Interface fatigue crack propagation in ceramic thermal barrier coatings

JSME International Journal, Series A: Solid Mechanics and Material Engineering

Volumn 46, Issue 3, 2003, Pages 403-408

  Mutoh, Yoshiharu ^a   Xu, Jin Quan ^a   Miyashita, Yukio ^a   Bernardo, Gomez G ^a   Takahashi, Masashi ^b  

^a NAGAOKA UNIVERSITY OF TECHNOLOGY   (Japan)

^b TOSHIBA CORPORATION   (Japan)

Author keywords

Ceramic coating; Crack propagation; Fatigue; Interface crack; Stress intensity factor

Indexed keywords

CERAMIC COATINGS; CERAMIC MATERIALS; CRACK PROPAGATION; FATIGUE OF MATERIALS; INTERFACES (MATERIALS); POROSITY;

INTERFACE CRACKS;

THERMAL BARRIER COATINGS;

CERAMICS;

EID: 0141572200     PISSN: 13447912     EISSN: None     Source Type: Journal    
DOI: 10.1299/jsmea.46.403     Document Type: Article

References (18)

1. Sheffler, K.D. and Gupta, D.K., Current Status and Future Trends in Turbine Application of Thermal Barrier Coating, J. Eng. Gas Turbines and Power, Trans. of ASME, Vol. 110 (1988), p. 605.
2. Nissley, D.M., Thermal Barrier Coating Life Modeling in Aircraft Gas Turbine Engines, J. Thermal Spray Tech., Vol. 6, No. 1 (1997), p. 91.
3. Janos, B.Z., Lugscheider, E. and Remer, P., Effect of Thermal Aging on the Erosion Resistance of Air Plasma Sprayed Zirconia Thermal Barrier Coating, Surface and Coating Tech., Vol. 113 (1999), p. 278.
4. Bartlett, A.H. and Maschio, R.D., Failure Mechanism of a Zirconia-8 wt% Yittoria Thermal Barrier Coating, J. Amer. Ceramic Soc., Vol. 78, No. 4 (1995), p. 1018.
5. Takeuchi, Y.R. and Kokini, K., Thermal Fracture of Multilayer Ceramic Thermal Barrier Coatings, J. Eng. Gas Turbines and Power, Vol. 116 (1994), p. 266.
6. Nusier, S.Q. and Newaz, G.M., Growth of Interfacial Cracks in a TBC/Superalloy System due to Oxide Volume Induced Internal Pressure and Thermal Loading, Int. J. Solids and Struct., Vol. 37 (2000), p. 2151.
7. Zhang, D.K., Kato, M. and Nakasa, K., Fracture Mechanics Analysis of Edge-indentation Method for Evaluation of Delamination Strength of Coating, J. Soc. Mat. Sci. Japan, Vol. 49, No. 5 (2000), p. 572.
8. Mutoh, Y., Xu, J.Q., Miyashita, Y., Kuroishi, T. and Sasaki, Y., On Evaluation of Adhesive Strength in a Scratch Test of Coating Materials, Trans. Jpn. Soc. Mech. Eng., (in Japanese), Vol. 68, No. 670 (2002), p. 909.
9. Zhu, D.M. and Miller, R. A., Investigation of Thermal Fatigue Behavior of Thermal Barrier Coating System, Surface and Coating Tech., Vol. 94 (1977), p. 94.
10. Wesling, K.F. and Socie, D.F., Fatigue of Thermal Barrier Coatings, J. American Ceramic Soc., Vol. 77 (1994), p. 1863.
11. Yuuki, R., Mechanics of Interface, (1992), Baifukan.
12. Yuuki, R. and Xu, J.Q., Development of the Boundary Element Method Program BEM2D and Analysis of Dissimilar Materials and Interface Cracks, SEISANKENKYU, Vol. 43, No. 7 (1991), p. 306.
13. Yuuki, R., Liu, J.Q., Xu, J.Q., Ohira, T. and Ono, T., Mixed Mode Fracture Criteria for an Interface Crack, Eng. Fract. Mech., Vol. 47, No. 3 (1994), p. 367.
14. Rice, J.R. and Sih, G.C., Plane Problems of Cracks in Dissimilar Media, J. Appl. Mech., Vol. 32 (1965), p. 418.
15. Rice, J.R., Elastic Fracture Mechanics Concepts for Interfacial Cracks, J. Appl. Mech., Vol. 55 (1988), p. 98.
16. Yuuki, R. and Xu, J.Q., Stress Based Criterion for an Interface Crack Kinking Out of the Interface in Dissimilar Materials, Eng. Fract. Mech., Vol. 41, No. 5 (1992), p. 635.
17. Sun, C.T. an Jih, C.J., On Strain Energy Release Rate for Interfacial Cracks in Bimaterial Media, Eng. Fract. Mech., Vol. 38, No. 7 (1987), p. 1279.
18. Erdogan, F. and Sih, G.C., On the Crack Extension in Plates under Plane Loading and Transverse Shear, Journal of Basic Engineering, Vol, 85 (1963), p. 519.