Stress corrosion life assessment of Alloy 600 PWR components

Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 243-250

  Amzallag, Claude ^a   Le Hong, Son ^a   Pagès, Claude ^a   Gelpi, Angel ^b  

^a EDF R AND D   (France)

^b AREVA NP   (France)

Author keywords

[No Author keywords available]

Indexed keywords

CARBIDES; CRACK INITIATION; CRACK PROPAGATION; MICROSTRUCTURE; PRECIPITATION (CHEMICAL); RELIABILITY; STRESS CORROSION CRACKING; SUPERALLOYS;

FLAW EVALUATION; MECHANICAL LOADING; REACTOR VESSEL HEAD; STRESS CORROSION LIFE ASSESSMENT;

PRESSURIZED WATER REACTORS;

EID: 0033489282     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch25     Document Type: Conference Paper

References (18)

1. - R. BOUDOT, P. VIDAL, A. GELPI "A method for the evaluation of the nickel based alloys susceptibility to PWSCC" Proceedings of 1992 EPRI Workshop on PWSCC of Alloy 600 in PWRs
2. - B. FLESCH et al. "Contraintes en service et sur-contraintes de denting dans les zones de transition des générateurs de vapeur dans les réacteurs 900 MWe et 1300 MWe" Conference Fontevraud II, 1990, France
3. - C. PICHON et al. "Residual life assessment of French PWR vessel head penetrations through metallurgical analysis" The 1994 ASME Pressure Vessels & Piping Conference, June 19-23, 1994 / Minneapolis, Minnesota USA
4. - C. BENHAMOU et al. "Susceptibility to stress corrosion cracking of alloy 600 material for vessel head penetrations" Conference Fontevraud III, 1995
5. - C. BENHAMOU, C. Amzallag Influence of manufacturing parameters on stress corrosion cracking of alloy 600 used in nuclear power plants Eurrocorr'99 Conference, 1999
6. - A.R. MC ILREE, T. OLBERG, J. NESTELL "Primary side stress corrosion cracking" Steam Generator Reference Book, EPRI-SGOG, 1985
7. - A.A. STEIN, A.R. MC ILREE "Relationship of annealing temperature and microstructure to primary side cracking of Alloy 600 steam generator tubing and the prediction of stress corrosion cracking in primary water" Second Int. Symposium on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, Monterey, 1985
8. - R. BRANDY, D. VAN ROOYEN "Mechanisms of stress corrosion cracking and intergranular attack in Alloy 600 in high temperature caustic and pure water" J. Materials for Energy System 7, no 3, 237, 1985
9. - D. VAN ROOYEN Update on SCC of Alloy 600 in high temperature water-Workshop of PWR SGtubing, San Diego, 1985
10. - H. ITOH et al. "Effect of pipe making process on SCC resistance of Alloy 600" PWSCC Workshop EPRI, Tampa, 1994
11. - J.M. BOURSIER "Fissuration par corrosion sous contrainte des alliages Fer-Nickel-Chrome en milieu primaire des réacteurs á eau sous pression" Ph. D. Thesis, Bordeaux University, 1993
12. - P. BERGE, D. BUISINE, A. GELPI "Surface preparation and stress corrosion cracking models" 13th International Corrosion Congress. Melburne. Australia Nov. 25-29, 1996
13. - S. LE HONG, C. AMZALLAG, A. GELPI "Model of the stress corrosion cracking initiation on alloy 600 in primary water of PWR" 9th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, August 1999
14. - C. FAIDY et al. "Life evaluation of CRDM nozzles through mechanical analysis" ASME PVP Conference, Minneapolis, June 1994
15. - C. FAIDY et al. "Comportement mécanique des adaptateurs de cuve" Conference Fontevraud III, 1994, France
16. - S. LE HONG et al. "Les contraintes résiduelles de fabrication sur les traversées de couvercle de cuve de réacteur á eau pressurisée" Journées AFIAP, 1995, France
17. - C. AMZALLAG, F. VAILLANT, A. TEISSIER "Derivation of stress corrosion crack growth laws for alloy 600 PWR components" ICONE 5 - 5th International Conference on Nuclear Engineering, May 1997
18. - C. AMZALLAG, F. VAILLANT "Stress corrosion crack propagation rates in reactor vessel head penetrations in alloy 600" 9th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, August 1999