Volumn 57, Issue 8, 2001, Pages 721-729

Variation of the fracture toughness of a high-strength pipeline steel under cathodic protection

(3) Andrews, P a McQueen, M a Millwood, N a

Author keywords

Cathodic protection; Crack tip opening displacement; Fracture toughness; Hydrogen embrittlement; Hydrogen induced stress cracking; Pipeline steel; X 80 steel

Indexed keywords

CALCULATIONS; CATHODIC PROTECTION; CRACKS; PH EFFECTS; STEEL; STRESSES;

STRESS CRACKING;

FRACTURE TOUGHNESS;

CATHODIC PROTECTION; CRACKING; FRACTURE TOUGHNESS; PIPELINE; STRESS;

EID: 0035422106 PISSN: 00109312 EISSN: None Source Type: Journal
DOI: 10.5006/1.3290400 Document Type: Article

Times cited : (12)

References (16)

1
- 5644255416
- API Specification 5L. 41st ed. (Washington, DC: API)
- (1995) Line Pipe

2
- 85037404093
- (in Japanese)
- (1980) Tetsu to Hagane , vol.67 , pp. 372
- Kasawara, K.¹ Isowaki, T.²

3
- 0004325093
- (in Japanese)
- (1992) Tetsu to Hagane , vol.78 , pp. 1818
- Yamaguchi, Y.¹ Nonaka, H.² Yamakaya, K.³

4
- 84856317596
- Fracture toughness (CTOD) of linepipe materials under cathodic protection
- paper no. 200 (Houston, TX: NACE International)
- (1997) CORROSION/97
- Hagiwara, N.¹ Oguchi, N.²

5
- 0003387776
- Standard test method for crack-tip opening displacement (CTOD) fracture toughness measurement
- ASTM E1290-98, (West Conshohocken, PA: ASTM)
- (1998) Annual Book of ASTM Standards

6
- 0003562246
- Standard test method for JIC. A measure of fracture toughness
- ASTM E813-89, (West Conshohocken, PA: ASTM)
- (1989) Annual Book of ASTM Standards

7
- 85037420189
- British Standard (BS) 7448 (London, England: British Standards Institution)
- (1991) Fracture Mechanics Toughness Tests , Issue.PART 1

8
- 0004197257
- Hydrogen-Induced stress corrosion cracking of the RAPL oil transportation pipeline as a result of the combined effect of cathodic protection and plastic deformation
- (London. England: Elsevier Applied Science)
- (1991) Proc. Pipe Protection Conference , pp. 257
- Punters, A.¹ Fikkers, A.T.² Vanstaen, G.³

9
- 0004254690
- (1988) Metall. Trans , vol.21 , Issue.A , pp. 1795
- Turnbull, A.¹ De Santa Maria, M.S.²

10
- 0013189565
- (1998) Corrosion , vol.54 , Issue.2 , pp. 115
- Qiao, L.J.¹ Luo, J.L.² Mao, X.³

11
- 0004261793
- (1993) Scr. Metall. Mater , vol.29 , pp. 623
- Griffiths, A.J.¹ Hutchings, R.B.² Turnbull, A.³

12
- 0022883111
- Evaluation of environmentally assisted cracking of a high-strength steel using elastic-plastic fracture mechanics techniques
- ASTM STP 905, (West Conshohocken, PA: ASTM)
- (1986) Fracture Mechanics , vol.17 , pp. 512
- Hackett, E.M.¹ Moran, P.J.² Gudas, J.P.³

13
- 0027589378
- (1993) Corrosion , vol.49 , Issue.5 , pp. 377
- Hartt, W.H.¹ Kumira, C.C.² Kessler, R.J.³

14
- 0642346318
- (1993) MP , vol.7 , pp. 14
- Wolfe, L.H.¹ Burnette, C.C.² Joosten, M.W.³

15
- 0031630711
- Variable amplitude corrosion fatigue behavior and hydrogen embrittlement of high-strength steels for offshore applications
- held May 24-29 (Golden, CO: The International Society of Offshore and Polar Engineers)
- (1998) Proc. 8th Int. Offshore and Polar Engineering Conference , pp. 116
- Coudert, E.¹ Renaudin, C.²

16
- 0003774697
- BSI PD 6493, (London, England: British Standards Institute)
- (1991) Guide on Methods for Assessing the Acceptability of Flaws in Fusion-Welded Structures

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.