Characterization of mode I delamination growth in glass/epoxy composite cylinders

Journal of Composite Materials

Volumn 34, Issue 5, 2000, Pages 398-419

  Ozdil, F ^a   Carlsson, L A ^a  

^a Florida Atlantic Univ   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COMPOSITE STRUCTURES; CRACK PROPAGATION; DELAMINATION; ELASTICITY; EPOXY RESINS; FRACTURE TOUGHNESS; GLASS; INTERFACES (MATERIALS); MATHEMATICAL MODELS; PLASTIC FILAMENTS;

BEAM SPECIMENS; BEAM THICKNESSES; CRACK LENGTHS; DELAMINATION GROWTH; ELASTIC FOUNDATION EFFECTS; GLASS EPOXY COMPOSITE CYLINDERS; PLY ANGLES;

LAMINATED COMPOSITES;

EID: 0033889398     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1106/TP78-3H2H-8NV2-1F9H     Document Type: Article

References (33)

1. Rajapakse, Y.D.S. (editor), "Mechanics of Thick Composites," AMD-Vol. 162, ASME, New York, 1993.
2. Girala, H.J. and Chaduri, R.A., "Structural Evaluation of Advanced Composite Thick-Section Cylinders Under Biaxial Compressive Loading," AMD-Vol. 162, Mechanics of Thick Composites, (Y.D.S. Rajapakse ed.), ASME, New York, 1993, p. 227.
3. Slaughter, W.S. and Fleck, N.A., "Micro-buckling of Fiber Composites," in AMD-Vol. 162, Mechanics of Thick Composites (Y.D.S. Rajapakse ed.), ASME, New York, 1993, p. 67.
4. Kardomateas, G.A. and Chung, C.B., "A Thin Film Modeling of Delamination Buckling in Pressure Loaded Laminated Composite Shells," AIAA J., Vol. 30, 1992, p. 2119.
5. Wang, S.S. and Choi, I., "The Interface Crack Between Dissimilar Anisotropic Composite Materials," J. Appl. Mech., Vol. 50, 1983, p. 169.
6. Ting, T.C.T., "Explicit Solutions and Invariance of the Singularities at an Interface Crack in Anisotropic Composites," Int. J. Solids Struct., Vol. 22, 1986, p. 965.
7. Raju, I.S., Crews Jr., J.H. and Aminpour, M.A., "Convergence of Strain Energy Release Rate Components for Edge-Delaminated Composite Laminates," Eng. Fracture Mech., Vol. 30, 1988, p. 383.
8. Suo, Z., "Singularities, Interfaces and Cracks in Dissimilar Anisotropic Media," Proc. Roy. Soc. Lond., Vol. A 427, 1990, p. 331.
9. Davidson, B.D. and Schapery, R.A., "Effect of Finite Width on Deflection and Release Rate of an Orthotropic Double Cantilever Beam Specimen," J. Compos. Mater., Vol. 22, 1988, p. 641.
10. Sun, C.T. and Zeng, S., "Delamination Characteristics of Double-Cantilever Beam and End-Notched Flexure Composite Specimens," Compos. Sci. Tech., Vol. 56, 1996, p. 451.
11. Hutchinson, J.W. and Suo, Z., "Mixed Mode Cracking in Layered Materials," Advances in Applied Mechanics, Vol. 29, 1992, p. 63.
12. Sundararaman, S. and Davidson, B.D., "New Test Methods for Determining Fracture Toughness as a Function of Mode Mix for Bimaterial Interfaces," Application of Fracture Mechanics in Electronic Packaging and Materials, ASME, EEP-Vol. 1/MD-Vol. 64, 1995, p. 141.
13. Ozdil, F. and Carlsson, L.A., "Beam Analysis of Angle-Ply Laminate DCB Specimens," Compos. Sci. & Tech., Vol. 59, 1999, p. 305.
14. Ewalds, H.L. and Wanhill, R.J.H., "Fracture Mechanics," Edward Arnold, London, 1989.
15. Whitney, J.M., "Structural Analysis of Laminated Anisotropic Plates," Technomic, Lancaster, 1987.
16. Jones, R.M., "Mechanics of Composite Materials," McGraw-Hill, New York, 1975.
17. Ozdil, F., Carlsson, L.A. and Li, X., "Characterization of Mode II Delamination Growth in Glass/Epoxy Composite Cylinders," to appear in J. Compos. Mater., 1999.
18. Wilkins, D.J., Eisenmann, J.R., Camin, R.A., Margolis, W.S. and Benson, R.A., "Characterizing Delamination Growth in Graphite-Epoxy," ASTM STP 775, 1982, p. 168.
19. Kanninen, M.F., "An Augmented Double Cantilever Beam Model for Studying Crack Propagation and Arrest," Int. J. Fracture, Vol. 9, No. 1, 1973, p. 83.
20. Kanninen, M.F., "A Dynamic Analysis of Unstable Crack Propagation and Arrest in the DCB Test Specimen," Int. J. Fracture, Vol. 10, No. 3, 1974, p. 415.
21. Hyer, M.W. and Knott, T.W., "Analysis of End-Fitting Induced Strains in Axially Loaded Glass-Epoxy Cylinders," in Composite Structs for SMES Plants (NISTIR5024), (R.P. Reed and J.D. McCloskey eds.), Oct. 1994.
22. Timoshenko, S.P., "Strength of Materials," Part 1, Kreiger, Melbourne, 1984.
23. Davidson, B.D., Krüger, R. and König, M., "Effects of Stacking Sequence on Energy Release Rate Distributions in Multi-Directional DCB and ENF Specimens," Eng. Fracture Mech., Vol. 55, 1996, p. 557.
24. Davies, P. and Rannou, F., "The Effects of Defects in Tubes: Part 1. Mode I Delamination Resistance," Applied Compos. Mater., Vol. 1, 1995, p. 333.
25. Chai, H., "The Characterization of Mode I Delamination Failure in Non-Woven Multidirectional Laminates," Composites, Vol. 15, 1984, p. 277.
26. Laksimi, A., Benzeggagh, M.L., Jing, G., Hecini, M. and Roelant, J.M., "Mode I Interlaminar Fracture of Symmetrical Cross-Ply Composites," Compos. Sci. & Tech., Vol. 41, 1991, p. 147.
27. Robinson, P. and Song, D.Q., "A Modified DCB Specimen for Mode I Testing of Multidirectional Laminates," J. Compos. Mater., Vol. 26, 1992, p. 1554.
28. Ic of a Unidirectional Glass/Epoxy Composite," Compos. Sci. & Tech., Vol. 35, 1989, p. 283.
29. Togho, K. et al., "Mode I Interlaminar Fracture Toughness and Fracture Mechanism of Angle-Ply Carbon/Nylon Laminates," J. Compos. Mater., Vol. 30, 1996, p. 650.
30. Ic in Angle-Ply Composites Using a Cantilever Beam Test Method," J. Reinf. Plast. & Compos., Vol. 2, 1983, p. 2.
31. Chou, I., Kimpara, I. and Kageyama, K., "Mode I and Mode II Fracture Toughness of Differently Oriented Interlaminar of Graphite/Epoxy Composites," 5th ASTM Symposium on Compos. Mater., Atlanta, 1993.
32. Suo, Z., Bao, G. and Fan, B. "Delamination R-Curve Phenomena Due to Damage," J. Mech. Phys. Solids, Vol. 40, 1992, p. 1.
33. Spearing, S.M. and Evans, A.G., "The Role of Fiber Bridging in the Delamination Resistance of Fiber-reinforced Composites," Acta Metall. Mater., Vol. 40, 1992, p. 2191.