New phenomena concerning the effect of imperfect bonding on radial matrix cracking in fiber composites

International Journal of Engineering Science

Volumn 39, Issue 18, 2001, Pages 2033-2050

  Liu, Y ^a   Ru, C Q ^a   Schiavone, P ^a   Mioduchowski, A ^a  

^a UNIVERSITY OF ALBERTA   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

BONDING; CRACK PROPAGATION; DEFORMATION; INTERFACES (MATERIALS); LOADS (FORCES); STIFFNESS MATRIX; STRESS INTENSITY FACTORS;

RADIAL MATRIX CRACKING;

FIBER REINFORCED MATERIALS;

EID: 0035546707     PISSN: 00207225     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0020-7225(01)00049-0     Document Type: Article

References (27)

1. Damage in composite-modeling of imperfect bounding
2. Effect of interfacial zone on mechanical behavior and failure of fiber-reinforced composites
3. Effect of interphases on micro and macromechanical behavior of hexageonal-array fiber composites
4. The interaction between a crack and an inclusion
5. On the effect of debonding on the overall behavior of composite materials
6. Fiber-matrix debonding defects on cracking in aligned fiber ceramic composites
7. Matrix fracture in fiber-reinforced ceramics
8. Interaction between an edge dislocation and a circular inclusion
9. Edge dislocation near an inclusion with a slipping interface
10. Interaction between a circular inclusion and an arbitrarily oriented crack
11. A circular inclusion with imperfect interface: Eshelby's tensor and related problems
12. Interfacial debonding analysis in multiple fiber reinforced composites
13. Crack-fiber interaction and interfacial failure modes in fiber-reinforced ceramics
14. Micromechanics of osteonal cortical bone fracture
15. Thermoelastic properties of fiber composite with imperfect interface
16. The spherical inclusion with imperfect interface
17. Weak interface in long fiber composites
18. Modeling of interphases in fiber-reinforced composites under transverse loading using the boundary element method
19. Inclusion problems
20. A circular inclusion with circumferentially inhomogeneous interface in antiplane shear
21. A circular inclusion with circumferentially inhomogeneous sliding interface in plane elastostatics
22. Residual stresses at interfaces in fiber reinforced composites. Residual stresses-III
23. A screw dislocation interacting with a coated fiber
24. The effect of a circular inclusion on the stress around a line crack in a sheet under tension
25. Effect thermoelastic moduli of a unidirectional fiber composite containing interfacial arc microcracks