Stress gradient effects in fretting fatigue

Tribology International

Volumn 36, Issue 2, 2003, Pages 71-78

  Nowell, David ^a   Dini, D ^a  

^a UNIVERSITY OF OXFORD   (United Kingdom)

Author keywords

Fretting fatigue; Notch analogue; Size effect; Stress gradient

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; STRESS ANALYSIS;

FRETTING FATIGUE;

TRIBOLOGY;

EID: 0037290525     PISSN: 0301679X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0301-679X(02)00134-2     Document Type: Article

References (48)

1. Eden E.M., Rose W.N., Cunningham F.L. The endurance of metals. Proc I Mech E. 4:1911;139.
2. Fenner AJ, Wright KHR, Mann JY. Fretting corrosion and its influence on fatigue failure. In: Proc Int Conf on Fatigue of Metals. London: I Mech E; 1956. p. 386.
3. Waterhouse R.B., Lamb M. Fretting corrosion of orthopaedic implant materials by bone cement. Wear. 60:1980;357-368.
4. Cardou A., Leblond A., Goudreau S., Cloutier L. Electrical conductor bending fatigue at suspension clamp: a fretting fatigue problem. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;257-266 M.E.P, London.
5. Farris T.N., Szolwinski M.P., Harish G. Fretting in aerospace structures and materials. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technology and practices, ASTM STP 1367. 2000;523-537 ASTM, West Conshohocken, PA.
6. Xi N.S., Zhong P.D., Huang H.Q., Yan H., Tao C.H. Failure investigation of blade and disk in first stage compressor. Engineering Failure Analysis. 7:2000;385-392.
7. Ruiz C., Nowell D. Designing against fretting fatigue in aeroengines. Fuentes M., Elices M., Martin-Meizoso A., Martinez-Esnaola J.M. Fracture mechanics, applications and challenges, Invited papers presented at the 13th European Conference on Fracture, ESIS publication 26. 2000;73-95 Elsevier, Amsterdam.
8. Attia MH, Waterhouse RB, editors. Standardization of fretting fatigue test methods and equipment, ASTM 1159. Philadelphia, PA: ASTM; 1990.
9. Hills D.A., Nowell D. Mechanics of fretting fatigue. 1994;Kluwer, Dordrecht.
10. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;M.E.P, London.
11. Hoeppner DW, Chandrasekaran V, Elliott CB, editors. Fretting fatigue: current technology and practices, ASTM STP 1367. West Conshohocken, PA: ASTM; 2000.
12. Kinyon SE, Hoeppner DW, Mutoh Y, editors. Fretting fatigue: experimental and analytical results, ASTM STP 1425. West Conshohocken, PA: ASTM; 2002.
13. Beard J. Palliatives for fretting fatigue. Waterhouse R.B., Lindley T.C. Fretting fatigue, ESIS 18. 1994;419-436 M.E.P, London.
14. Hills D.A., Nowell D. The development of a fretting fatigue experiment with well-defined characteristics. Attia M.H., Waterhouse R.B. Standardisation of fretting fatigue methods and equipment, ASTM STP 1159. 1992;69-84 ASTM, Philadelphia, PA.
15. Nishioka K., Hirakawa K. Fundamental investigations of fretting fatigue (part 5: the effect of relative slip amplitude). Bull JSME. 12:(52):1969;692-697.
16. Vingsbo O., Söderberg S. On fretting maps. Wear. 126:(2):1988;131-147.
17. Nowell D., Hills D.A., Moobola R. Length scale considerations in fretting fatigue. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technology and practices, ASTM STP 1367. 2000;141-153 ASTM, Philadelphia, PA.
18. Ciavarella M, Dini D, Demelio GP. Fretting fatigue, surface damage or fatigue phenomenon? Presented at 10th International Conference on Fracture, Honolulu; December 2001.
19. Szolwinski M.P., Harish G., McVeigh P.A., Farris T.N. Experimental study of fretting crack nucleation in aerospace alloys with emphasis on life prediction. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technology and practices, ASTM STP 1367. 2000;267-281 ASTM, Pennsylvania, PA.
20. Murthy H., Farris T.N., Slavik D.C. Fretting fatigue of Ti-6Al-4V subject to blade/disk contact loading. Materials Science Research, International Special Technical Publication 1, Materials Science for the 21st Century. 2001;200-207 Japan Society of Materials Science.
21. Nowell D., Araújo J.A. Analysis of pad size effects in fretting fatigue using short crack arrest methodologies. Int J Fatigue. 21:1999;947-956.
22. Nowell D., Araújo J.A. Prediction of fretting fatigue life using volume averaged multiaxial initiation parameters. Becker A.A. Proc. 4th Int. Conf. on Modern Practice in Stress and Vibration Analysis, Nottingham; 2000 Sep 5-7. 2000;223-234 EMAS, West Midlands.
23. Bramhall R. Studies in fretting fatigue. D.Phil. thesis, University of Oxford; 1973.
24. Johnson K.L. Contact mechanics. 1985;Cambridge University Press.
25. Nowell D. An analysis of fretting fatigue. D.Phil. Thesis, University of Oxford; 1988.
26. Hills D.A., Nowell D., O'Connor J.J. On the mechanics of fretting fatigue. Wear. 125:1988;129-156.
27. Araújo JA, Nowell D. The use of critical plane approaches to predict fretting fatigue initiation life of components subjected to different contact stress fields. In: Proc 6th International Conference on Biaxial/Multiaxial Fatigue, Lisbon; 2001.
28. Ruiz C., Boddington P.H.B., Chen K.C. An investigation of fatigue and fretting in a dovetail joint. Exp Mech. 24:(3):1984;208-217.
29. Ruiz C, Chen KC. Life assessment of dovetail joints between blades and discs in aero-engines. In: Proc. Int. Conf. on Fatigue. Sheffield: I. Mech. E; 1986.
30. Fouvry S., Kapsa P., Vincent L. A multiaxial fatigue analysis of fretting contact taking into account the size effect. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technology and practices, ASTM STP 1367. 2000;167-182 ASTM, Pennsylvania, PA.
31. Dang Van K., Griveau B., Message O. On a new multiaxial fatigue limit criterion: theory and application. Brown M.W., Miller K.J. Biaxial and multiaxial fatigue. 1989;479-496 Mech. Eng. Pubs, London.
32. Araújo J.A., Nowell D. The effect of rapidly varying contact stress fields on fretting fatigue. Int. J. Fatigue. 24:(7):2002;763-776.
33. Smith K.N., Watson P., Topper T.H. A stress-strain function for the fatigue of metals. J. Mater. 5:(4):1970;767-778.
34. Fatemi A., Socie D.F. A critical plane approach to multiaxial fatigue damage including out of phase loading. Fatigue Fract Eng Mater Struct. 11:1988;149-165.
35. Doner M, Bain KR, Adams JH. Evaluation of methods for the treatment of mean stress effects on low-cycle fatigue. J. Eng. Power 1981:1-9.
36. Slavik DC, McClain RD, Farris TN, Murthy H. Fatigue crack initiation modelling for applications with stress gradients in smooth and notched geometries. In: Proc. 6th Annual HCF Conference, Jacksonville, FL; 2001.
37. Nowell D., Araújo J.A. Small crack methodologies and crack arrest in fretting fatigue. Ravichandran K.S., Ritchie R.O., Murakami Y. Small fatigue cracks: mechanics, mechanisms, and applications. 1999;361-372 Elsevier.
38. Nowell D., Araújo J.A. Analysis of pad size effects in fretting fatigue using short crack arrest methodologies. Int J Fatigue. 21:1999;947-956.
39. Chan K.S., Lee Y.-D., Davidson D.L., Hudak S.J. Jr. A fracture mechanics approach to high cycle fretting fatigue based on the worst case fret concept: I. Model development. Int J Fracture. 112:2001;299-330.
40. Chan K.S., Lee Y.D., Davidson D.L., Hudak S.J. Jr. A fracture mechanics approach to high cycle fretting fatigue based on the worst case fret concept: II. Experimental evaluation. Int J Fracture. 112:2001;331-353.
41. Giannakopoulos A.E., Lindley T.C., Surseh S. Aspects of equivalence between contact mechanics and fracture mechanics: theoretical connections and a life prediction methodology for fretting-fatigue. Acta Mater. 46:1998;2955-2967.
42. Giannakopoulos A.E., Lindley T.C., Surseh S. Similarities of stress concentration in contact at round punches and fatigue at notches: implication to fretting fatigue crack initiation. Fatigue Fract Eng Mater Struct. 23:2000;561-571.
43. Ciavarella M., Hills D.A., Monno G. Influence of rounded edges on indentation by a flat punch. Proc I Mech E. 212(C):1998;219-228.
44. Ciavarella M., Demelio G., Hills D.A. An analysis of rotating bending fretting fatigue tests using bridge specimens. Hoeppner D.W., Chandrasekaran V., Elliott C.B. Fretting fatigue: current technology and practices, ASTM STP 1367. 2000;404-417 ASTM, Pennsylvania, PA.
45. Hills D.A., Nowell D., Sackfield A. Mechanics of elastic contacts. 1993;Butterworth-Heinemann, Oxford.
46. Lazzarin P., Tovo R., Filippi S. Stress distribution in finite size plates with edge notches. Int J Fracture. 91:1998;269-282.
47. Nowell D. Strain changes caused by finite width slots, with particular reference to residual stress measurement. J Strain Analysis. 34:(4):1999;285-294.
48. Crouch S.L., Starfield A.M. Boundary element methods in solid mechanics: with applications in rock mechanics and geological engineering. 1983;George Allen and Unwin, London.