Impact damage and hygrothermal effects on fatigue bending strength of orthotropy composite laminates

KSME International Journal

Volumn 13, Issue 7, 1999, Pages 524-535

  Im, Kwang Hee ^a   Sun Kyu, Kim ^b   Yang, In Young ^a  

^a Chosun University   (South Korea)

^b Iksan National College   (South Korea)

Author keywords

Carbon Fiber Reinforced Plastics (CFRP); Foreign Object Damages (FOD); Hygrothermals; Impact damages; Impact energy; Moisture absorbtion content; Residual fatigue bending strength

Indexed keywords

EID: 0033164794     PISSN: 12264865     EISSN: None     Source Type: Journal    
DOI: 10.1007/BF03186443     Document Type: Article

References (18)

1. ASTM, 1973, Foreign Object Impact Damage to Composites, STP568. pp. 2160∼2190.
2. Bakis C. E. and Stinchcomb W. W. (Hahn H. H), 1989, "Response of Thick, Notched Laminates Subjected to Tension-Compression Cycle Loads," Composite Materials : Fatigue and Fracture, ASTM STP, 907, pp. 314∼438.
3. Challenger K. D., 1986, "The Damage Tolerance of Carbon Fiber Reinforced Composites," A Workshop Summary, Composite Struct., pp. 295 ∼318.
4. Dewimille B., Tjoris J., Mailfert R. and Bunsell A. R., 1980, "Hygrothermal Aging of an Unidirectional Epoxy Composites During Water Immersion," Advances in Composite Materials, Vol. 1, pp. 597∼612.
5. Im K. H., Sim J. K. and Yang I. Y., 1996, "Impact Damages and Residual Bending Strength of CFRP Composite Laminates Subjected to Impact Loading," KSME International Journal, Vol. 10, No. 4, pp. 423∼434.
6. Ishai O. and Arnon V., 1978, "Instantaneous Effects of Internal Moisture Conditions on Strength of Glass-Fiber-Reinforced Plastics," ASTM, pp. 267∼276.
7. Lubin G., 1982, "Handbook of Composites, Van Nostrand Reinhold," p. 147.
8. Ma C. C. M., Huang Y. H., and Chang M. J., 1991, "Hygrothermal Effect on the PEEK/C. F. and PPS/C. F. under Impact Loading(I)," ANTEC, pp. 2029∼2096.
9. Malvern L. E., Sun C. T. and Liu D., 1989, "Delamination Damage in Central Impacts at Subperformation Speeds on Laminated Kevlar/ Epoxy Plates," ASTM. STP. 1012, pp. 387∼405.
10. Rotem A. and Nelson H. G., 1990, "Residual Strength of Composite Laminate Subjected to Tensile-Compressive Fatigue Loading," Journal of Composites Technology & Research, Vol. 12, No. 2, pp. 76∼84.
11. Smith B. W. and Grove R. A., 1987, "Determination of Crack Propagation Directions in Graphite/Epoxy Structures," Composites and Metals, ASTM. STP. 948, pp. 154∼173.
12. Sirkis J. S., Chang C. C. and Smith B. T., 1994, "Low Velocity Impact of Optical Fiber Embedded Laminated Graphite/Epoxy Panels. Part I : Macro-Scale," Journal of Composite Materials, Vol. 28, No. 14, pp. 1347∼1371.
13. Stephen W. and Hahn H. T., 1980, Introduction to Composite Materiale, Technomic Publishing C., Inc., pp. 329∼340.
14. Takeda T., 1985, "Impulsive Response and Fracture of Composites ( I )," Journal of the Japan Society for Composite Materials, Vol. 11, No. 4, pp. 151∼161.
15. Tanaka T., Kurokawa T., etc., 1989, "Damage and Residual Bending Strength of Graphite/ Epoxy Composite Laminates Subjected to Normal Impact," Journal of the Japan Society for Aeronautical & Space Sciences, Vol. 37, No. 25, pp. 29∼36.
16. Tsai S. W. and Hahn H. T., 1980, Introduction to Composite Materials, Technomic Publishing Cc., Inc., pp. 329∼376.
17. Whitney J. M., Daniel I. M. and Pipes R. B., 1984, Experimental Mechanics of Fiber Reinforced Composite Materials, Prentice-Hall, Inc., pp. 250∼255.
18. Yang I. Y., Matsumoto H., Adachi T., 1994, "Impact Damages of CFRP Laminates Subjected to High Temperature Atmosphere," JSME (A), Vol. 60, No. 571, pp. 841∼845.