Stress corrosion cracking of low alloy steels under high pressure and high temperature conditions

NACE - International Corrosion Conference Series

Volumn 1996-March, Issue , 1996, Pages

  Friedrich, H ^a   Frank, J ^a   Gladen, H ^a,b   Stratmann, M ^a  

^a UNIVERSITY OF ERLANGEN NUREMBERG   (Germany)

^b TE C Technologiepark Center   (Germany)

Author keywords

High pressure; High temperature; Low alloy steels; Low cycle fatigue; Strain induced corrosion cracking; Stress corrosion cracking; Water

Indexed keywords

ALLOY STEEL; BIOCHEMICAL OXYGEN DEMAND; BRITTLE FRACTURE; CORROSION FATIGUE; CORROSIVE EFFECTS; CRACK PROPAGATION; CRACKS; DISSOLVED OXYGEN; HIGH STRENGTH STEEL; HIGH TEMPERATURE CORROSION; LIME; MANGANESE ALLOYS; PLASTIC DEFORMATION; RESIDUAL STRESSES; SCANNING ELECTRON MICROSCOPY; STEEL CORROSION; STEEL METALLURGY; STRAIN RATE; SULFUR COMPOUNDS; TENSILE STRENGTH; TENSILE TESTING; TERNARY ALLOYS; WATER;

CRACK PROPAGATION RATE; HIGH PRESSURE; HIGH PRESSURE AND HIGH TEMPERATURE CONDITIONS; HIGH PRESSURE HIGH TEMPERATURE; HIGH TEMPERATURE; LOW CYCLE FATIGUES; STRAIN INDUCED; STRESS CORROSION BEHAVIOR;

STRESS CORROSION CRACKING;

EID: 0012955611     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (35)

1. P.H. Effcriz, P. Forchhammer, VGB Kraftwerkstech. 62 (1982) p.633.
2. F.P. Ford, "Modelling of environmentally-assisted cracking of structural steels in water", 17. Mctalltagung: Umgebungsabhängiges Bruchverhaltcn, Dresden, 1990, p.71.
3. J. Hickling, D. Blind, Nucl.Eng.Dcs. 91 (1986) p.305.
4. P.M. Scott, Corros.Sci. 25 (1985) p.583.
5. J. Conglcton, T. Shoji, R.N. Parkins, Corros.Sci. 25 (1985) p.633.
6. K. Rippstcin, Doctoral Thesis, University of Erlangen-Nürnberg, 1986.
7. K. Rippstein, H.Kaesche, Corros.Sci. 29 (1989) p.517.
8. M.O. Spcidel, R.M. Magdowski, "Stress corrosion cracking of nuclear reactor pressure vessel steel in water: crack initiation versus crack growth", CORROSION '88, paper no. 283, St.Louis, MO, March 1988.
9. Z. Szklarska-Smialowsaka, D.D. MacDonald, H. Choi, EPR1 NP 2853, RPT 115-5, Final Report, Palo Alto, CA, 1983.P.2-2.
10. K. Törröncn, Fractographic evaluation of specimens of A533B pressure vessel steel, Final Report, EPRI, 1984.
11. B. Iskluth, Doctoral Thesis, MPA Stuttgart, 1989.
12. E. Lenz, N. Wieling, H. Münster, The Metallurgical Society, 1988, p.283.
13. M.O. Speidel, R.M. Pcdrazzoli, "Ursachen und Geschwindigkeit des umgebungsabhängigen Bruchs in metallischen Werkstoffen", 17. Mctalllagung: Umgebungsabhängiges Bruchvcrhalten, Dresden, 1990, p.l.
14. H. Choi, F.H. Beck, Z. Szklarska-Smialowska, D.D. MacDonald, Corros. NACE 38 (1982) p.l36.
15. E. Tenckhoff, M. Erve, E. Lenz, G. Vazoukis, "Umgebungseinfluß auf das Rißwachstum von niedriglegierlen Stählen-Ergebnisse und deren Ubertragbarkeit auf LWR-Komponcntcn", 14. MPA-Seminar, Stuttgart, 1988.
16. H. Kacsche, "Testing of stress corrosion cracking of low alloy steel in high-temperature, high-pressure water", Life Prediction of Corrodible Structures, Proc. 3rd NACE IRMC Symp., Cambridge, 1991.
17. R.C. Newman, "Anodic stress corrosion cracking: slip-disssolution and film-induced cleavage", Corrosion-Deformation Interactions, Fonlainblcau, 1992.
18. H. Keller, HJ. Grabkc, H.P. Stoppa Werkstoffe u. Korros. 32 (1981) p.275.
19. M.O. Speidel, R.M. Pcdrazzoli, Tagungsbericht 17. MPA-Scminar, Stuttgart, 1991.
20. V. Schmidt, M.Moser, "Rißbildung durch innere und äußere Medien", 17.Mctalltagung: Umgebungsabhängiges Bruchvcrhalten, Dresden, 1990, p. 151
21. Z. Szklarska-Smialowska, Corros. NACE 28 (1972) p.388.
22. H. Kaeschc, "Die Spannungsrißkorrosion der Stähle in Wässern: Der Stand der forschenden Untersuchung", Spannungsrißkorrosion von Stahl in Wasser, Ergebnisse der Werkstoff-Forschung, Zürich, 1988.
23. R.M. Magdowski, "Spannungsrißkorrosion von ferritischen Stählen in Wasser", Moderne Stähle, Reihe Ergebnisse der Werkstoff-Forschung, Verlag Schweizerische Akademie der Wissenschaften, 1987, p.l07.
24. Z. Szklarska-Smialowska, E. Lunarska, Wcrstoffc Korros. 32 (1981) p.478.
25. G. Wranglcn, Corros.Sci. 14 (1974) p.331.
26. U. Rohlfs, Doctoral Thesis, University of Erlangcn-Nürnberg, 1983.
27. U.Rohlfs, H. Kaeschc, Der Maschinenschaden 57 (1984) p.l 1.
28. H. Keller, HJ. Grabke, Werkstoffe Korros. 32 (1981) p.540.
29. Forschungsvorhaben 1500 304 B: Komponentcnsichcrhcit (Phase II), Final Report, MPA Stuttgart, 1990.
30. D.D. MacDonald, J.Elcctrochcm.Soc. 126 (1979) p.1618.
31. P. Wcidingcr, Diploma Thesis, University of Erlangcn-Nürnberg, 1992.
32. H. Gladcn, Doctoral Thesis, University of Erlangcn-Nürnberg, 1994.
33. K.E. Hcuslcr, B. Kusian, D. McPhaii, Bcr.Bunscngcs.Phys.Chcm. 94 (1990) p.1443.
34. J. Frank, Diploma Thesis, University of Erlangen-Nürnbcrg, 1995.
35. H.Kacsche, Die Korrosion der Metalle, 3.Auflage, Springer Verlag, Berlin, 1990.