Thermodynamic prediction of the nonstoichiometric phase Zr1-zCezO2-x in the ZrO2-CeO1.5-CeO2 system

Journal of the European Ceramic Society

Volumn 23, Issue 1, 2003, Pages 99-106

  Huang, Shuigen ^a   Li, Lin ^a   Vleugels, Jef ^b   Wang, Peiling ^c   Van Der Biest, Omer ^b  

^a SHANGHAI UNIVERSITY   (China)

^b UNIVERSITY OF LEUVEN   (Belgium)

^c SHANGHAI INSTITUTE OF CERAMICS   (China)

Author keywords

CeO2; Defects; Mechanical properties; Phase equilibria; Sintering; ZrO2

Indexed keywords

OXYGEN; PARAMETER ESTIMATION; PARTIAL PRESSURE; SINTERING; THERMODYNAMIC PROPERTIES; ZIRCONIUM COMPOUNDS;

NONSTOICHIOMETRIC PHASES;

CERAMIC MATERIALS;

THERMODYNAMICS;

EID: 0037212571     PISSN: 09552219     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0955-2219(02)00073-0     Document Type: Article

References (25)

1. Transformation toughening in zirconia-containing ceramics
2. 3 systems
3. 1.5 system
4. 2 system in air
5. 10
6. 2 system
7. 2 system
8. Strengthening of ceria-doped tetragonal zirconia polycrystals by reduction-induced phase transformation
9. 2±x >; Ln = Y, La, Nd, Gd
10. 2 below 1400 °C
11. 2 system
12. 2 system
13. 2 system
14. 3 from 1350 °C to 1900 °C
15. Specific heat of non-stoichiometric ceria (CeOy)
16. 2 single crystals
17. 2-x pour 1.5 < O/Ce < 2
18. Calculation of quasi-binary and quasi-ternary oxide systems I
19. Optimization of phase diagrams by a least squares method using simultaneously, different types of data
20. Enthalpies de formation des alliages liquides bismuth-etain-gallium a 723 K
21. A critical evaluation of indentation techniques for measuring fracture toughness: I, direct crack measurements
22. Impulse excitation apparatus to measure resonant frequencies, elastic moduli, and internal friction at room and high temperature