Water chemistry in a crack tip under irradiation, (II)

Journal of Nuclear Science and Technology

Volumn 40, Issue 5, 2003, Pages 334-342

  Satoh, Tomonori ^a   Satoh, Yoshiyuki ^a   Uchida, Shunsuke ^a  

^a TOHOKU UNIVERSITY   (Japan)

Author keywords

BWR type reactors; Crack tip; Hydrogen peroxide; Irradiation assisted stress corrosion cracking; Water radiolysis

Indexed keywords

BOILING WATER REACTORS; CRACK PROPAGATION; DIFFUSION; GAMMA RAYS; NEUTRONS; RADIOLYSIS; STRESS CORROSION CRACKING;

CRACK TIPS;

IRRADIATION;

EID: 0038457435     PISSN: 00223131     EISSN: None     Source Type: Journal    
DOI: 10.1080/18811248.2003.9715363     Document Type: Article

References (14)

1. S. Uchida, H. Fujimoto, E. Ibe, etal., “A procedure for evaluating residual life of major components in light water reactors,” Proc. 7th Int. Symp. Environmental Degradation ofMaterials in Nuclear Power Systems-Water Reactors, Breckenridge, Colorado, Aug. 7-10, 1995, p. 959 (1995).
2. P. L. Andresen, “Perspective and direction of stress corrosion cracking in hot water,” Proc. 10th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems-Water Radiolysis, Lake Tahoe, Nevada, Aug. 5-9, 2001, (2001).
3. S. Uchida, E. Ibe, K. Nakata, et al., Nucl. Technol., 110, 250 (1995).
4. S. Uchida, N. Shigenaka, M. Tachibana, et al., J. Nucl. Sci. Technol., 35[4],301 (1998).
5. T. Satoh, S. Uchida, K. Furukawa, et al., J. Nucl. Sci. Technol., 38[9], 773 (2001).
6. S. Uchida, T. Satoh, K. Furukawa, et al., “Crevice chemistry under gamma ray irradiation,” Proc. 10th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems- Water Radiolysis, Lake Tahoe, Nevada, Aug. 5-9, 2001, (2001).
7. J. Elliot, D. R. McCracken, G. V. Buxton, et al., “Estimation of rate constants for near-diffusion-controlled reactions in water at high temperatures,” J. Chem. Soc. Faraday Trans., 86[9], 1539(1990).
8. S. Uchida, M. Tachibana, A. Watanabe, etal., J.Nucl. Sci. Technol., 37[3], 257 (2000).
9. Y. Wada, A. Watanabe, M. Tachibana, et al., J. Nucl. Sci. Technol., 37[10], 901 (2000).
10. Y. Wada, A. Watanabe, M. Tachibana, et al., J. Nucl. Sci. Technol., 38[3], 183 (2001).
11. Y. Murayama, T. Satoh, S. Uchida, et al., J. Nucl. Sci. Technol., 39[11], 1199 (2002).
12. C. W. Gear, Numerical Initial Value Problems in Ordinary Differential Equations, Prentice-Hall, Englewood Cliffs, New Jersey, (1971).
13. D. R. Lide, Handbook of Chemistry and Physics, CRC Press, (1994).
14. P. L. Andresen, “Effects of nitrate on the stress corrosion cracking of sensitizing stainless steel I, High temperature water,” Proc. 7th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Breckenridge, Colorado, Aug. 7-10, 1995, p. 609 (1995).