Stress corrosion cracking of alloy 600 and alloy 690 in hydrogen/steam at 380°C

Corrosion Science

Volumn 39, Issue 3, 1997, Pages 565-587

  Sui, G ^a   Titchmarsh, J M ^b   Heys, G B ^c   Congleton, J ^a  

^a NEWCASTLE UNIVERSITY   (United Kingdom)

^b SHEFFIELD HALLAM UNIVERSITY   (United Kingdom)

^c HMNII   (United Kingdom)

Author keywords

A. nickel alloys; B. STEM; C. stress corrosion

Indexed keywords

ANNEALING; CRACK INITIATION; CRACKS; ELECTRON MICROSCOPY; GRAIN BOUNDARIES; HYDROGEN; MATERIALS TESTING; NICKEL ALLOYS; STEAM; STRAIN; STRAIN MEASUREMENT;

HYDROGEN STEAM ENVIRONMENT; REVERSED U BEND TEST; SCANNING TRANSMISSION ELECTRON MICROSCOPY; STRAIN DISTRIBUTION;

STRESS CORROSION CRACKING;

ALLOYS; CORROSION; CRACKING; STRESS;

EID: 0031106381     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(97)86103-3     Document Type: Article

References (16)

1. P. Scott and M. Le Calvar, Some Possible Mechanisms of Intergranular Cracking of Alloy 600 in PWR Primary Water, Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, p. 657. San Diego, CA (1993).
2. C. H. Shen and P. G. Shewmon, Met. Trans. A 21A, 1261 (1990).
3. R. Bandy and D. Van Rooyen, Corrosion 40, 425 (1984).
4. E. L. Hall and C. L. Briant, Met. Trans. A 16A, 1225 (1985).
5. S. M. Payne and P. McIntyre, Corrosion 44, 314 (1987).
6. N. Totsuka, E. Lumarska, G. Cragnolino and Z. Szklarska-Smialowska, Corrosion 43, 505 (1987).
7. I. A. Vatter and J. M. Titchmarsh, Ultramicroscopy 28, 236 (1989).
8. S. G. Was, H. H. Tischner and R. M. Latanision, Met. Trans. A 12A, 1397 (1981).
9. E. L. Hall and C. L. Briant, Met. Trans. A 16A, 1397 (1985).
10. T. M. Angeliu and G. S. Was, Grain Boundary Chemistry and Precipitation in Controlled Purity Alloy 690, Proc. 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, p. 564. Jekyll Island, GA (1989).
11. N. Totsuka and Z. Szklarska-Smialowska, Corrosion 43, 734 (1987).
12. N. Totsuka and Z. Szklarska-Smialowska, Corrosion 44, 124 (1988).
13. K. Norring, J. Engstron, and P. Norberg, Intergranular Stress Corrosion Cracking in Steam Generator Tubing - Testing of Alloy 690 and Alloy 600 Tubes, Proc. 3rd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, p. 587. Warrendale, PA (1987).
14. R. H. Jones and S. M. Brummer, Environmental-Induced Crack Growth Processes in Nickel-Base Alloys, Environment-Induced Cracking of Metals, NACE-10, p. 287. Kohler, Wisconsin (1988).
15. R. C. Scarberry, W. L. Mankins, and M. J. Pohovey, Carbon Solubility in Alloy 690, Proceedings of Workshop on Thermally Treated Alloy 690 Tubes for Nuclear Steam Generators, paper 1. Pittsburgh, Pennsylvania (1986).
16. G. S. Was, Corrosion 46, 319 (1990).