Stress corrosion cracking of reactor pressure vessel steels under boiling water reactor conditions

Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 901-910

  Heldt, J ^a   Seifert, H P ^a  

^a PAUL SCHERRER INSTITUTE   (Switzerland)

Author keywords

[No Author keywords available]

Indexed keywords

BOILING WATER REACTORS; CRACK INITIATION; CRACK PROPAGATION; CREEP; ELECTRIC CONDUCTIVITY; FRACTURE MECHANICS; PLASTICITY; PRESSURE VESSELS; STRESS CORROSION CRACKING;

CRACK GROWTH RATE; LOW ALLOY STEEL; SMALL SCALE YIELDING; STATIC LOADING;

STEEL;

EID: 0033489073     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch95     Document Type: Conference Paper

References (15)

1. P.M. Scott, D.R. Tice, "Stress Corrosion in Low Alloy Steels", Nuclear Engineering & Design, 119 (1990), 399-413.
2. J. Hickling, D. Blind, "Strain-Induced Corrosion Cracking of Low Alloy Steel in LWR Systems - Case Histories and Identification of Conditions Leading to Susceptibility", Nuclear Engineering & Design, 91 (1986), 305-330.
3. H.P. Seifert, J. Heldt, B. Tirboned, "Stress Corrosion Cracking of Low Alloy Reactor Pressure Steels under Boiling Water Reactor Conditions", (PSI report, Paul Scherrer Institute, Switzerland, 1999).
4. J. Hickling, "Evaluation of Acceptance Criteria for Data of Environmentally-Assisted Cracking in Light Water Reactors", (SKI Report 94:14, Statens Kärnkraftinspektion, 1994).
5. F.P. Ford, P.L. Andresen, "Stress Corrosion Cracking of Low Alloy Steels in 288 °C Water", (Paper presented at NACE Corrosion 89, New Orleans, LA, USA, 1989), paper 498.
6. A. Kraus, "Stress Corrosion Cracking of Pressure Vessel Steels in High Temperature Water" (Ph.D. thesis, ETH Zürich, 1994), 44-55.
7. P.L. Andersen, "Effects of Testing Characteristics on Observed SCC Behavior in BWRs", (Paper presented at Corrosion NACE 98, San Diego, CA, USA, 1998), paper 137.
8. T. Shoji, "The Critical Cracking Potential of Reactor Pressure Vessel Steel in Pressurized High Temperature Water", (3th Int. Atomic Energy Agency Specialists Meeting on Subcritical Growth, Moscow, USSR, 1990), 109.
9. H.P. Seifert, J. Heldt, U. Ineichen "Stress Corrosion Cracking of Low Alloy Reactor Pressure Vessel Steel in Oxygenated High Temperature Water", (PSI annual report 1997 - Annex IV), 93-100.
10. R.M. Magdowski, A. Kraus, M.O. Speidel, "Stress Corrosion Cracking of Reactor Pressure Vessel Steel in 288°C Water: The Effect of Oxygen, Electrochemical Potential, and Steel Composition", (paper presented at Corrosion NACE 94, 1994), paper 133.
11. A. Oehlert, A. Atrens "Primary Creep and Stress Corrosion Cracking", Fundamental Aspects of Stress Corrosion Cracking, ed. S.M. Bruemmer et al., TMS, (1992), 255-275.
12. B. Iskluth "Beitrag zur Spannungsrißkorrosion am Beispiel eines niedriglegierten warmfesten Feinkornbaustahles in sauerstoffhaltigem Hochtemperaturwasser", (Ph.D thesis, MPA Staatliche Materialprüfungsanstalt Universität Stuttgart, 1989), 128-141.
13. E. Lenz, N. Wieling "Strain-Induced Corrosion Cracking of Low Alloy Steels in LWR-Systems - Interpretation of Susceptibility by Means of a Three Dimensional (T, ε, Dissolved Oxygen) Diagram", Nuclear Engineering & Design, 9 (1986), 305-330.
14. H. Friedrich et al. "Stress Corrosion Cracking of Low Alloy Steels under High Pressure and High Temperature Conditions" (Paper presented Corrosion NACE 96, 1996, Baltimore, MD, USA), paper 98.
15. V. Läpple "Untersuchungen zum korrosionsgestützten Rißwachstum ferritischer Stähle in sauerstoffhaltigem Hochtemperaturwasser" (Technisch-wissenschaftlicher Bericht der MPA Stuttgart 96/02, 1996).