Growth of interfacial cracks in a TBC/superalloy system due to oxide volume induced internal pressure and thermal loading

International Journal of Solids and Structures

Volumn 37, Issue 15, 2000, Pages 2151-2166

  Nusier, S Q ^a   Newaz, G M ^a  

^a Wayne State University   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COATING; INTERFACE; OXIDATION; THERMAL CRACKING;

COATINGS; CRACK PROPAGATION; FINITE ELEMENT METHOD; INTERFACES (MATERIALS); MATHEMATICAL MODELS; OXIDATION; PRESSURE EFFECTS; RESIDUAL STRESSES; SUPERALLOYS; THERMAL INSULATING MATERIALS; THERMAL STRESS;

THERMAL BARRIER COATINGS (TBC); THERMAL EXPANSION MISMATCH;

FRACTURE MECHANICS;

EID: 0034681087     PISSN: 00207683     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0020-7683(98)00321-7     Document Type: Article

References (26)

1. ABAQUS, 1995. Hibbitt, Karlsson and Sorensen, Inc.
2. Aravas N., Sharma S.M. An elastoplastic analysis of the interface crack with contact zones. J. Mech. Phys. Solids. 39:(3):1991;311-344.
3. Blanchard J.P., Ghoniem N.M. Relaxation of thermal stress singularities in bonded viscoelastic quarter planes. Transactions of the ASME. 56:1989;756-762.
4. Bottega W.J., Maewal A. Delamination buckling and growth in laminates. Transactions of the ASME. 50:1983;184-189.
5. Bottega W.J., Maewal A. Dynamics of delamination buckling. International Journal of Non-Linear Mechanics. 18:(6):1983;449-463.
6. Chai H. Three-dimensional fracture analysis of thin-film debonding. Int. J. Fracture. 46:1990;237-256.
7. Chang G.C., Phucharoen W., Miller R.A. Finite element thermal stress solutions for thermal barrier coatings. Surface and Coatings Technology. 32:1987;307-325.
8. Dattaguru B., Venkatesha K.S., Ramamurthy T.S., Buchholz F.G. Finite element estimates of strain energy release rate components at the tip of an interface crack under mode I loading. Engineering Fracture Mechanics. 49:(3):1994;451-463.
9. Eshelby J.D. The continuum theory of lattice defects. Solid State Physics. 3:1956;79-141.
10. Evans A.G., Hutchinson J.W. On the mechanics of delamination and spalling in compressed films. Int. J. Solids Struct. 20:(5):1984;455-466.
11. Hellen T.K. On the method of virtual crack extensions. Int. J. Num. Meth. 9:1975;187-207.
12. Holmes J.W., McClintock F.A., O'Hara K.S., Conners M.E. Thermal fatigue testing of coated monocrystalline superalloys. Low Cycle Fatigue ASTM STP. 942:1988;672-691.
13. Jin Z., Noda N. Crack-tip singular fields in nonhomogeneous materials. Transactions of the ASME. 61:1994;738-740.
14. Kokini K., Hornack T.R. Transient thermal load effects on coatings bonded to cylindrical substrates and containing circumferential cracks. Journal of Engineering Materials and Technology. 110:1988;35-40.
15. Nahta R., Moran B. Domain integrals for axisymmetric interface crack problems. Int. J. Solids Struct. 30:(15):1993;2027-2040.
16. Newaz G.M., Nusier S.Q., Chaudhury Z.A. Damage accumulation mechanisms in thermal barrier coatings. ASME, Journal of Engineering Materials and Technology. 120:(2):1998;149-153.
17. Nusier S.Q., Newaz G.M. Analysis of interfacial cracks in a TBC/superalloy system under thermal loading. Journal of Engineering Fracture Mechanics. 60:(5-6):1998;577-581.
18. Oneil D.A., Wayne S.F. Numerical simulation of fracture in coated brittle materials subjected to tribo-contact. Journal of Engineering Materials and Technology. 116:1994;471-478.
19. Rice J.R. Mathematical analysis in the mechanics of fracture. Leibowitz H. Fracture, An Advanced Treatise Vol. 2. 1968;191-311 Academic Press, New York.
20. Ryan R.L., McCafferty E. Rupture of an oxide blister. J. Electrochem. Soc. 142:(8):1995;2594-2597.
21. Suo Z. Wrinkles of the oxide scale on an aluminum-containing alloy at high temperature. Journal of Mechanics and Physics of Solids. 43:(6):1995;829-846.
22. Takeuchi Y.R., Kokini K. Thermal fracture of multilayer ceramic thermal barrier coatings. Journal of Engineering for Gas Turbines and Power. Trans. ASME. 116:1994;266-271.
23. Van der Zande H.D., Grootenboer H.J. A finite element approach to interface cracks. Journal of Applied Mechanics. 53:1986;573-578.
24. Wan K., Mai Y. Fracture mechanics of a shaft-loaded blister of thin flexible membrane on rigid substrate. Int. J. Fract. 74:1995;181-197.
25. Williamson R.L., Rabin B.H., Drake J.T. Finite element analysis of thermal residual stresses at graded ceramic-metal interfaces: part I - Model description and geometrical effects. J. Appl. Phys. 74:1993;1310-1320.
26. Yin W. Axisymmetric buckling and growth of a circular delamination in a compresses laminate. Int. J. Solids and Struct. 21:(5):1985;503-514.