Effects of hydrogen peroxide on intergranular stress corrosion cracking of stainless steel in high temperature water, (IV): Effects of oxide film on electrochemical corrosion potential

Journal of Nuclear Science and Technology

Volumn 38, Issue 3, 2001, Pages 183-192

  Wada, Yoichi ^a   Watanabe, Atsushi ^a   Tachibana, Masahiko ^a   Ishida, Kazushige ^a   Uetake, Naohito ^a   Uchida, Shunsuke ^a,d   Akamine, Kazuhiko ^a   Sambongi, Mitsuru ^b   Suzuki, Shunichi ^b   Ishigure, Kenkichi ^c,e  

^a HITACHI LTD   (Japan)

^b TOKYO ELECTRIC POWER COMPANY   (Japan)

^c UNIVERSITY OF TOKYO   (Japan)

^d TOHOKU UNIVERSITY   (Japan)

^e SAITAMA INSTITUTE OF TECHNOLOGY   (Japan)

Author keywords

BWR; Electrochemical corrosion potential; HWC; Hydrogen peroxide; Intergranular stress corrosion cracking; Oxide film; Stainless steels; Water chemistry

Indexed keywords

ELECTROCHEMICAL CORROSION; HIGH TEMPERATURE EFFECTS; HYDROGEN PEROXIDE; POLYTETRAFLUOROETHYLENES; STRESS CORROSION CRACKING; WATER;

ELECTROCHEMICAL CORROSION POTENTIAL; INTERGRANULAR STRESS CORROSION CRACKING; OXIDE FILM;

STAINLESS STEEL;

EID: 0035272276     PISSN: 00223131     EISSN: None     Source Type: Journal    
DOI: 10.1080/18811248.2001.9715020     Document Type: Article

References (17)

1. Uchida, S., et al: J. Nucl. Sci. Technol., 35, 301 (1998).
2. Uchida, S., et al: J. Nucl. Sci. Technol., 37, 257 (2000).
3. Wada, Y., et al: J. Nucl. Sci. Technol., 37, 901 (2000).
4. Uchida, S., et al.: Nucl. Technol., 110, 250 (1995).
5. Andresen, P. L., et al: State of knowledge of radiation effects on environmental cracking in light water reactor core materials, Proc. 4th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems- Water Reactors, Jekyll Island, Georgia, August 6-10, 1989, NACE, (1989).
6. Kim, Y. J.: Corrosion, 55, 81 (1999).
7. Kim, Y. J.: Corrosion, 51, 849 (1995).
8. Honda, T., et al: Boshoku Gijutsu, 37, 278 (1988) [in Japanese].
9. Kim, Y. J., et al: Development of ECP models for BWR application, Proc. Int. Symp. On Environmental Degradation of Materials in Nuclear Power System-Water Reactors, Breckenridge, Aug. 7-10, 1995, NACE, Vol. 2, 699 (1996).
10. Hishida, M., et al: Corrosion, 41, 570 (1985).
11. Macdonald, D. D., Macdonald, M. U.: Corrosion Sci., 32, 51 (1991).
12. Macdonald, D. D.: Calculation of corrosion potentials in boiling water, Proc. 5th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems- Water Reactors, Monterey, California, Aug. 25-29, 1991, ANS, 935 (1991).
13. Wada, Y., et al: Numerical simulation of SCC environment in a BWR primary coolant system, Proc. 8th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Amelia Island, California, Aug. 13-15, 1997, NACE, 574 (1997).
14. Kim, Y. J., et al: Electrochemical interactions of hydrogen, oxygen and hydrogen peroxide on metal surface in high temperature, high purity water, Proc. 8th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Amelia Island, California, Aug. 13-15, 1997, Natl. Assoc, of Corrosion Engineers, 641 (1997).
15. Ishigure, K., et al.: Solubility measurements and interactions of metal ions with oxides, Proc. Int. Conf. On Water Chemistry of Nuclear Reactor Systems 6, Vol. 2, Oct. 12-15, 1992, Bournmouth, BNES, 119 (1992).
16. Dinov, K., et al.: J. Nucl. Mater., 207, 266 (1993).
17. Hanzawa, Y.: Nucl. Sci. Eng., 127, 292 (1997).