An energy criterion for the initiation of interface failure ahead of a matrix crack in brittle matrix composites

Composite Interfaces

Volumn 9, Issue 2, 2002, Pages 143-156

  Martin, Eric ^a   Leguillon, Dominique ^a   Lacroix, Cécile ^a  

^a DIF   (France)

Author keywords

Ceramic matrix composite; Crack deflection; Energetic analysis; Interfacial debonding

Indexed keywords

BRITTLE FRACTURE; CRACK PROPAGATION; DEBONDING; ELASTICITY; FRACTURE TOUGHNESS; INTERFACES (MATERIALS); NUCLEATION; STRESS CONCENTRATION;

INTERFACIAL TOUGHNESS;

CERAMIC MATRIX COMPOSITES;

EID: 0036090303     PISSN: 09276440     EISSN: None     Source Type: Journal    
DOI: 10.1163/156855402760116076     Document Type: Article

References (26)

1. The influence of the interphase and associated interfaces on the deflection of matrix cracks in ceramic matrix composites
2. A mechanism for the control of crack propagation in all brittle systems
3. Fatigue crack growth in selectively reinforced titanium metal matrix composites
4. The role of the interface in fiber reinforced brittle matrix
5. Crack deflection at an interface between two orthotropic media
6. Crack deflection at an interface between dissimilar elastic materials
7. The interaction of a crack with an interface crack as a theoretical model for debonding
8. Direct observation and modelling of the crack fibre interaction process in continuous fibre-reinforced ceramics: Model experiments
9. Growth of interface defects and its effect on crack deflection and toughening criteria
10. Asymptotic and numerical analysis of a crack branching in non-isotropic materials
11. Fracture in heterogeneous materials - Weak and strong singularities
12. Interface debonding ahead of a primary crack
13. Matrix crack deflection at an interface between a stiff matrix and a soft inclusion
14. Evaluation of the tensile interface strength in brittle matrix composite systems
15. The effect of flaws on the propagation of cracks at bimaterials interfaces
16. Conditions for matrix crack deflection at an interface in ceramic matrix composites
17. A revisited criterion for crack deflection at an interface in brittle matrix composites
18. Energy criterion for crack deflection at an interface between two orthotropic media
19. Fibre matrix interphases and interfaces in ceramic matrix composites processed by CVI
20. On the micromechanical failure modes in a class of ideal brittle matrix composites Part 1. Coated-fiber composites
21. Fracture normal to a bimaterial interface: Effects on plasticity on crack-tip shielding and amplification
22. The disruption of a longitudinal interface by a moving transverse crack
23. Interface effects on crack deflection and bridging during fatigue crack growth of titanium matrix composites
24. Delamination study using four-point bending of bilayers