Composite Structures

Volumn 47, Issue 1-4, 1999, Pages 635-641

Optimum in situ strength design of laminates under combined mechanical and thermal loads

(2) Wang, J a Karihaloo, B L b

a PEKING UNIVERSITY (China)

b CARDIFF UNIVERSITY (United Kingdom)

Author keywords

Failure criterion; First ply failure; In situ strength; Optimum design; Thermal load

Indexed keywords

CRACK INITIATION; DELAMINATION; FAILURE ANALYSIS; FIBER REINFORCED MATERIALS; FRACTURE MECHANICS; NONLINEAR PROGRAMMING; OPTIMIZATION; SHEAR STRENGTH; TENSILE STRENGTH; THERMAL STRESS;

MULTIDIRECTIONAL FIBER REINFORCED COMPOSITE LAMINATE; OPTIMUM STRENGTH DESIGN; TRANSVERSE CRACKING; TSAI-HILL FAILURE CRITERION;

LAMINATED COMPOSITES;

DESIGN; FIBER REINFORCED COMPOSITE; LOADING; STRENGTH;

EID: 0033303932 PISSN: 02638223 EISSN: None Source Type: Journal
DOI: 10.1016/S0263-8223(00)00040-4 Document Type: Conference Paper

Times cited : (17)

References (15)

1
- 0008129158
- Air Force Flight Dynamic Laboratory, Wright-Patterson AFB
- (1969) Parametric Study of Tsai's Strength Criterion for Filamentary Composites. TR-68-168
- Sandhu, R.S.¹

2
- 84965878999
- Optimum filament orientation criteria
- (1970) J Comp Mater , vol.4 , pp. 422-425
- Brandmaier, H.E.¹

3
- 0016434282
- Strength optimization for cylindrical shells of laminated composites
- (1975) J Comp Mater , vol.9 , pp. 53-66
- Chao, C.C.¹ Sun, C.T.² Koh, S.L.³

4
- 0020161065
- An optimal design of simple symmetric laminates under the first ply failure criterion
- (1982) J Comp Mater , vol.16 , pp. 341-355
- Park, W.J.¹

5
- 0023984395
- On laminate configurations for simultaneous failure
- (1988) J Comp Mater , vol.22 , pp. 271-286
- Fukunaga, H.¹ Chou, T.-W.²

6
- 0008123482
- Optimization of symmetrically laminated composites rectangular plates
- In: Wu Y, Gu Z, Wu R, editors; Beijing: International Academic Publishers
- (1989) Proceedings of the Seventh International Conference on Composite Materials , vol.3 , pp. 289-294
- Miravete, A.¹

7
- 0025862851
- Strength optimization of laminated composites with respect to layer thickness and/or layer orientation angle
- (1991) Comput and Struct , vol.40 , pp. 1429-1439
- Fukunaga, H.¹ Vanderplaats, G.N.²

8
- 0008285450
- Cracked composite laminates least prone to delamination
- (1994) Proc. Roy. Soc. London A , vol.44 , pp. 17-35
- Wang, J.¹ Karihaloo, B.L.²

9
- 0029719228
- Optimum in situ strength design of composite laminates Part I: In situ strength parameters
- (1996) J Comp Mater , vol.30 , pp. 1314-1337
- Wang, J.¹ Karihaloo, B.L.²

10
- 0029701674
- Optimum in situ strength design of composite laminates Part II: Optimum design
- (1996) J Comp Mater , vol.30 , pp. 1338-1358
- Wang, J.¹ Karihaloo, B.L.²

11
- 0020098389
- Experimental determination of in situ transverse lamina strength in graphite/epoxy laminates
- (1982) J Comp Mater , vol.16 , pp. 103-116
- Flaggs, D.L.¹ Kural, M.H.²

12
- 0025741967
- Damage tolerance of laminated composites containing an open hole and subjected to compressive loadings Part I: Analysis
- (1991) J Comp Mater , vol.25 , pp. 2-43
- Chang, F.-K.¹ Lessard, L.B.²

13
- 0023397243
- The in situ ply shear strength distributions in graphite/epoxy laminated composite
- (1987) J Comp Mater , vol.21 , pp. 708-733
- Chang, F.-K.¹ Chen, M.H.²

14
- 0020129076
- Influence of layer thickness on the strength of angle-ply laminates
- (1982) J Comp Mater , vol.16 , pp. 216-227
- Herakovich, C.T.¹

15
- 0008123964
- Fracture mechanics and optimization - a useful tool for fibre-reinforced composite design
- (1995) Comp Struct , vol.31 , pp. 151-162
- Wang, J.¹ Karihaloo, B.L.²

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.