Scale adhesion, sulfur content, and TBC failure on single crystal superalloys

Ceramic Engineering and Science Proceedings

Volumn 23, Issue 4, 2002, Pages 485-495

  Smialek, James L ^a  

^a NASA GLENN RESEARCH CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ADHESION; ANNEALING; COMPOSITION EFFECTS; DECARBURIZATION; DELAMINATION; DESULFURIZATION; FAILURE (MECHANICAL); OXIDATION; SINGLE CRYSTALS; SULFUR; THERMAL BARRIER COATINGS;

BUCKLING FAILURE MODES; HYDROGEN ANNEALING; SCALE ADHESION; SULFUR CONTENT;

SUPERALLOYS;

EID: 0036460595     PISSN: 01966219     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (19)

1. 3 Scales," JOM, 52 [1] 22-26 (2000).
2. J.L. Smialek, "Advances in the oxidation resistance of high-temperature turbine materials," Surface and Interface Analysis, 31 582-592 (2001).
3. J.L. Smialek, "Oxidation Resistance and Critical Sulfur Content of Single Crystal Superalloys," Transactions of the ASME, 120 370-374 (1998).
4. J.L. Smialek, "Toward Optimum Scale and TBC Adhesion on Single Crystal Superalloys," pp. 211-220 in High Temperature Corrosion and Materials Chemistry, 98-9, Edited by E.J. Opila, P.Y. Hou, D.Shores, M. McNallan, and R. Oltra. The Electrochemical Society, Pennington, NJ, 1998.
5. J.L. Smialek and B.A. Pint, "Optimizing Scale Adhesion for Single Crystal Superalloys," Materials Science Forum, 369-372 459-466 (2001).
6. J.L. Smialek and G.N. Morscher, "Delayed Alumina Scale Spallation on Rene'N5: Moisture Effects and Acoustic Emission," Materials Science and Engineering, accepted for publication.
7. G.H. Meier, F.S. Pettit, and J.L. Smialek, "The Effects of Reactive Element Additions and Sulfur Removal on the Adherence of Alumina to Ni- and Fe-Base Alloys," Werkstoffe und Korrosion, 46 232-240 (1995).
8. V.Sergo and D.R. Clarke, "Observation of Subcritical Spall Propagation of a Thermal Barrier Coating," Journal of the American Ceramic Society, 81 [12] 142-161 (1998).
9. 3," Journal of Materials Science, 27 2377-2382 (1992).
10. J.A. Haynes, B.A. Pint, K.L. Moore, I.G. Wright, and J.L. Smialek, "Superalloy Substrate Influences on the Oxidation Behavior of Aluminide Bond Coatings," submitted to Oxidation of Metals.
11. 3 Interfaces, Acta Materialia., 45 3503-3513 (1997)
12. I.G. Wright, B.A. Pint, W.Y. Lee, K.B. Alexander, and K. Prüßner, "Some Effects of Metallic Substrate Composition on Degradation of Thermal Barrier Coatings," pp. 95-113 in High Temperature Surface Engineering," Book 693, Edited by J. Nicholls and D. Rickerby, Institute of Materials, London, 2000
13. J.L. Smialek, "The Effect of Hydrogen Annealing on the Impurity Content of Alumina-Forming Alloys," Oxidation of Metals, 55 [1/2] 75-86 (2001).
14. W.Y. Lee, Y Zhang, I.G. Wright, B.A. Pint, and P.K. Liaw, "Effect of Sulfur Impurity on the Scale Adhesion Behavior of a Desulfurized Ni-based Superalloy Aluminized by Chemical Vapor Deposition," Metallurgical Transactions, 29A 833-841 (1998).
15. B. A. Pint, I. G. Wright, W. Y. Lee, Y. Zhang, K. Prüßner and K. B. Alexander, "Substrate and Bond Coat Compositions: Factors Affecting Alumina Scale Adhesion," Materials Science and Engineering, A245 201-211 (1998).
16. X. Peng and D.R. Clarke, "Piezospectroscopic Analysis of Interface Debonding in Thermal Barrier Coatings," Journal of the American Ceramic Society," 83, [5] 1165-1170 (2000).
17. R. Janakiraman, G.H. Meier, and F. S. Pettit, "The Effect of Water Vapor on the Oxidation of Alloys that Develop Alumina Scales for Protection", pp. 38-62 in Cyclic Oxidation of High Temperature Materials, Editors M. Schutze and W.J. Quadakker, European Federation of Corrosion, Institution of Materials, London, 1999.
18. H.E. Evans, G.P. Mitchell, R.C. Lobb, and D.R.J. Owen, "A numerical analysis of oxide spallation," Proceedings of the Royal Society of London, 440A 1-22 (1993).
19. J.L. Smialek: "Segmented Thermal Barrier Coating" U.S. Patent 6,316,078, Nov. 13, 2001.