Mixed monolayers self-assembled on mica surface

Langmuir

Volumn 17, Issue 14, 2001, Pages 4274-4281

  Kitaev, Vladimir ^a   Seo, Minseok ^a   McGovern, Mark E ^a   Huang, Yen Jung ^a   Kumacheva, Eugenia ^a  

^a UNIVERSITY OF TORONTO   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

POSITIVELY CHARGED AMPHIPHILES;

ATOMIC FORCE MICROSCOPY; COMPOSITION; CONTACT ANGLE; MICA; SELF ASSEMBLY; SILANES; X RAY PHOTOELECTRON SPECTROSCOPY;

MONOLAYERS;

EID: 0035838782     PISSN: 07437463     EISSN: None     Source Type: Journal    
DOI: 10.1021/la0015359     Document Type: Article

References (44)

1. Ulman, A. Thin Solid Films 1996, 273, 48.
2. (a) Nuzzo, R.G.; Allara, D.L. J. Am. Chem. Soc. 1983, 105, 4481.
3. (b) Nyquist, R.M.; Eberhardt, A.S.; Silks, L.A.; Li, Z.; Yang, X.; Swanson, B.I. Langmuir 2000, 16, 1793.
4. (c) Beake, B.D.; Leggett, G. J. Phys. Chem. Chem. Phys. 1999, 14, 3345.
5. Lagutchev, A.S.; Song, K.J.; Huang, J.Y.; Yang, P.K.; Chuang, T. J. Chem. Phys. 1998, 226, 337.
6. (a) Banga, R.; Yarwood, J.; Morgan, A.M.; Evans, B.; Kells, J. Langmuir 1995, 11, 4393.
7. (b) Hoffmann, H.; Mayer, U.; Krischanitz, A. Langmuir 1995, 11, 1304.
8. (c) Takahara, A.; Kojio, K.; Ge, S.R.; Kajiyama, T. J. Vac. Sci. Technol., A 1996, 14, 1747.
9. (d) Calistri-Yeh, M.; Kramer, E.J.; Sharma, R.; Zhao, W.; Rafailovich, M.H.; Sokolov, J.; Brock, J.D. Langmuir 1996, 12, 2747.
10. (e) Yang, J.Y.M.; Frank, C.W. Org. Thin Films 1998, 695, 67.
11. Xu, F.; Zhu, J.; Mirkin, C.A. Langmuir 2000, 16, 2169.
12. Nakagawa, T.; Soga, M. Jpn. J. Appl. Phys. 1997, 36, 5226.
13. Fang, J.; Knobler, C.M. Langmuir 1996, 12, 1368.
14. Magonov, S.; Whangbo, M.-H. Surface Analysis with STM and AFM; VCH: Weinheim, 1996.
15. (a) Christenson, H.K.; Gruen, D.W.R.; Horn, R.G.; Israelachvili, J.N. J. Chem. Phys. 1987, 87, 1834.
16. (b) Klein, J.; Kumacheva, E. J. Chem. Phys. 1998, 108, 6996.
17. (a) Carson, G.A.; Granick, S. J. Mater. Res. 1990, 5, 1745.
18. (b) Schwartz, D.K.; Israelachvili, J.; Steinberg, S.; Zasadzinski, J.A.N. Phys. Rev. Lett. 1992, 69, 3354.
19. (c) Woodward, J.T.; Ulman, A.; Schwartz, D.K. Langmuir 1996, 12, 3626.
20. (a) Herder, P.C.; Claesson, P.M.; Herder, C.E. J. Colloid Interface Sci. 1987, 119, 155.
21. (b) Chen, Y.L.; Chen, S.; Frank, C.; Israelachvili, J. J. Colloid. Interface Sci. 1992, 153, 244.
22. Mao, G.; Tsao, Y.; Tirrell, M.; Davis, T.; Hessel, V.; Ringsdorf, H. Langmuir 1995, 11, 942.
23. (a) McGovern, M.E.; Kallury, K.M.R.; Thompson, M. Langmuir 1994, 10, 3607.
24. (b) McGovern, M.E.; Thompson, M. Can. J. Chem. 1999, 77, 1678.
25. (a) Kitaev, V.; Schillen, K.; Kumacheva, E. J. Polym. Sci., Part B 1998, 36, 1567.
26. (b) Sohn, D.; Kitaev, V.; Kumacheva, E. Langmuir 1999, 15, 1698.
27. (a) Cheng, S.S.; Scherson, D.A.; Sukenik, C.N. Langmuir 1995, 11, 1190.
28. (b) Fryxell, G.E.; Rieke, P.C.; Wood, L.L.; Engelhard, M.H.; Williford, R.E.; Graft, G.L.; Campbell, A.A.; Wiacek, R.J.; Lee, L.; Halverson, A. Langmuir 1996, 12, 5064.
29. Wasserman, S.R.; Tao, Y.-T.; Whitesides, G.M. Langmuir 1989, 5, 1074.
30. Ulman, A. Private communication.
31. For immobilization of rigid-rod polypeptide molecules, such as poly(γ-benzyl-L-glutamate), in a homeotropic orientation on the surface, the required fraction of active functional groups in the layer is ca. 8 mol %. Thus, even with a relatively low yield of activation of ester groups in the mixed silane layer, the concentration of F-Si in the layer of ca. 15 mol % should be sufficient for polypeptide attachment.
32. Berresheim, K.; Mattern-Klossen, M.; Wilmers, M. Fresenius' J. Anal. Chem. 1991, 341, 121.
33. The signal of the C(1s) peak was not reliable because of the unavoidable carbon contaminations.
34. Andrade, J.D: Surface and Interfacial Aspects of Biomedical Polymers; Plenum Press: New York, 1985.
35. Solletti, J.M.; Botreau, M.; Sommer, F.; Brunat, W.L.; Kasas, S.; Tran Minh Duc; Cello, M.R. Langmuir 1996, 12, 5379.
36. Bain, C.D.; Whitesides, G.M. J. Phys. Chem. 1989, 93, 1670.
37. (a) Wenzel, R.N. Ind. Eng. Chem. 1936, 28, 988.
38. (b) Neumann, A.W.; Good, R.J. J. Colloid Interface Sci. 1972, 38, 341.
39. The value of λ = 3.75 ± 0.25 nm was found for pure hydrocarbons. We assumed that the same λ can be used for C-8 molecules composed of a relatively long hydrocarbon tail and a single functional silane group.
40. Ulman, A. In Characterization of Organic Films; Butterworth-Heinemann: Boston, 1995; pp 21-31.
41. Inglese, A.; De Lisi, R.; Milioto, S. J. Phys. Chem. 1996, 100, 2260.
42. Eriksson, L.G.T.; Claesson, P.M.; Eriksson, J.C.; Yaminsky, V.V. J. Colloid Interface Sci. 1996, 181, 476.
43. Tanuma, S.; Powell, S.J.; Penn, D.R. Surf. Sci. 1987, 192, L849.
44. 11a However, the value of λ = 2.1-2.2 nm agrees well with the theoretical estimate of λ = 2.15 nm for K(2p) (ref 29).