Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures

Dental Materials

Volumn 19, Issue 7, 2003, Pages 662-669

  Bona, Alvaro Della ^a   Anusavice, Kenneth J ^b   DeHoff, Paul H ^c  

^a UNIVERSITY OF PASSO FUNDO   (Brazil)

^b UNIVERSITY OF FLORIDA   (United States)

^c University of North Carolina at Charlotte   (United States)

Author keywords

Empress ceramic; Fractography; Fracture surface; Leucite based ceramic; Lithia disilicate based ceramic; Monolithic and multilayer structures; Structural reliability

Indexed keywords

BENDING STRENGTH; HOT PRESSING; MULTILAYERS; STATISTICAL METHODS; VENEERS; WEIBULL DISTRIBUTION;

CERAMIC STRUCTURES;

CERAMIC PRODUCTS;

EID: 0042128629     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0109-5641(03)00010-1     Document Type: Article

References (29)

1. Kelly J.R. Perspectives on strength. Dent Mater. 11:1995;103-110.
2. Ritter J.E. Critique of test methods for lifetime predictions. Dent Mater. 11:1995;147-151.
3. Ban S., Anusavice K.J. Influence of test method on failure stress of brittle dental materials. J Dent Res. 69:1990;1791-1799.
4. Giordano R.A., Pelleiter L., Campbell S., Pober R. Flexural strength of an infused ceramic, glass ceramic, and feldspathic porcelain. J Prosthet Dent. 73:1995;411-418.
5. Thompson G.A. Influence of relative layer height and testing method on the failure mode and origin in a bilayered dental ceramic composite. Dent Mater. 16:2000;235-243.
6. DeHoff P.H., Anusavice K.J., Hathcock P.W. An evaluation of the four-point flexural test for metal-ceramic bond strength. J Dent Res. 61:1982;1066-1069.
7. Coffey J.P., Anusavice K.J., DeHoff P.H., Lee R.B., Hojjatie B. Influence of contraction mismatch and cooling rate on flexural failure of PFM systems. J Dent Res. 67:1988;61-65.
8. Tinschert J., Zwez D., Marx R., Anusavice K.J. Structural reliability of alumina-, feldspar-, leucite-, mica- and zirconia-based ceramics. J Dent. 28:2000;529-535.
9. Johnson C.A. Fracture statics of multiple flaw distribution. Bradt R.C., Evans A.G., Hasselman D.P.H., Lange F.F. Fracture mechanics of ceramics: surface flaws, statics, and microcracking. vol. 5:1983;365-386 Plenum Press, New York.
10. McCabe J.F., Carrick T.E. A statistical approach to the mechanical testing of dental materials. Dent Mater. 2:1986;139-142.
11. International Organization for Standardization. Dental Ceramics. 2nd ed:1995;ISO. ISO 6872.
12. Krautkramer J., Krautkramer H. Ultrasonic testing of materials. 3rd ed:1983;Springer, Berlin. p. 580.
13. Mecholsky J.J. Jr. Fractography: determining the sites of fracture initiation. Dent Mater. 11:1995;113-116.
14. Mecholsky J.J. Jr. Fracture mechanics principles. Dent Mater. 11:1995;111-112.
15. Ritter J.E. Predicting lifetimes of materials and material structures. Dent Mater. 11:1995;142-146.
16. Kelly J.R., Campbell S.D., Bowen H.K. Fracture-surface analysis of dental ceramics. J Prosthet Dent. 62:1989;536-541.
17. Kelly J.R., Giordano R., Pober R., Cima M.J. Fracture surface analysis of dental ceramics: clinically failed restorations. Int J Prosthodont. 3:1990;430-440.
18. Thompson J.Y., Anusavice K.J., Naman A., Morris H.F. Fracture surface characterization of clinically failed all-ceramic crowns. J Dent Res. 73:1994;1824-1832.
19. Jung Y.-G., Wuttiphan S., Peterson I.M., Lawn B.R. Damage modes in dental layer structures. J Dent Res. 78:1999;887-897.
20. Wuttiphan S., Lawn B.R., Padture N.P. Crack suppression in strongly bonded homogeneous/heterogeneous laminates: a study on glass/glass ceramic bilayers. J Am Cer Soc. 79:1996;634-640.
21. Wakabayashi N., Anusavice K.J. Crack initiation modes in bilayered alumina/porcelain disks as a function of core/veneer thickness ratio and supporting substrate stiffness. J Dent Res. 79:2000;1398-1404.
22. Anusavice K.J., Tsai Y.L. Stress distribution in ceramic crown forms as a function of thickness, elastic modulus, and supporting substrate. Bumgardner J.D., Puckett A.D. Proceedings of the Sixteenth Southern Biomedical Engineering Conference. 1997:1997;264-267 IEEE, Biloxi, MS.
23. Lüthy H., Dong J.K., Wohlwend A., Schārer P. Effects of veneering and glazing on the strength of heat-pressed ceramics. Schweiz Monatsschr Zahnmed. 103:1993;1257-1260.
24. Fairhurst C.W., Lockwood P.E., Ringle R.D., Thompson W.O. The effect of glaze on porcelain strength. Dent Mater. 8:1992;203-207.
25. Höland W., Schweiger M., Frank M., Rheinberger V. A comparison of the microstructure and properties of the IPS Empress 2 and the IPS Empress glass-ceramics. J Biomed Mater Res. 53:2000;297-303.
26. Mecholsky J.J. Jr. Quantitative fracture surface analysis of glass materials. Simmons C.J., El-Bayoumi O. Experimental techniques of glass science. 1993;483-520 American Ceramic Society, Westerville.
27. Mandelbrot B.B., Passoja D.E., Paulley A.J. Fractal character of metals. Nature. 308:1984;721-722.
28. Mecholsky J.J. Jr. Fractography, fracture mechanics, and fractal geometry: an integration. Varner J.R., Frechette V.D., Quinn G.D. Fractofraphy of glasses and ceramics III. Ceramic Transactions 64. 1996;385-393.
29. Mecholsky J.J. Jr, Freiman S.W. Relationship between fractal geometry and fractography. J Am Ceram Soc. 74:1991;3136-3138.