Modelling of stress corrosion crack initiation on alloy 600 in primary water of PWRs

Author keywords

[No Author keywords available]

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; MATHEMATICAL MODELS; PRESSURIZED WATER REACTORS; RESIDUAL STRESSES; STRESS CORROSION CRACKING; STRESS INTENSITY FACTORS;

EID: 0033489231     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch11     Document Type: Conference Paper
Times cited : (25)

References (12)
  • 2
    • 0012911520 scopus 로고    scopus 로고
    • Commissariat à l'Energie Atomique internal report
    • G. SANTARINI, Commissariat à l'Energie Atomique internal report, (1998).
    • (1998)
    • Santarini, G.1
  • 3
    • 0342848812 scopus 로고
    • Comprehensive interpretation of constant extension rate test: A method for the characterization and the prediction of intergranular stress corrosion cracking
    • Brighton, UK, October 3-5
    • G. SANTARINI, Comprehensive interpretation of constant extension rate test: a method for the characterization and the prediction of intergranular stress corrosion cracking, Eurocorr'88, Brighton, UK, October 3-5 (1988).
    • (1988) Eurocorr'88
    • Santarini, G.1
  • 5
    • 0003702224 scopus 로고
    • Fissuration par corrosion sous contrainte des alliages Fer-Nickel-Chrome en milieu primaire des réacteurs à eau pressurisée
    • Ph.D. Thesis, University of Bordeaux I, January 14
    • J.M. Boursier, Fissuration par corrosion sous contrainte des alliages Fer-Nickel-Chrome en milieu primaire des réacteurs à eau pressurisée, Ph.D. Thesis, University of Bordeaux I, January 14 (1993).
    • (1993)
    • Boursier, J.M.1
  • 6
    • 0012966383 scopus 로고
    • Influence of the surface conditions on the sensitivity of alloy 600 tubes to stress corrosion cracking in water
    • Espoo, June 14
    • P. Todeschini et al., Influence of the surface conditions on the sensitivity of Alloy 600 tubes to stress corrosion cracking in water, Eurocorr'92, Espoo, June 14 (1992).
    • (1992) Eurocorr'92
    • Todeschini, P.1
  • 7
    • 0029256928 scopus 로고
    • The influence of the strain rate on the stress corrosion cracking of alloy 600 in high temperature primary water
    • J.M. Boursier, D. Desjardins, F. Vaillant, The influence of the strain rate on the stress corrosion cracking of Alloy 600 in high temperature primary water, Corrosion Science, Vol. 37, no. 3, pp. 493-508, (1995).
    • (1995) Corrosion Science , vol.37 , Issue.3 , pp. 493-508
    • Boursier, J.M.1    Desjardins, D.2    Vaillant, F.3
  • 8
    • 0003696595 scopus 로고    scopus 로고
    • Influence de la teneur en chrome et de la structure des alliages de nickel sur leur comportement en corrosion sous contrainte en milieu primaire des réacteurs à eau pressurisée
    • Ph.D. Thesis, University of Grenoble, October 29th
    • J.D. Mithieux, Influence de la teneur en chrome et de la structure des alliages de nickel sur leur comportement en corrosion sous contrainte en milieu primaire des réacteurs à eau pressurisée, Ph.D. Thesis, University of Grenoble, October 29th (1997).
    • (1997)
    • Mithieux, J.D.1
  • 10
    • 0021544490 scopus 로고
    • The estimation of crack tip strain rate parameters characterising environment assisted crack growth data
    • (R.P. Gangloff)
    • D.P.G. Lidbury, The estimation of crack tip strain rate parameters characterising environment assisted crack growth data, The Embrittlement by the Localised Crack Environment (R.P. Gangloff, p 149), (1983).
    • (1983) The Embrittlement by the Localised Crack Environment , pp. 149
    • Lidbury, D.P.G.1
  • 11
    • 0021548432 scopus 로고
    • Stress corrosion cracking of reactor pressure vessel steel in high temperature water
    • T. Shoji, J. Congleton, R.N. Parkins, Stress corrosion cracking of reactor pressure vessel steel in high temperature water, Corrosion Science, 25, n° 8/9, p 633, (1985).
    • (1985) Corrosion Science , vol.25 , Issue.8-9 , pp. 633
    • Shoji, T.1    Congleton, J.2    Parkins, R.N.3
  • 12
    • 4243206138 scopus 로고    scopus 로고
    • Mécanismes de la corrosion sous contrainte de l'alliage 600 monocristallin et polycristallin en milieu primaire : Rôle de l'hydrogène
    • Ph.D. Thesis, Ecole des Mines de Saint Etienne, January 8th
    • F. Foct, Mécanismes de la corrosion sous contrainte de l'alliage 600 monocristallin et polycristallin en milieu primaire : Rôle de l'hydrogène, Ph.D. Thesis, Ecole des Mines de Saint Etienne, January 8th (1999).
    • (1999)
    • Foct, F.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.