A finite-element model of mixed-mode delamination in laminated composites with an R-curve effect

Composites Science and Technology

Volumn 61, Issue 10, 2001, Pages 1413-1427

  Yan, Ai Min ^a   Marechal, E ^b   Nguyen Dang, H ^a  

^a UNIVERSITY OF LIÈGE   (Belgium)

^b SAMTECH   (Belgium)

Author keywords

B. Interface; B. Modelling; C. Computational simulation; C. Delamination; C. Fibre bridging

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FINITE ELEMENT METHOD; FRACTURE MECHANICS; MONOLAYERS; PLASTIC DEFORMATION; STRESS ANALYSIS;

CRACK INTERFACES;

LAMINATED COMPOSITES;

COMPOSITE PROPERTY; COMPUTER SIMULATION; DELAMINATION; FIBER REINFORCED COMPOSITE; FIBER-MATRIX INTERFACE; MATHEMATICAL MODEL;

EID: 0035422587     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0266-3538(01)00041-0     Document Type: Article

References (31)

1. Stress analysis of the double cantilever beam specimen
2. Failure analysis of composite laminates with free edge
3. Interface failure at ply drops in CFRP/sandwich panels
4. Imperfect interlaminar interfaces in laminated composites: Interlaminar stresses and strain-energy release rates
5. Delamination fracture of multidirectional carbon-fiber/epoxy composites under mode I, mode II and mixed-mode I/II loading
6. The mixed-mode delamination of fibre composite materials
7. Characterization of mode II delamination growth in glass/epoxy composite cylinders
8. Characterization of mode I delamination growth in glass/epoxy composite cylinders
9. Characterization of mixed mode delamination growth in glass/epoxy composite cylinders
10. A damage prediction method for composite structures
11. Damage analysis of inter-laminar fracture specimens
12. Identification and forecast of delamination in composite laminates by an interlaminar interface model
13. Damage analysis by damage mechanics: Some applications
14. A damage analysis tool for laminate delamination
15. Mechanics and mechanisms of delamination in a poly (ether sulphone)-fibre composite
16. The effects of geometry, rate and temperature on the mode I, mode II and mixed mode I/II interlaminar fracture of carbon-fibre/poly (ether-ether ketone) composites
17. Mode I interlaminar fracture of symmetrical cross-ply composites
18. A modified DCB specimen for mode I testing of multidirectional laminates
19. Mixed-mode bending method for delamination testing
20. Multiple-cracked fatigue crack growth by BEM
21. On the numerical integration of interface elements
22. Imperfect interlaminar interfaces in laminated composites: Bending buckling and transient responses
23. A combined stress-based and fracture-mechanics-based model for predicting delamination in composites
24. Delamination R-curve phenomena due to damage
25. Delamìnation and fiber bridging modelling in composite samples
26. Modelling R-curve effects in delamination damage mechanisms
27. Mixed-mode delamination in laminated composites with R-curve effect
28. Fracture mechanics of delamination tests
29. Delamination fracture criteria for composite laminates
30. Corrections for mode II fracture toughness specimens of composites materials