Thermal shock resistance of yttria-stabilized zirconia with Palmqvist indentation cracks

Journal of the European Ceramic Society

Volumn 23, Issue 1, 2003, Pages 107-114

  Fargas, G ^a   Casellas, D ^a   Llanes, L ^a   Anglada, M ^a  

^a UNIVERSITAT POLITÈCNICA DE CATALUNYA   (Spain)

Author keywords

Indentation; Palmqvist cracks; Thermal shock resistance; ZrO2

Indexed keywords

FRACTURE TOUGHNESS; POLYCRYSTALS; SHOCK PROBLEMS; STRESSES;

THERMAL SHOCKS;

ZIRCONIA;

CERAMICS; CORROSION RESISTANCE; CRACK; HIGH TEMPERATURE CORROSION; MATHEMATICAL ANALYSIS; ZIRCONIUM OXIDE;

EID: 0037212965     PISSN: 09552219     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0955-2219(02)00065-1     Document Type: Article

References (17)

1. Perspective on the development of high-toughness ceramics
2. Transformation toughening in zirconia-containing ceramics
3. Transformation toughening
4. Quantitatives studies of thermal shock in ceramics based on a novel test technique
5. Elastic energy as design criteria for thermal shock
6. Thermal stress resistance parameters for brittle refractory ceramics: A. compendium
7. The Vickers indentation technique used to evaluate thermal shock resistance of brittle materials
8. 5 or Ag particles
9. Analysis and prediction of thermal shock in brittle materials
10. Failure due to semielliptical surface cracks under arbitrary stress distributions
11. An analysis of the residual intensity factor of Vickers indentation cracks
12. 2 ceramics with mixed TZP/PSZ microstructures
13. Indentation pre-cracking of Y-TZP: Implications to R-curves and strength
14. A critical evaluation of indentation techniques for measuring fracture toughness: 1, direct crack measurements