Effects of temperature on impact damages in CFRP composite laminates

Composites Part B:Engineering

Volumn 32, Issue 8, 2001, Pages 669-682

  Im, Kwang Hee ^a   Cha, Cheon Seok ^b   Kim, Sun Kyu ^c   Yang, In Young ^b  

^a Woosuk University   (South Korea)

^b Chosun University   (South Korea)

^c Iksan National College   (South Korea)

Author keywords

B. Delamination; C. Transverse cracking; Carbon fiber reinforced plastics (CFRP)

Indexed keywords

CRACK INITIATION; DELAMINATION; LAMINATED COMPOSITES; NONDESTRUCTIVE EXAMINATION;

SCANNING ACOUSTIC MICROSCOPY (SAM);

CARBON FIBER REINFORCED PLASTICS;

EID: 0035545806     PISSN: 13598368     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-8368(01)00046-4     Document Type: Article

References (28)

1. Damage and residual bending strength of graphite/epoxy composite laminates subjected to normal impact
2. Hygrothermal effect on the PEEK/C.F. and PPS/C. F. under impact loading(I)
3. Impulsive response and fracture of composites (I)
4. Foreign object damages to composite materials
5. The damage tolerance of carbon fiber reinforced composites: A workshop summary
6. Effect of impact loading on damage and residual compressive strength of CFRP laminated beams
7. Impact damages and residual bending strength of CFRP composite laminates subjected to impact loading
8. Determination of crack propagation directions in graphite/epoxy structures. Composites and metals
9. Delamination damage in central impacts at subperformation speeds on laminated Kevlar/Epoxy plates
10. Horizontal wing structure of civil airplane using composite materials
11. Multiple transverse failure in 90° cross-ply laminate of a glass fiber-reinforced polyester
12. On multiple transverse cracking in glass fiber expoxy cross-ply laminates
13. Impact on laminated composite materials
14. Effects of sea water immersion on the impact resistance of glass reinforced epoxy composites
15. Computational models for high-temperature multilayered composite plates and shells
16. Cryogenic properties of composite materials
17. High-temperature damage tolerence of carbon fiber-reinforced plastics
18. A study on residual fatigue bending strength and damage behavior of CFRP composites subjected to impact loading
19. Impact damage and hygrothermal effects on fatigue bending strength of orthotropy composite laminates
20. Impact damage characterization of carbon fiber/epoxy composites with multi-layer reinforcement
21. Response of thick, notched laminates subjected to tension-compression cycle loads. Composite materials: Fatigue and fracture
22. Residual strength of composite laminate subjected to tensile-compressive fatigue loading
23. The mechanical performance and impact behaviour of carbon-fiber reinforced PEEK
24. Detection of impact damage in CFRP laminates
25. Impact damages in CFRP laminates under high temperature
26. An Investigation of the effects of temperature on the impact behavior and residual tensile strength of an aramid aluminum laminates (arall-1 laminates). Composite materials: Fatigue and fracture
27. Delamination damage in central impacts at subperformation speeds on laminated Kevlar/Epoxy plates