a Thermal Shock, J. Thermal Stresses, vol. 19, pp. 317-339, 1996.
10. B. H. Wu and F. Erdogan, Crack Problems in FGM Layers under Thermal Stresses, J. Thermal Stresses, vol. 19, pp. 237-265, 1996.
11. N. Noda and Z. H. Jin, A Crack in Functionally Gradient Materials under Thermal Shock, Arch. Appl. Mech., vol. 64, pp. 99-110, 1994.
12. Z. H. Jin and N. Noda, An Internal Crack Parallel to the Boundary of a Nonhomogeneous Half Plane under Thermal Loading, Int. J. Engrg. Sci, vol. 31, pp. 793-806, 1993.
13. N. Noda and Z. H. Jin, Thermal Stress Intensity Factors for a Crack in a Strip of a Functionally Gradient Material, Int. J. Solids and Structures, vol. 30, pp. 1039-1056, 1993.
14. Y. D. Lee and F. Erdogan, Residual /Thermal Stresses in FGM and Laminated Thermal Barrier Coatings, Int. J. Fracture, vol. 69, pp. 145-165, 1994.
15. F. Erdogan and A. A. Rizk, Fracture of Coated Plates and Shells under Thermal Shock, Int. J. Fracture, vol. 53, pp. 169-185, 1992.
16. S. Dag, Crack Problems in a Functionally Graded Layer under Thermal Stresses, M.S. Thesis, Middle East Technical University, Ankara, 1997.