A correlation between anodic film properties and stress corrosion cracking behavior of Alloy 600 and Alloy 690 in high-temperature caustic solutions

Corrosion

Volumn 59, Issue 3, 2003, Pages 203-206

  Hur, D H ^a  

^a Korea Atomic Energy Research Institute   (South Korea)

Author keywords

Alloy 600; Alloy 690; Anodic films; Auger electron spectroscopy; Electrochemical impedance spectroscopy; Semiconductivity; Sodium hydroxide; Stress corrosion cracking

Indexed keywords

ALLOYS; CAPACITANCE; COMPOSITION; SPECTROSCOPIC ANALYSIS;

ANODIC FILMS;

STRESS CORROSION CRACKING;

ALLOY; CORROSION; CRACKING; TEMPERATURE;

EID: 0037356335     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3277551     Document Type: Article

References (17)

1. G.-P. Yu, H.-C. Yao, Corrosion 46 (1990): p. 391.
2. T. Yonezawa, K. Onimura, N. Sasaguri, T. Kusakabe, H. Nagano, K. Yamanaka, T. Minami, M. Inoue, "Effect of Heat Treatment on Corrosion Resistance of Alloy 690," Proc. 2nd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (La Grange Park, IL: American Nuclear Society [ANS]. 1985), p. 593.
3. J.R. Crum, Corrosion 42 (1986): p. 368.
4. D.G. Briceno, M.L. Castano, M.S. Garcia, Nucl. Eng. Des. 165 (1996): p. 161.
5. G. Sui, J.M. Titchmarsh, G.B. Heys, J. Congleton, Corros. Sci. 39 (1997): p. 565.
6. F. Vaillant, J. Mithieux, O. Bouvier, D. Vancon, G. Zacharte, Y. Brechet, F. Louchet, "Influence of Chromium Content and Microstructure on Creep and PWSCC Resistance of Nickel-Based Alloys," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Warrendale, PA: The Minerals, Metals, and Materials Society [TMS], 1999), p. 251.
7. J.R. Cels, J. Electrochem. Soc. 123 (1976): p. 1, 152.
8. J.R. Cels, Corrosion 34 (1978): p. 198.
9. N. Pessall, G.P Airey, B.P. Lingenfelter, Corrosion 35 (1979): p. 100.
10. N. Pessall, Corros. Sci. 20 (1980): p. 225.
11. J.S. Baek, J.G. Kim, D.H. Hur, J.S. Kim, Corros. Sci. 45 (2003): p. 983.
12. C.Y. Chao, L.F. Lin, D.D. Macdonald, J. Electrochem. Soc. 128 (1981): p. 1, 187.
13. D.D. Macdonald, J. Electrochem, Soc. 139 (1992): p. 3,434.
14. J.B. Lumsden, P.J. Stocker, "Inhibition of IGA in Nickel-Based Alloys in Caustic Solution," CORROSION/88, paper no. 252 (Houston, TX: NACE International, 1988).
15. R. Bandy, R. Roberge, D. van Rooyen, Corrosion 41 (1985): p. 142.
16. D.H. Hur, J.S. Kim, J.S. Baek, J.G. Kim, Corrosion 58 (2002): p. 1,031.
17. S.A. Shei, W.J. Yang, "Stress Corrosion Crack Tip Microstructure in Nickel-Based Alloys," CORROSION/94, paper no. 154 (Houston, TX: NACE, 1994).