Micromechanical modeling of fracture initiation in 7050 aluminum

Engineering Fracture Mechanics

Volumn 69, Issue 18, 2002, Pages 2163-2186

  Hill, Michael R ^a   Panontin, Tina L ^b  

^a University of California Davis   (United States)

^b NASA AMES RESEARCH CENTER   (United States)

Author keywords

Aluminum; Constraint; Fracture; Micromechanical modeling

Indexed keywords

ALUMINUM; FINITE ELEMENT METHOD; FRACTURE; MECHANICAL TESTING;

PLASTIC STRAIN;

FRACTURE MECHANICS;

ALUMINUM; FRACTURE;

EID: 0037191423     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(01)00148-5     Document Type: Article

References (30)

1. The effect of residual stresses on brittle and ductile fracture initiation predicted by micromechanical models
2. Effect of thermomechanical loading on near tip constraint
3. Triaxial residual stresses affect driving force and constraint to alter fracture toughness
4. On the influence of state of stress on ductile failure initiation in high strength steels
5. On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states
6. WARP3D: 3-D dynamic nonlinear fracture analysis of solids using parallel computers and workstations
7. Test method for determining J-R curves
8. On the influence of microstructure on crack propagation mechanisms and fracture toughness of metallic materials
9. Role of state of stress in crack-tip failure processes
10. Cell model for nonlinear fracture analysis-II. Fracture-process calibration and verification
11. Experimentally verified finite element study of the stress-strain response of crack geometries experiencing large-scale yielding
12. Relationship between constraint and ductile fracture initiation as defined by micromechanical analyses
13. Family of crack-tip fields characterized by a triaxiality parameter. Part I: Structure of fields
14. Family of crack-tip fields characterized by a triaxiality parameter. Part II: Fracture applications
15. Two-parameter fracture mechanics: Theory and applications
16. The texture and formation of shear bands in a hot rolled 7050 aluminum alloy
17. IC, a measure of fracture toughness
18. Assessment of the reliability of J-R-curve testing as demonstrated through two nordic round-robin test
19. J-resistance curve testing of short crack bend specimens using unloading compliance
20. Test method for plain-strain fracture toughness of metallic materials
21. Micromechanical modeling of temperature-dependent initiation fracture toughness in advanced aluminum alloys
22. Direct evaluation of J-resistance curves from load displacement records
23. Obtaining J-resistance curves using the key-curve and elastic unloading compliance methods: An integrity assessment study
24. Nonincremental evaluation of modified J-R curve