Experimental and analytical characterization of transverse cracking behavior in carbon/bismaleimide cross-ply laminates under mechanical fatigue loading

(2) Kobayashi, Satoshi a Takeda, Nobuo b

a TOKYO METROPOLITAN UNIVERSITY (Japan)

b UNIVERSITY OF TOKYO (Japan)

Author keywords

A. Laminates; A. Thermosetting resin; B. Fatigue; B. Transverse cracking

Indexed keywords

CRACKS; FATIGUE OF MATERIALS; HIGH TEMPERATURE EFFECTS; LAMINATES; OPTICAL MICROSCOPY; STRUCTURAL LOADS; THERMOSETS; X RAY RADIOGRAPHY;

TRANSVERSE CRACKING;

CARBON FIBER REINFORCED PLASTICS;

EID: 0036714165 PISSN: 13598368 EISSN: None Source Type: Journal
DOI: 10.1016/S1359-8368(02)00028-8 Document Type: Article

Times cited : (27)

References (17)

1
- 0031623094
- The influence of the variation of the coefficient of thermal expansion with temperature on the microcracking behavior of K3B/IM7 and X5260/G40-800 composites
- (1998) Compos Part B , vol.29 , pp. 391-396
- Huang, X.¹ Eduljee, R.F.² Gillespie J.W., Jr.³

2
- 0033362191
- Effect of moisture absorption on hot/wet compressive strength of T800H/PMR-15 carbon/polyimide
- (1999) J Compos Mater , vol.33 , pp. 1685-1698
- Shimokawa, T.¹ Hamaguchi, Y.² Katoh, H.³

3
- 0032818337
- The effect of thermal aging on the Mode I interlaminar fracture behavior of a high-temperature IM7/LarC-RP46 composite
- (1999) Compos Sci Technol , vol.59 , pp. 1271-1286
- Hutapea, P.¹ Yuan, F.G.²

4
- 0033221992
- Bismaleimide composites come of age: BMI sciences and applications
- (1999) SAMPE J , vol.35 , pp. 13-22
- Boyd, J.¹

5
- 0034025162
- Matrix cracking behavior of K3B/IM7 composite laminates subject to static and fatigue loading
- (2000) Compos Struct , vol.49 , pp. 435-441
- Huang, X.¹ Gillespie J.W., Jr.² Eduljee, R.F.³ Shen, Z.⁴

6
- 0034326163
- Thermal degradation of IM7/BMI5260 composite materials: Characterization by X-ray photoelectron spectroscopy
- (2000) Mater Sci Engng A , vol.293 , pp. 88-94
- Ohno, S.¹ Lee, M.H.² Lin, K.Y.³ Ohuchi, F.S.⁴

7
- 0019637018
- Fatigue of composite materials: Damage mechanisms and fatigue-life diagrams
- (1982) Proc R Soc Lond , vol.A378 , pp. 461-475
- Talreja, R.¹

8
- 0022245951
- A conceptual framework for the interpretation of fatigue damage mechanisms in composite materials
- (1985) J Compos Tech Res , vol.7 , pp. 25-29
- Talreja, R.¹

9
- 85167969617
- An investigation of cumulative damage development in quasi-isotropic graphite/epoxy laminates
- (1980) ASTM STP , vol.775 , pp. 40-62
- Masters, J.E.¹ Reifsnider, K.L.²

10
- 84958508474
- Characterization of delamination onset and growth in a composite laminate
- (1980) ASTM STP , vol.775 , pp. 140-167
- O'Brien, T.K.¹

11
- 0002359452
- Metals Park, OH: ASM International
- (1987) Strength, failure and fatigue analysis of laminates, composites, engineering materials handbook , vol.1 , pp. 236-251
- Wang, A.S.D.¹

12
- 0022873696
- Damage mechanisms and accumulation in graphite/epoxy laminates
- (1986) ASTM STP , vol.907 , pp. 274-297
- Charewicz, A.¹ Daniel, I.M.²

13
- 0001502051
- Fracture mechanics analysis of composite microcracking: Experimental results in fatigue
- American Society for Composites
- (1990) Proceedings of the Fifth Technical Conference on Composites Materials , pp. 287-295
- Liu, S.¹ Nairn, J.A.²

14
- 0003903977
- Microcracking, microcrack-induced delamination, and longitudinal splitting of advanced composite structures
- (1992) NASA Contractor Report , pp. 4472
- Nairn, J.A.¹

15
- 0000621169
- Microscopic fatigue damage progress in CFRP cross-ply laminates
- (1995) Composites , vol.26 , pp. 859-867
- Takeda, N.¹ Ogihara, S.² Kobayashi, A.³

16
- 84970126128
- The strain energy release rate of composite microcracking: A variational approach
- (1989) J Comp Mater , vol.23 , pp. 1106-1129
- Nairn, J.A.¹

17
- 0022098062
- Analysis of cracked laminates: A variational approach
- (1985) Mech Mater , vol.4 , pp. 121-136
- Hashin, Z.¹

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.