A new route to carbon nanotubes [1]

Carbon

Volumn 41, Issue 1, 2003, Pages 179-181

  Shioyama, H ^a   Akita, T ^a  

^a NATIONAL INSTITUTE OF ADVANCED INDUSTRIAL SCIENCE AND TECHNOLOGY AIST   (Japan)

Author keywords

A. Carbon nanotubes, Intercalation compounds; B. Chemical treatment; C. Transmission electron microscopy

Indexed keywords

GRAPHITE; INTERCALATION COMPOUNDS; PYROLYSIS; TRANSMISSION ELECTRON MICROSCOPY; X RAY POWDER DIFFRACTION;

GRAPHITE INTERCALATION COMPOUNDS (GIC);

CARBON NANOTUBES;

EID: 0037215507     PISSN: 00086223     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0008-6223(02)00278-6     Document Type: Letter

References (11)

1. Shioyama H., Sakakihara H., Iwashita N., Tatsumi K., Sawada Y. On the generation of fine metallic particles in graphite matrix. J Mater Sci Lett 13:1994;1056-1057.
2. Shioyama H., Sakakihara H., Enomoto H., Iwashita N., Tatsumi K., Sawada Y. Fine metallic particles in graphite matrix. J Mater Sci Lett 15:1996;453-454.
3. Shioyama H. Polymerization of isoprene and stylene in the interlayer spacing of graphite. Carbon 35:1997;1664-1665.
4. Shioyama H., Tatsumi K., Iwashita N., Fujita K., Sawada Y. On the interaction between the potassium-GIC and unsaturated hydrocarbons. Synth Metals 96:1998;229-233.
5. Shioyama H. On the interaction between the alkali metal-GIC and unsaturated hydrocarbons. Mol Cryst Liq Cryst 340:2000;101-106.
6. Iijima S. Helical microtubes of graphitic carbon. Nature 354:1991;56-58.
7. Thess A., Lee R., Nikolaev P., Dai H., Petit P., Robert J., Xu C., Lee Y.H., Kim S.G., Rinzler A.G., Colbert D.T., Scuseria G.E., Tmoanek D., Fischer J.E., Smalley R.E. Crystalline ropes of metallic carbon nanotubes. Science 273:1996;483-487.
8. Bacon R. Growth, structure, and properties of graphite whiskers. J Appl Phys 31:1960;283-290.
9. Burleigh D.D., Thrower P.A. Irradiation damage to pyrolytic graphites at very high temperatures. Carbon 11:1973;505-510.
10. Kaburagi Y., Yoshida A., Hishiyama Y., Nagata Y., Inagaki M. Microstructure and crystallinity of highly crystalized graphite films prepared from aromatic polyimide films. Tanso 166:1995;19-27.
11. Despres J.F., Daguerre E., Lafdi K. Dynamic bond length as an explanation for the flexibility of graphene layers. Carbon 40:2002;445-447.