Novel synthesis of polymer and carbonaceous nanomaterials via a micelle/silicate nanostructured precursor

Chemical Communications

Volumn , Issue 17, 2002, Pages 1844-1845

  Moriguchi, Isamu ^a   Koga, Yasuhiro ^a   Matsukura, Ryosuke ^a   Teraoka, Yasutake ^b   Kodama, Masaya ^c  

^a NAGASAKI UNIVERSITY   (Japan)

^b KYUSHU UNIVERSITY   (Japan)

^c NATIONAL INSTITUTE OF ADVANCED INDUSTRIAL SCIENCE AND TECHNOLOGY AIST   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON; DIVINYLBENZENE; NANOPARTICLE; POLYMER; SILICATE;

ARTICLE; MICELLE; POLYMERIZATION; POROSITY; PRECURSOR; SURFACE PROPERTY; SYNTHESIS;

EID: 0036969991     PISSN: 13597345     EISSN: None     Source Type: Journal    
DOI: 10.1039/b204622a     Document Type: Article

References (10)

1. C. T. Kresge, M. E. Leonowicz, W. J. Roth, J. C. Vartuli and J. S. Beck, Nature, 1992, 359, 710.
2. S. Inagaki, Y. Fukushima and K. Kuroda, J. Chem. Soc., Chem. Commun., 1993, 680.
3. Q. Huo, D. I. Margolese, U. Ciesla, D. G. Gemuth, P. Feng, T. E. Goer, P. Sieger, A. Firouzi, B. F. Chmelka, F. Schmuth and G. D. Stucky, Chem. Mater., 1994, 6, 1176.
4. Y. M. Setoguchi, Y. Teraoka, I. Moriguchi, S. Kagawa, N. Tomonaga, A. Yasutake and J. Izumi, J. Porous. Mater., 1997, 4, 129.
5. J. S. Beck, R. H. Schmitt, E. L. Glove and R. D. Grown, J. Am. Chem. Soc., 1960, 82, 5292.
6. Y. Teraoka, S. Ishida, A. Yamasaki, N. Tomonaga, A. Yasutake, J. Izumi, I. Moriguchi and S. Kagawa, Microporous Mesoporous Mater., 2001, 48, 151.
7. The size of p-divinylbenzene is estimated to be 11 × 7 × 3.2 nm from CPK modeling.
8. Mesoporous silica was dispersed in liquid DVB under stirring at room temperature for 2 h and then was filtered off. The DVB-impregnated sample was the subjected to the same heating treatment as the above composite.
9. R. Ryoo, S. H. Joo and S. Jun, J. Phys. Chem. B, 1999, 103, 1401.
10. I. Moriguchi, Y. Koga and Y. Teraoka, unpublished data.