Numerical analysis of indentation-induced cracking of brittle coatings on ductile substrates

International Journal of Solids and Structures

Volumn 39, Issue 6, 2002, Pages 1427-1442

  Abdul Baqi, A ^a   Van der Giessen, E ^b  

^a DELFT UNIVERSITY OF TECHNOLOGY   (Netherlands)

^b UNIVERSITY OF GRONINGEN   (Netherlands)

Author keywords

Coatings; Cohesive surface; Fracture; Indentation

Indexed keywords

BRITTLENESS; COATINGS; CRACK INITIATION; ELASTICITY; INDENTATION;

COHESIVE SURFACES;

SOLIDS;

BRITTLE MEDIUM; COATING; CRACK INITIATION; CRACK PROPAGATION; MATHEMATICAL ANALYSIS;

EID: 0037066164     PISSN: 00207683     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0020-7683(01)00280-3     Document Type: Article

References (19)

1. Indentation-induced interface delamination of a strong film on a ductile substrate
2. Delamination of a strong film from a ductile substrate during indentation unloading
3. Analysis of elastic and plastic deformation associated with indentation testing of thin films on substrates
4. Computational modelling of impact damage in brittle materials
5. Computation of post-bifurcation and post-failure behaviour of strain-softening solids
6. A method for interpreting the data from depth-sensing indentation instruments
7. Elastic contact versus indentation modeling of multi-layered materials
8. Elastic analysis of some punch problems for a layered medium
9. Measurement of fracture toughness of ultra-thin amorphous carbon films
10. Fracture mechanisms of thin amorphous carbon films in nanoindentation
11. Accurate determination of the mechanical properties of thin aluminum films deposited on sapphire flats using nanoindentations
12. Elastic modulus, indentation pressure and fracture toughness of hybrid coatings on glass
13. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments
14. Numerical and experimental study of the circular cracks observed at the contact edges of the indentations of coated systems with soft substrates
15. Energy base approach to the failure of brittle coatings on metallic substrates
16. The mechanical performance of DLC films on steel substrate
17. Void nucleation by inclusion debonding in a crystal matrix
18. Numerical simulations of fast crack growth in brittle solids