Bolt bearing fatigue of polymer matrix composites at elevated temperature

International Journal of Fatigue

Volumn 24, Issue 2-4, 2002, Pages 197-204

  Counts, W A ^a   Johnson, W S ^a  

^a GEORGIA INSTITUTE OF TECHNOLOGY   (United States)

Author keywords

Bearing failure; Bearing fatigue; Bolted composite joint; Elevated temperature

Indexed keywords

AGING OF MATERIALS; BEARING CAPACITY; BOLTS; BUCKLING; COMPUTER SIMULATION; DELAMINATION; FAILURE ANALYSIS; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE; HIGH TEMPERATURE EFFECTS; LOADS (FORCES); STRESS ANALYSIS;

POLYMER MATRIX COMPOSITES (PMC);

NONMETALLIC MATRIX COMPOSITES;

EID: 0036141002     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(01)00073-1     Document Type: Article

References (14)

1. Fatigue failure of composite bolted joints
2. Strength and lifetime of bolted laminates
3. Bearing failure of bolted composite joints. Part I: Experimental characterization
4. Failure mechanisms in bolted CFRP
5. Fatigue of bolted joints in (0/90) CFRP laminates
6. On the bearing strength of fibre metal laminates
7. On the bearing strength of bolted graphite/epoxy laminates
8. Bolt bearing behavior of highly loaded polymer matrix composite joints at elevated temperatures with and without clamp-up
9. Evaluation of bolt bearing behavior of highly loaded composite joints at elevated temperature
10. Assessing life prediction methodologies for fasteners under bending loads
11. Influence of the variation of the coefficient of thermal expansion with temperature on the microcracking behavior of K3B/IM7 and X5260/G40-800 composites
12. Temperature effect on ultimate bearing strength of polymeric composite joints
13. Development of composites, adhesives and sealants for high speed commercial airplanes