Creep of uncoated and Cu-Cr coated NARloy-Z

Materials Science and Engineering: A

Volumn 263, Issue 1, 1999, Pages 8-14

  Walter, R J ^a   Chiang, K T ^a  

^a BOEING COMPANY   (United States)

Author keywords

Copper alloy; Creep; Cu Cr coating; NARloy Z; Oxidation

Indexed keywords

BRITTLENESS; CHROMATE COATINGS; CRACK PROPAGATION; CREEP TESTING; GAS ABSORPTION; GRAIN BOUNDARIES; HIGH TEMPERATURE EFFECTS; OXIDATION; PRECIPITATION (CHEMICAL); STRESS ANALYSIS;

STRESS ACCELERATED GRAIN BOUNDARY OXIDATION; STRESS RUPTURE CREEP TESTING;

COPPER ALLOYS;

COATING; CORROSION; CREEP; OXIDATION;

EID: 0033617095     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0921-5093(98)01080-6     Document Type: Article

References (14)

1. H. Leidheiser, Jr., The Corrosion of Copper, Tin and Their Alloys, Krieger Publishing Company, Melbourne, FL, 1979.
2. Chiang K.T., Ampaya J.P. Oxidation kinetics of Cu-30vol.%Cr coating. Surf. Coatings Technol. 78:1996;243-247.
3. Appleby W.K., Tylecote R.F. Stresses during the gaseous oxidation of metals. Corrosion Sci. 10:1970;325-341.
4. W. Carpenter, B.S. Kang, K.M. Chang, SAGBO mechanism on high temperature cracking behavior of Ni-base superalloys, in: Superalloys 718, 625, 706 and Various Derivatives, Proceedings of the Fourth International Symposium, Pittsburgh, PA, 1997, pp. 679-688.
5. B.S. Kang, G. Zhang, P. Liu, M. Ellathur, Fatigue and fracture at elevated temperatures, in: Proceedings of the Symposium, 1995 ASME International Mechanical Engineering Congress and Exposition, San Francisco, CA, 12-17 November 1995, ASME, pp. 225-254.
6. Hayes R.W., Smith D.F., Wanner E.A., Earthman J.C. Effect of environment on the rupture behavior of alloys 909 and 718. Mater. Sci. Eng. A177:1994;43-53.
7. Higo Y., Pickard A.C., Knott J.F. Effects of grain size and stacking fault energy on fatigue-crack-propagation thresholds in Cu-Al aluminum alloys. Met. Sci. 15:1981;233-240.
8. Marchand N.J., Bailon L.P., Dickson D.I. Near-threshold fatigue crack growth in copper and alpha-brass: gain-size and environmental effects. Metall. Trans. A. 19A(October):1988;2575-2587.
9. Tien J.K., Thompson A.W., Bernstein I.M., Richards R.J. Hydrogen transport by dislocations. Metall. Trans. A. 35(7):1976;821-829.
10. Tromans D., Sun R.-H. Intergranular/transgranular fatigue of copper: influence of environment on crack path and propagation rates. Mater. Sci. Eng. A219:1996;56-65.
11. Nieh T.G., Nix W.D. Embrittlement of copper due to segregation of oxygen to grain boundaries. Metall. Trans. A. 12A(May):1981;893-901.
12. V. Sklenicka, Intergranular surface cracking in high temperature creep, in: Conference Proceedings - Corrosion, Les editions de Physeque, B.P. 112, F-91944 Les Ulis Cedex A, France, October 1992.
13. Biner S.B., Spitzig W.A. Creep characteristics of wire-drawn Cu-20%Nb. Mater. Sci. Eng. A150:1992;213-220.
14. K.T. Chiang, G.H. Meier, F.S. Pettit, Oxidation behavior of copper-chromium composites, in: S.B. Newcomb, J.A. Little (Eds.), Microscopy of Oxidation - 3, Institute of Materials, London, 1997, pp. 453-461.