Damage Evolution and Stress Analysis in Zirconia Thermal Barrier Coatings during Cyclic and Isothermal Oxidation

Journal of the American Ceramic Society

Volumn 84, Issue 10, 2001, Pages 2385-2393

  Singh, Jitendra P ^a   Nair, Balakrishnan G ^a   Renusch, Daniel P ^a   Sutaria, Manish P ^a   Grimsditch, Marcus H ^a  

^a ARGONNE NATIONAL LABORATORY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ELASTIC MODULI; FAILURE (MECHANICAL); HARDNESS; MICROSCOPIC EXAMINATION; MICROSTRUCTURE; NUCLEATION; OXIDATION; SPECTROSCOPY; STRESS ANALYSIS; STRESS CONCENTRATION; THERMAL CYCLING; ZIRCONIA;

DAMAGE EVOLUTION; HYDROSTATIC STRESSES; ISOTHERMAL OXIDATION; PROTRUSIONS;

THERMAL BARRIER COATINGS;

EID: 0035497687     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2001.tb01019.x     Document Type: Article

References (37)

1. S. M. Gupta and D. K. Gupta, "The Evolution of Thermal Barrier Coatings in Gas Turbine Applications," J. Eng. Gas Turb. Power, 111, 301-305 (1989).
2. J. T. DeMasi-Marcin, K. D. Sheffler, and S. Bose, "Mechanisms of Degradation and Failure in a Plasma-Deposited Thermal Barrier Coating," J. Eng. Gas Turb. Power, 112, 521-26 (1990).
3. R. D. Maier, C. M. Scheuermann, and C. W. Andrews, "Degradation of a Two-Layer Thermal Barrier Coating under Thermal Cycling," Am. Ceram. Soc. Bull., 60 [5] 555-60 (1981).
4. T. E. Strangman, E. D. Felton, and N. E. Ulion, "High-Temperature Oxidation Resistant Coatings for the Directionally Solidified Ni-Nb-Cr-Al Eutectic Superalloy," Am. Ceram. Soc. Bull., 56 [8] 700-705 (1977).
5. 3/Ni-22Cr-10A1-1Y Thermal Barrier Coatings," J. Am. Ceram. Soc., 72 [2] 212-18 (1989).
6. D. Zhu and R. A. Miller, "Investigation of Thermal High Cycle and Low Cycle Fatigue Mechanisms of Thick Thermal Barrier Coatings," Mater. Sci. Eng., A, A245. 212-23 (1998).
7. J. P. Singh, M. Sutaria, and A. Chopra, "Thermomechanical Behavior of Plasma-Sprayed Zirconia Thermal Barrier Coatings," Ceram. Eng. Sci. Proc., 19 [4] 313-22 (1998).
8. T. M. Yonushonis, "Overview of Thermal Barrier Comings in Diesel Engines," J. Therm. Spray Technol., 6 [1] 50-56 (1997).
9. R. L. Jones, "Some Aspects of Hot Corrosion of Thermal Barrier Coatings," J. Therm. Spray Technol., 6 [1] 77-84 (1997).
10. Z. Mutasim and W. Brentnall, "Thermal Barrier Coatings for Industrial Gas Turbine Applications: An Industrial Note," J. Therm. Spray Technol., 6 [1] 105-108 (1997).
11. G. C. Chang, W. Phucharoen, and R. A. Miller, "Behavior of Thermal Barrier Coatings for Advanced Gas Turbine Blades," Surf. Coat. Technol., 30, 13-28 (1987).
12. G. J. Petrus and B. L. Ferguson, "A Software Tool to Design Thermal Barrier Coatings," J. Therm. Spray Technol., 6 [1] 29-34 (1997).
13. A. M. Freborg, B. L. Ferguson, W. J. Brindley, and G. J. Petrus, "Modeling Oxidation-Induced Stresses in Thermal Barrier Coatings," Mater. Sci. Eng., A, A245, 182-90 (1998).
14. C.-H. Hsueh, J. A. Haynes, M. J. Lance, P. F. Becher, M. K. Ferber, E. R. Fuller Jr., S. A. Langer, W. C. Carter, and W. R. Cannon, "Effects of Interface Roughness on Residual Stresses in Thermal Barrier Coatings," J. Am. Ceram. Soc., 82 [4] 1073-75 (1999).
15. B. G. Nair, J. P. Singh, and M Grimsditch, "A Model for Residual Stress Evolution in Air-Plasma-Sprayed Thermal Barrier Coatings," Ceram Eng. Sci. Proc., 21 [3] 133-42 (2000).
16. D. M. Nissley, "Thermal Barrier Coating Life Modeling in Aircraft Gas Turbine Engines," J. Therm. Spray Technol., 6 [1] 91-98 (1997).
17. 3," J. Appl. Phys., 49 [2] 580-83 (1978).
18. Q. Ma and D. R. Clarke, "Stress Measurement in Single-Crystal and Polycrystalline Ceramics Using Their Optical Fluorescence," J. Am. Ceram. Soc., 76 [6] 1433-40 (1993).
19. D. M. Lipkin and D. R. Clarke, "Measurement of the Stress in Oxide Scales Formed by Oxidation of Alumina-Forming Alloys," Oxid. Met., 45 [3/4] 267-80 (1996).
20. D. M. Renusch, M. Grimsditch, I. Koshelev, B. V. Veal, and P. Y. Hou, "Strain Determination in Thermally Grown Alumina Scales Using Fluorescence Spectroscopy," Oxid. Met., 48 [5/6] 471-95 (1997).
21. R. J. Christensen, D. M. Lipkin, and D. R. Clarke, "Nondestructive Evaluation of the Oxidation Stresses through Thermal Barrier Coatings Using Cr34 Piezospectroscopy," J. Appl. Phys. Lett., 69 [24] 3754-56 (1996).
22. M. J. Lance, J. A. Haynes, W. R. Cannon, and M. K. Ferber, "Piezospectroscopic Characterization of Thermal Barrier Coatings"; pp. 229-37 in Ceramic Transactions, Vol. 89, Nondestructive Evaluation of Ceramics, Edited by C. H. Schilling and J. N. Gray, American Ceramic Society, Westerville, OH, 1998.
23. J. P. Singh, B. Nair, D. Renusch, M. Sutaria, and M. Grimsditch, "Damage Evolution and Residual Stresses in Plasma-Sprayed Zirconia Thermal Barrier Coatings," Ceram. Eng. Sci. Proc., 20 [3] 487-92 (1999).
24. D. R. Clarke, R. J. Christensen, and V. Tolpygo, "The Evolution of Oxidation Stresses in Zirconia Thermal Barrier Coated Superalloy leading to Oxidation Failure," Surf. Coat. Technol., 94-95, 89-93 (1997).
25. D. B. Marshall, T. Noma, and A. G. Evans, "A Simple Measurement for Determining Elastic-Modulus-to-Hardness Ratios Using Knoop Indentation Measurements," J. Am. Ceram. Soc., 65 [10] C-175-C-176 (1982).
26. J. P. Singh, M. Sutaria, and M. Ferber, "Use of Indentation Technique to Measure Elastic Modulus of Plasma-Sprayed Zirconia Thermal Barrier Coating," Ceram. Eng. Sci. Proc., 18 [4] 191-200 (1997).
27. J. K. Wright, R. L. Williamson, D. Renusch, B. Veal, M. Grimsditch, P. Y. Hou, and R. M. Cannon, "Residual Stresses in Convoluted Oxide Scales," Mater. Sci. Eng., A. A262, 246-55 (1999).
28. R. A. Miller and C. E. Lowell, "Failure Mechanisms of Thermal Barrier Coatings Exposed to Elevated Temperatures," Thin Solid Films, 95, 265-73 (1982).
29. M. Gell, K. Vaidyanathan, B. Barber, J. Cheng, and E. Jordan, "Mechanism of Spollation in Platinum Aluminide/Electron Beam Physical Vapor-Deposited Thermal Barrier Coatings," Metall. Mater. Trans. A, 30A, 427-35 (1999).
30. A. G. Evans, G. B. Crumley, and R. E. Demaray, "On the Mechanical Behavior of Brittle Coatings and Layers," Oxid. Met., 20 [5/6] 193-216 (1983).
31. B. G. Nair, J. P. Singh, and M. Grimsditch, "Analytical Modeling of Residual Stress Evolution in Air-Plasma-Sprayed Thermal Barrier Coatings," Ceram. Eng. Sci. Proc., 22 [4] 417-26 (2001).
32. E. A. G. Shillington and D. R. Clarke, "Spalling Failure of a Thermal Barrier Coating Associated with Aluminum Depiction in the Bond-Coat," Acta Mater., 47 [4] 1297-305 (1999).
33. 3 Scales on Fe-Al and Ni-Al Alloys at 1100°C," Solid State Ionics, 53-56, 229-37 (1992).
34. D. W. Jordan and K. T. Faber, "X-ray Residual Stress Analysis of a Ceramic Thermal Barrier Coating Undergoing Thermal Cycling, Thin Solid Films, 235, 137-41 (1993)
35. A. M. Freborg; private communication, 1999.
36. M. Y. He, A. G. Evans, and J. W. Hutchinson, "Effects of Morphology on Decohesion of Compressed Thin Films," Mater. Sci. Eng., A, A235, 168-81 (1998).
37. S. Uran, B. W. Veal, M. Grimsditch, J. Pearson, and A. Berger, "Effect of Surface Roughness on Oxidation: Changes in Scale Thickness, Composition, and Residual Stress," Oxid. Met., 54 [1/2] 73-85 (2000).