Formation of ordered mesoporous carbon material from a silica template by a one-step chemical vapour infiltration process

Chemistry Letters

Volumn , Issue 10, 2002, Pages 1062-1063

  Vix Guterl, Cathie ^a   Boulard, Séverine ^a,b   Parmentier, Julien ^a,b   Werckmann, Jacques ^a,b   Patarin, Joël ^a,b  

^a INSTITUT DE CHIMIE DES SURFACES ET INTERFACES   (France)

^b CNRS   (France)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON; SILICON DIOXIDE;

ARTICLE; CHEMICAL REACTION; SYNTHESIS; VAPOR;

EID: 0037027267     PISSN: 03667022     EISSN: None     Source Type: Journal    
DOI: 10.1246/cl.2002.1062     Document Type: Article

References (17)

1. H. F. Stoeckli, Carbon, 28, 1 (1990).
2. F. Rodriguez-Reinoso, in "Fundamental Issues in Control of Carbon Gasification Reactivity," ed. by J. Lahaye and P. Ehrburger, Kluwer Academic Publishers, Netherlands (1991), Vol. 192, p 533.
3. T. Kyotani, Carbon, 38, 269 (2000).
4. T. Kyotani, T. Nagai, S. Inoue, and A. Tomita, Chem. Mater., 9, 609 (1997).
5. Z.-X. Ma, T. Kyotani, and A. Tomita, Chem. Comm., 2000, 2365.
6. C. T. Kresge, M. E. Leonowicz, J. W. Roth, J. C. Vartuli, and J. S. Beck, Nature, 359, 710 (1992).
7. J. S. Beck, J. C. Vartuli, J. W. Roth, M. E. Leonowicz, C. T. Kresge, K. D. Schmitt, C. T. W. Chu, D. H. Olson, E. W. Sheppard, S. B. McCullen, J. B. Higgins, and J. L. Schlenker, J. Am. Chem. Soc., 114, 10834 (1992).
8. R. Ryoo, S. H. Joo, and S. Jun, J. Phys. Chem. B, 103, 7743 (1999).
9. R. Ryoo, S. H. Joo, M. Kruk, and M. Jaroniec, Adv. Mater., 13, 677 (2001).
10. M. Kruk, M. Jaroniec, R. Ryoo, and S. Hoon Joo, J. Phys. Chem. B, 104, 7960 (2000).
11. K. Schumacher, C. Von Hohenesche, K. K. Unger, R. Ulrich, A. Du Chesne, U. Wiesner, and H. W. Spiess, Adv. Mater., 11, 1194 (1999).
12. Estimated from the amount of nitrogen adsorbed at a relative pressure of 0.95 at 77 K.
13. Powder XRD patterns were recorded on a STOE STADI-P diffractometer, Cu Kα1 radiation (λ = 0.15406 nm).
14. S = 0.4 mm) electron microscope.
15. a(TEM) is determined by HRTEM using the fringe spacings measured from the position of the Bragg peaks in the Fourier transformed images.
16. Determined by nitrogen gas adsorption measurements carried out on a Micromeritics ASAP 2010 apparatus.
17. J. Parmentier, J. Dentzer, C. Vix-Guterl, and J. Patarin, Ceram. Int., 28, 1 (2002).